1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2003 02 27 Revised Para 3.0 inserted ; Para 3.1, 3.2, 3.3, 3.10, 3.11, 4 deleted 2000 07 31 Activated N. J. Komatsu Printed copies are uncontrolled Page 1 of 2 Copyright 2003, Ford Global Technologies, Inc.
2、FABRIC, TWILL II, PATTERN, FLAT WOVEN, WSS-M1H824-A UNLAMINATED 1. SCOPE The material defined by this specification is a woven jacquard polyester face fabric. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for the 2001 Model Year. 3. REQUIREMEN
3、TS In addition to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M
4、99P1111-A). 3.4 FABRIC CONSTRUCTION 3.4.1 Fabric Count, +/- 5 % tolerance (ASTM D 3775) Warp 246 ends/10 cm Weft 132 picks/10 cm 3.4.2 Fabric Weight, min (FLTM BN 106-01) 285 - 315 g/m23.5 COMPOSITION (ASTM D 629) Fabric 100 % polyester ENGINEERING MATERIAL SPECIFICATION WSS-M1H824-A Page 2 of 2 Cop
5、yright 2003, Ford Global Technologies, Inc. 3.6 YARN CONSTRUCTION (ASTM D 1244) Warp 730 dtex f144 (air texturised, semi-dul)Weft 750 dtex f192 (air texturised, semi-dul)3.7 METHOD OF DYEING Yarn dyed and spun or as approved by Materials Engineering 3.8 FINISHED OPERATIONS As approved by Materials E
6、ngineering 3.9 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute Note: Not required on face fabric when used as a fully bonded composite. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification: 5.1 Purchase departments will ensure that both materials defined in this specification and shipped to any one assembly plant will be produced by one supplier only.