1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2008 12 05 N-STATUS No Replacement L. Schmalz, FNA / M. Montgomery, FOE 2004 05 26 Activated N. J. Komatsu Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 1 of 2 FABRIC, KISMET PATTERN, DBR KNITTED, WSS-M1H89
2、8-A UNLAMINATED NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a 6 bar 44 gauge warp knitted, simulated velour, double bar raschel; polyester bodycloth. 2. APPLICATION This specification was released originally for material used for as an interior trim fabric fo
3、r C195 China. 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For
4、Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3887) Wales 90 wales/10 cm Courses 126 courses/10 cm 3.2.2 Fabric Weight, range 520 +/- 50 g/m2(FLTM BN 106-01) 3.3 COMPOSITION (ASTM D 629) Fabric 100% polyester 3.4 YARN CONSTRUCTION (ASTM D
5、 1244) Pile (1) 500dtex f144 (polyester, texturized, semi-dull) Back 110 dtex f34 (polyester, texturized, semi-dull) ENGINEERING MATERIAL SPECIFICATIONWSS-M1H898-A Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 2 of 2 3.5 METHOD OF DYEING Yarn dyed or as approved
6、by Materials Engineering 3.6 FINISHING OPERATIONS As approved by Materials Engineering 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase departments will ensure that both materials defined in this specification and shipped to any one assembly plant will be produced by one supplier only.