1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2005 02 03 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 1 of 2 FABRIC, MORTAR II PATTERN, KNIT WSS-M1H890-A3 1. SCOPE The material defined by this specification is a MORTAR II patte
2、rn, a 56 Gauge, Single Raschel knit, body cloth of good quality and uniform composition. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for S197 2005 Mustang seat bolster. 3. REQUIREMENTS In addition, to the requirements listed herein, the fabr
3、ic shall meet all requirements of WSS-M8P18-A1/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% t
4、olerance (ASTM D 3887) Wales 134 wales/10 cm Courses 189 courses/10 cm 3.2.2 Fabric Weight, +/- 5% g/m2 (FLTM BN 106-01) Face w/Backcoat 345 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 100% Polyester Backcoat Acrylic ENGINEERING MATERIAL SPECIFICATIONWSS-M1H890-A3 P
5、rinted copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Face 16.7 tex f36 (Semi dull Polyester) Middle 16.7 tex f36 (Semi dull Polyester) Back 16.7 tex f36 (Semi dull Polyester) 3.5 METHOD OF DYEING Piece Dye 3.6 FINISHING OPERATIONS Knit, Setmake, Dye, Tenter Dry, Tenter backcoat, Inspect