1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2003 01 23 Activated M. Dumitrescu Printed copies are uncontrolled Page 1 of 2 Copyright 2003, Ford Global Technologies, Inc. FABRIC, MADISON PATTERN, WARP KNIT WSS-M1H900-A 1. SCOPE The material defined by
2、this specification is a double needle bar 56 Gauge pile warp knitted, simulated Corduroy, MADISON PATTERN, polyester bodycloth of good quality and uniform composition 2. APPLICATION This specification was released originally for material used as an interior trim fabric for Sable 2004 seat insert. 3.
3、 REQUIREMENTS In addition, to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials
4、(WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5 % tolerance (ASTM D 3887) Wales 100 wales/10 cm Courses 185 courses/ 10 cm 3.2.2 Fabric Weight, range, g/m2(FLTM BN 106-01) Laminated * Face w/no Backcoat 536 - 655 417 - 510 * 3 mm foam thickness ENGINEERING MATERIAL SPECIFICATION
5、WSS-M1H900-A Page 2 of 2 Copyright 2003, Ford Global Technologies, Inc. 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 100% Polyester 3.4 YARN CONSTRUCTION (ASTM D 1244) Face A 11.1 tex f50 (polyester) B 11.1 tex f100 (textured polyester) Middle 11.1 tex f34 (polyester) Back 11.1 tex f33 (textured polyester) 3.5 METHOD OF DYEING Disperse Piece Dye 3.6 FINISHING OPERATIONS Heat Set, Slit, Dye, Tenter Dry, Millitex, Inspect