1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2008 12 17 N-STATUS No Replacement B. Haggart, FNA 2003 02 18 Revised Para 3.0 inserted ; Para 3.1, 3.2, 3.8, 3.9, 4 deleted 1997 11 12 Activated L. Daniv Printed copies are uncontrolled Page 1 of 2 Copyrigh
2、t 2008, Ford Global Technologies, Inc. FABRIC MANITOU II PATTERN, KNIT WS-M1H76-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a 32 gage pattern, knit bodycloth of good quality and uniform composition. 2. APPLICATION This specification was released originally
3、for material used as an interior trim fabric for PN 96/UN 93. 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Company
4、s Standard Requirements For Production Materials (WSS-M99P1111-A). 3.3 FABRIC CONSTRUCTION 3.3.1 Fabric Count, +/- 5 % tolerance (ASTM D387) Wales 61 wales/ 10cm Course 75 course/ 10m 3.3.2 Fabric Weight, range 265 - 311 g/m2(FLTM BN 106-01) 3.4 COMPOSITION (ASTM D 629) Tolerance as specified in WSS
5、-M8P18-A1/A4. Fabric 100 % Polyester ENGINEERING MATERIAL SPECIFICATION WSS-M1H766-A Page 2 of 2 Copyright 2008, Ford Global Technologies, Inc. 3.5 YARN CONSTRUCTION (ASTM D 1244) Face (A) 16.7 tex textured (100 % polyester, 4.9 dtex, 34 filaments) (B) Same as (A) Middle 16.7 tex, textured (100 % polyester, 5.1 dtex, 3 filaments) Back 16.7 tex, textured (100 % polyester, 5.1 dtex, 3 filaments) 3.6 METHOD OF DYEING Yarn dyed and solutionye3.7 FINISHING OPERATIONS Slit, Shear, 3 Brush, Heatset