1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2009 01 06 N-STATUS No Replacement B. Haggart, FNA 2003 03 21 Revised Para 3.0 inserted ; Para 3.1, 3.2, 3.3, 3.10, 3.11, 4 deleted 1997 11 11 Activated L. Daniv Printed copies are uncontrolled Page 1 of 2 C
2、opyright 2009, Ford Global Technologies, Inc. FABRIC, BENSON PATTERN, WOVEN WSS-M1H762-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a jacquard pattern, flat woven bodycloth of good quality and uniform composition. 2. APPLICATION This specification was releas
3、ed originally for material used as an interior trim fabric for PN 96 insert, laminated with 3 mm foam and pink poly. 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirements of: WSS-M8P18-A1/A4. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material
4、suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 FABRIC CONSTRUCTION 3.4.1 Fabric Count, +/- 5 % tolerance (ASTM D 3775) Warp 165.4 ends/10 cm Fill 118.1 picks/10 cm 3.4.2 Fabric Weight, range 413.4 - 489.2 g/m2(FLTM BN 10
5、6-01) 3.5 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4. Fabric 100 % Polyester Backcoating None ENGINEERING MATERIAL SPECIFICATION WSS-M1H762-A Page 2 of 2 Copyright 2009, Ford Global Technologies, Inc. 3.6 YARN CONSTRUCTION (ASTM D 1244) Warp 118.1 tex z 59 tpm (100% polyester, 2.5 dtex, 51 mm staple) 2 ply S 393.7 tpm Fill 66.7 tex, air textured (100% polyester, 2.45 dtex, 136 filaments) 2 ply air entangled 3.7 METHOD OF DYEING Yarn dyed 3.8 FINISHING OPERATIONS Needle and Lamination 3.9 FLAME RETARDANT USED No