1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2003 04 23 Revised Para 3.0 inserted; Para 3.1, 3.2, 3.3, 3.9, 4 deleted 2002 04 22 Activated M. Dumitrescu Printed copies are uncontrolled Page 1 of 2 Copyright 2003, Ford Global Technologies, Inc. FABRIC,
2、MORGAN PATTERN, PILE WARP KNIT WSS-M1H903-A 1. SCOPE The material defined by this specification is a Raschel 56 Gauge pile warp knitted, MORGAN PATTERN, polyester bodycloth of good quality and uniform composition 2. APPLICATION This specification was released originally for material used as an inter
3、ior trim fabric for Windstar 2004 seat insert. 3. REQUIREMENTS In addition, to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4 as applicable. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Company
4、s Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 FABRIC CONSTRUCTION 3.4.1 Fabric Count, +/- 5% tolerance (ASTM D 3887) Wales 118 wales/10 cm Courses 252 courses/ 10 cm 3.4.2 Fabric Weight, range, g/m2(FLTM BN 106-01) Face w/ Backcoat 375 - 395 Fabric laminated* 430 - 476 * 3 m
5、m foam ENGINEERING MATERIAL SPECIFICATION WSS-M1H903-A Page 2 of 2 Copyright 2003, Ford Global Technologies, Inc. 3.5 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 100% Polyester Backcoat Acrylic 3.6 YARN CONSTRUCTION (ASTM D 1244) Face 7.8 tex f72 (semi-dull Polyester) Middle 7.8 tex f36 (full-dull Polyester) Back 16.7 tex f36 (semi-dull Polyester) 3.7 METHOD OF DYEING Disperse Piece Dye 3.8 FINISHING OPERATIONS Shear, Heat Set, Dye, Tenter Dry, Range, Millitex, Inspect