1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2008 12 17 N-STATUS No Replacement B. Haggart, FNA 2003 04 16 Revised Para 3.0 inserted; Para 3.1, 3.2, 3.3, 3.9, 4 deleted 2002 01 30 Activated M. Dumitrescu Printed copies are uncontrolled Page 1 of 2 Copy
2、right 2008, Ford Global Technologies, Inc. FABRIC, APEX II PATTERN, FLAT CIRCULAR KNIT WSS-M1H876-A2 NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is an APEX pattern, flat CIRCULAR KNIT bodycloth of good quality and uniform composition. The fabric is tri-laminated
3、 with a foam and knitted scrim. 2. APPLICATION This specification was released originally for material used as a bolster of seat fabric for the 2003 P-150 Series 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirements of: WSS-M8P18-A1/A4. Material specif
4、ication requirements are to be used for initial qualification of materials. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 FABRIC CONSTRUCTION 3.4.1 Fabric Coun
5、t, +/- 5 % tolerance (ASTM D 3887) Wales 100/10 cm Courses 134/10 cm 3.4.2 Fabric Weight, range (FLTM BN 106-01) Face Fabric 429 - 503 g/m2Laminated to 3 mm foam 596 - 699 g/m2Knitted Scrim 45.6 g/m2Total 642 - 745 g/m2ENGINEERING MATERIAL SPECIFICATION WSS-M1H876-A2 Page 2 of 2 Copyright 2008, Ford
6、 Global Technologies, Inc. 3.5 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4. Fabric 100 % Polyester Knitted Scrim 100 % Nylon Tricot Scrim 3.6 YARN CONSTRUCTION (ASTM D 1244) Face A. 50% 16.7 tex f96 (natural polyester) x 3 B. 50% 16.7 tex f34 (natural polyester) x 3 3.7 METHOD OF DYEING Piece dyed 3.8 FINISHING OPERATIONS Dye, Slit, Heat Set, Lamination, Inspect