1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2005 09 14 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 1 of 2 FABRIC, TWILL GR PATTERN, FLAT WOVEN WSS-M1H756-A3 1. SCOPE The material defined by this specification is a piece dyed
2、 Dobby woven polyester face fabric. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for the 2005 ESCAPE Insert/Bolster seat cover. 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18
3、-A1/A2/A3/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3775) Warp (ends/10
4、cm) 150 Weft (picks/10 cm) 165 3.2.2 Fabric Weight, Laminated * Face w/backcoat g/m2, +/- 10% (FLTM BN 106-01) 440 339 * laminated with 3 mm foam 3.3 COMPOSITION (ASTM D 629) Fabric 100% Semi-dull polyester Backcoat Acrylic ENGINEERING MATERIAL SPECIFICATIONWSS-M1H756-A3 Printed copies are uncontrol
5、led Copyright 2005, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 80.6 tex f196 (textured) Weft 80.6 tex f196 (textured) 3.5 METHOD OF DYEING Piece dyed 3.6 FINISHED OPERATIONS Dye, dry, backcoat, laminate 3.7 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute Note: Not required on face fabric when used as a fully bonded composite.