1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2003 07 11 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 1 of 2 FABRIC, STAMPS PATTERN, PILE KNITTED WSS-M1H930-A 1. SCOPE The material defined by this specification is a 4 bar 28 g
2、auge warp knitted, simulated velour, and etching to design the pattern, polyester bodycloth of good quality and uniform composition. 2. APPLICATION This specification was released originally for material used as an interior trim fabric, seat insert for D258 2004 Model Year. 3. REQUIREMENTS In additi
3、on to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A).
4、3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3887) Wales 137 wales/10 cm Courses 229 courses/10 cm 3.2.2 Fabric Weight, range 393 435 g/m2(FLTM BN 106-01) 3.3 COMPOSITION (ASTM D 629) Fabric 100% polyester 3.4 YARN CONSTRUCTION (ASTM D 1244) Face (A) 8.0 tex f36 (polyester, s
5、emi-dull, round) (B) 7.7 tex f47 (polyester, dull) Middle 7.7 tex f36 (polyester, semi-dull, round) Back 7.7 tex f36 (polyester, semi-dull, round) ENGINEERING MATERIAL SPECIFICATIONWSS-M1H930-APrinted copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 2 of 2 3.5 METHOD OF DY
6、EING Piece dyed 3.6 FINISHING OPERATIONS As Approved by Materials Engineering 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase departments will ensure that both materials defined in this specification and shipped to any one assembly plant will be produced by one supplier only.