1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2008 12 16 N-STATUS Replaced by WSS-M1H1091-A V. Demarchi, FSAO 2005 01 21 Activated L. Neves Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 1 of 2 FABRIC, KROMA PATTERN, WOVEN JACQUARD, UNLAMINATED WSS-M1H9
2、78-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a woven jacquard polyester face fabric. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for 2005 Model Year. 3. REQUIREMENTS In addition to the requirement
3、s listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTI
4、ON 3.2.1 Fabric Count, +/- 10% tolerance (ASTM D 3775) Warp 250 yarn/10 cm Weft 280 yarn/10 cm 3.2.2 Fabric Weight, +/- 10% tolerance 380.0 g/m (FLTM BN 106-01) 3.3 COMPOSITION (ASTM D 629) Fabric 100% Polyester 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 500 dtex f122, Semi-Dull, Round, Textured Polye
5、ster Weft (A) 800 dtex f182, Semi-Dull, Round, Textured Polyester (B) 600 dtex f158, Semi-Dull, Round, Textured Polyester ENGINEERING MATERIAL SPECIFICATIONWSS-M1H978-A Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 2 of 2 3.5 METHOD OF DYEING Warp Yarn Dyed Weft
6、Yarn Dyed 3.6 FINISHING OPERATIONS Weave, Wash, Heat Set 3.7 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, 100 mm/minute Note: Not required on face fabric when used as a fully bonded composite. 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase departments will ensure that material defined in this specification and shipped to anyone assembly plant will be produced by one supplier only.