1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 1 2014 08 22 Revised See Summary of Revisions R.Haigh, EU 2014 04 08 Released R. Released R. Haigh, EU Controlled document at www.MATS Copyright 2014, Ford Global Technologies, Inc. Page 1 of 15 OIL, ENGINE, INITIAL AND SERVICE FILL SAE
2、0W-30 WSS-M2C950-A 1. SCOPE These material specifications defined the minimum acceptable performance requirements and physical/chemical properties of engine oils to be used by Ford Motor Company in its worldwide engine/vehicle manufacturing operations. 2. APPLICATION This specification is released i
3、n Europe for service fill engine oils used for lubrication of spark ignition engines using gasoline and compression ignition engines using diesel. The Section 3.1 titled STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS applies only to engine oils supplied directly to Ford Motor Company and / or its af
4、filiates. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3.2 PERFORMANCE 3.2.1 General Test Requirements Where applicable, the required engine tests
5、 shall be conducted in accordance with the most recently approved procedures as described in the ACEA(xx) sequences. All tests under surveillance by ASTM must be conducted using test equipment monitored by and calibrated to the requirements of the ASTM Test Monitoring Center. All engine performance
6、testing used to support a claim of compliance with the ACEA sequences must be generated according to the EELQMS. Suppliers must demonstrate commitment to comply with the ATIEL Report values - “NIL“ or Trace“ are not permissible S _ _ _ _ _ P _ _ _ _ _ Zn _ _ _ _ _ Ba _ _ _ _ _ Ca _ _ _ _ _ Mg _ _ _
7、_ _ Na _ _ _ _ _ N _ _ _ _ _ B _ _ _ _ _ Cu _ _ _ _ _ Cl _ _ _ _ _ Sulfated Ash _ _ _ _ _ V. Tests Conducted _ _ _ _ _ Comments: _ _ _ _ _ Signature_ Title_ ENGINEERING MATERIAL SPECIFICATION WSS-M2C950-A Copyright 2014, Ford Global Technologies, Inc. Page 12 of 15 (Supplement A, p. 6 of 7) Oil Comp
8、any_ Date_ Product Name_ Viscosity Grade_ Product Code_ Specification Test Mfg. Physical/Chemical Properties Requirements Results Limits Viscosity at 150 C (ASTM D 445), mm2/s report _ _ Viscosity at 100 C (ASTM D 445), mm2/s 9.3-.001%) report _ _ Signature_ Title_ ENGINEERING MATERIAL SPECIFICATION
9、 WSS-M2C950-A Copyright 2014, Ford Global Technologies, Inc. Page 14 of 15 (Supplement B, p. 1 of 1) Oil Company_ Date_ Product Name_ Viscosity Grade_ Product Code_ Quality Control Certification Physical/Chemical Properties Approved Limits Frequency Viscosity at 150 C (ASTM D 445), mm2/s _ _ Viscosi
10、ty at 100 C (ASTM D 445), mm2/s _ _ Viscosity at 40 C (ASTM D 445), mm2/s _ _ Density (ASTM D 1298), kg/L _ _ Viscosity at -25 C (ASTM D 5293), mPa.s _ _ Viscosity at -30 C (ASTM D 5293), mPa.s _ _ Low Temp. Pumping Viscosity at -30 C, mPa.s _ _ (ASTM D 4684) at -35 C, mPa.s _ _ Pour Point (ASTM D 9
11、7), C _ _ Stable Pour Point (SAE J 300 App. B), C _ _ Gelation Index (ASTM D 5133) _ _ Flash Point (ASTM D 93), C _ _ Volatility Evap. Loss, 1 h at 250 C (ASTM D 5800), % _ _ Shear Stability (ASTM D 445), mm2/s at 100 C After ASTM D 6278 or CEC L-14-A-93 _ _ Viscosity at 150 C and 106 s-1 CEC L-36-A
12、-90, mPa.s New Oil _ _ After ASTM D 6278 or CEC L-14-A-93 _ _ Copper Corrosion (ASTM D 130, 3 h at 100 C) _ _ Filterability (ASTM D 6795), % flow reduction, max _ _ Water Tolerance (ASTM D 6794), % _ _ Foaming (ASTM D 892) without Option A Sequence I, mL _ _ Sequence II, mL _ _ Sequence III, mL _ _
13、High Temperature Foaming (ASTM D6082), mL _ _ Total Acid Number (ASTM D 664), mg KOH/g _ _ Total Base Number (ASTM D 2896), mg KOH/g _ _ Sulfated Ash (ASTM D 874), % _ _ Phosphorus content, % _ _ Cleanliness Max Particle Size _ _ Cleanliness Particle Count _ _ Barium, % _ _ Boron, % _ _ Calcium, % _
14、 _ Chlorine, % _ _ Copper, % _ _ Magnesium, % _ _ Molybdenum, % _ _ Nitrogen, % _ _ Potassium, % _ _ Silicon, % _ _ Sodium, % _ _ Sulfur, % _ _ Zinc, % _ _ Other (.001%) _ _ ENGINEERING MATERIAL SPECIFICATION WSS-M2C950-A Copyright 2014, Ford Global Technologies, Inc. Page 15 of 15 Signature_ Title_ MaterialsEngineering Concurrence_