1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2003 12 15 Activated B HennesseyPrinted copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 1 of 4 THERMOPLASTIC ELASTOMER, STYRENE POLYOLEFIN BLOCK WSS-M2D505-A3 COPOLYMER (TES), 70 DUROMETER A HARDNESS, EXTERIOR APPLI
2、CATIONS 1. SCOPE The materials defined by this specification are U.V. stabilized thermoplastic styrene-ethylene/butylene-styrene copolymer elastomers. The materials can be processed by conventional thermoplastic molding techniques such as injection and/or extrusion molding. 2. APPLICATION This speci
3、fication was released originally for material used for window encapsulation seals, door belt line seals, roof profile seals and windshield trim seals. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requir
4、ements For Production Materials (WSS-M99P1111-A). 3.2 DYNAMIC MECHANICAL ANALYSIS (ASTM D 4065) Ford Motor Company, at its option, may establish shear modulus/damping vs. temperature curves plotted for - 50 to + 170 C temperature range for material/parts supplied to this specification. The shear mod
5、ulus and damping curves established for initial approval shall constitute the reference standard and shall be kept on file at the designated material laboratory. All samples shall produce shear modulus and damping curves that correspond to the reference standard when tested under the same conditions
6、. 3.3 MATERIAL TESTING 3.3.1 Preparation of Test Specimens Whenever possible, all test specimens shall be die-cut from the finished parts. When not feasible, specimens cut from molded test sheets manufactured from the same material and with equivalent cure to the molded parts are recommended. The te
7、st sheets shall have the following dimensions: 150 x 150 mm, min x 2.0 +/- 0.2 mm ENGINEERING MATERIAL SPECIFICATIONWSS-M2D505-A3Printed copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 2 of 4 3.4 ORIGINAL PROPERTIES 3.4.1 Density, +/- 0.05 g/cm31.14 (ISO 1183, Method A) 3
8、.4.2 Hardness, Durometer A 70 +/- 5 (ISO 868, 15 second dwell) 3.4.3 Tensile Strength, MPa, min (ISO 37/type 1/500 mm/min) I. Parallel to Flow 4.2 II. Perpendicular to Flow 4.9 3.4.3.1 Elongation at Break, %, min (Test method according to para 3.4.3) I. Parallel to Flow 300 II. Perpendicular to Flow
9、 450 3.4.3.2 Modulus at 100% Elongation, MPa, min (Test method according to para 3.4.3) I. Parallel to Flow 3.2 II. Perpendicular to Flow 2.0 3.4.4 Tear Strength, kN/m, min (ISO 34, specimen angular type) 3.4.4.1 Parallel to Flow 22 3.4.4.2 Perpendicular to Flow 26 3.4.5 Brittleness Point, max - 40
10、C (ISO 812, Type B specimen/ ASTM D 2137, Method A) 3.4.6 Ozone Resistance, max 0 Rating (FLTM BP 101-01, Procedure A) 3.4.7 Compression Set, %, max 22 (ISO 815, 22 h at 23 +/- 2 C) ENGINEERING MATERIAL SPECIFICATIONWSS-M2D505-A3Printed copies are uncontrolled Copyright 2003, Ford Global Technologie
11、s, Inc. Page 3 of 4 3.4.8 Compression Set, %, max 39 (ISO 815, 22 h at 70 +/- 2 C) 3.4.9 Compression Set, max 55 (ISO 815, 22 h at 100 +/- 2 C) 3.4.10 Migration Staining Rating 4 minimum (FLTM BN 103-01, ISO 105-A02/ AATCC Evaluation Procedure 2) 3.5 HEAT AGING (ISO 188, 150 +/- 50 air change/h, 100
12、0 h at 125 +/- 2 C) 3.5.1 Hardness Change, +/- 5 3.5.2 Tensile Strength Change, max - 40% 3.5.3 Elongation Change, max - 40% 3.5.4 Visual Evaluation No surface tackiness or cracks when folded flat against self. 3.6 FLAMMABILITY (ISO 3795 / FMVSS 302) Burn Rate, max 100 mm/minute 3.7 WEATHERING RESIS
13、TANCE After exposure in accordance with 3.7.1, 3.7.2 and 3.7.3 the material shall show no color change in excess of specified Gray Scale rating (AATCC Evaluation Procedure 1/ ISO 105-A02). In addition, there shall be no cracking, crazing or other deterioration. A slight loss of gloss or chalking wil
14、l be allowed provided an acceptable appearance can be achieved by washing and/or polishing with Ford car polish (auto wax) after the outdoor exposure, by permission of the affected Product Development Materials Activity. All initial approval will be based on the preliminary Weatherometer exposure, p
15、ending Florida and Arizona exposure results for final approval. 3.7.1 Xenon Arc Weatherometer Exterior Rating 4 (SAE J1960, 2500 kJ/m2exposure minimum, specimen size: 60 x 60 minimum x 2.0 +/- 0.1 mm thick, smooth surface, low gloss injection molded specimen) ENGINEERING MATERIAL SPECIFICATIONWSS-M2
16、D505-A3Printed copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 4 of 4 3.7.2 Weathering Rating 4 12 months Florida 12 months Arizona Exterior (SAE J1976, 5 south, direct weathering inland, specimen size: 60 x 60 minimum x 2.0 +/- 0.1 mm thick, smooth surface, low gloss inj
17、ection molded specimen) 3.7.3 Weathering Rating 3-4 24 months Florida 24 months Arizona Exterior (SAE J1976, 5 south, direct weathering inland, specimen size: 60 x 60 minimum x 2.0 +/- 0.1 mm thick, smooth surface, low gloss injection molded specimen) 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 RECYCLING CODE TES