1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2003 10 10 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 1 of 2 FABRIC, TANGO PATTERN, KNIT DOOR INSERT WSS-M1H941-A 1. SCOPE The material defined by this specification is a TANGO P
2、ATTERN, a 56 Gauge, Single Raschel knit, body cloth of good quality and uniform composition. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for U364 MERCURY. The fabric is fully bonded to the substrate. 3. REQUIREMENTS In addition, to the requi
3、rements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTI
4、ON 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3887) Wales 184.5 wales/10 cm Courses 279 courses/ 10 cm 3.2.2 Fabric Weight, +/- 5% g/m2 (FLTM BN 106-01) Laminated * Face fabric 583.5 390 * 3 mm foam thickness 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 84% Polyest
5、er Binder 16% Polyurethane ENGINEERING MATERIAL SPECIFICATIONWSS-M1H941-APrinted copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Face 73% 9.4 texf156 (SD tex Polyester) Back 27% 7.77 texf36 (SD WD Polyester) 3.5 METHOD OF DYEING Piece Dye 3.6 FINISHING OPERATIONS Knit, dye, finish, face finish, bulk, finish, face finish, coat, bulk finish, face finish, emboss