1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2014 11 24 N Status No replacement named D. Murtonen, NA 2003 01 14 Revised Para 3.0 inserted ; Para 3.1, 3.2, 3.3, 3.7, 4 deleted 1998 06 08 Activated N.J. Komatsu Page 1 of 3 Copyright 2014, Ford Global Te
2、chnologies, Inc. FABRIC, VINYL COATED, MULTI-PURPOSE WSS-M2F195-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is an expanded vinyl coated knitted fabric. 2. APPLICATION This specification was released originally for material used as a cover material for interior
3、 trim fabric for use in India. 3. REQUIREMENTS In addition to the requirements listed herein, this material shall meet all requirements of WSS-M8P3-D1/D2/D3, PERFORMANCE, FLEXIBLE POLYMERIC FILM, INTERIOR QUALITY material performance specification except for COLD IMPACT. Assemblies specifying WSS-M2
4、F195-A must also meet the requirements of the requirements of the WSS-M15P4-E INTERIOR TRIM-ASSEMBLY PERFORMANCE specification. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M9
5、9P1111-A). 3.4 APPEARANCE (FLTM BI 109-01) The color, pattern and finish shall match the approved master sample, or shall be as specified on the Engineering Drawing. 3.5 VINYL COATED FABRIC 3.5.1 *Backing Fabric (see para 5, General Information) * Or Engineering Approved Alternative. 3.5.2 Weight, r
6、ange (ASTM D 751, sample method) Backing Fabric 65 +/- 5 gm2 Total 685 +/- 68 gm2 (Fabric Backing and Vinyl Coating) ENGINEERING MATERIAL SPECIFICATION WSS-M2F195-A Page 2 of 3 Copyright 2014, Ford Global Technologies, Inc. 3.5.3 Thickness, range, +/- 10 % Vinyl Skin 0.270 mm Total 1.2 mm 3.5.4 Resi
7、stance to Tear (Trapezoid), min (ASTM D 5733) Warp 60 N Fill 70 N 3.5.5 Breaking Strength, min (ASTM D 751, grab method) Warp 400 N Fill 350 N 3.5.6 Stiffness, max (ASTM D 747, direct reading at 60 angle with a 0.01 N-m moment weight) Warp 22 Fill 22 3.5.7 Low Temperature Impact, min 4 J (FLTM BN 12
8、8-01) Original - 25 C Heat Aged (7 days at 80 C) - 20 C No visible cracking when tested as received and after heat aging. 3.5.8 Dimensional Stability, 15 minutes at 100 C, max (SAE J883, oven aged in ASTM E 145 oven type 11A, 150 +/- 5 air changes per hour) Warp +/- 2 % Fill +/- 1 % 3.5.9 Stretch an
9、d Set, % range (SAE J855) Stretch Set Warp 10 - 40 0 - 5 Fill 50 - 120 0 - 15 ENGINEERING MATERIAL SPECIFICATION WSS-M2F195-A Page 3 of 3 Copyright 2014, Ford Global Technologies, Inc. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification 5.1 BACKING FABRIC 5.1.1 Composition (ASTM D 276) Fabric Polyester continuous filament Yarn fiber 167 dTex 5.1.2 Fabric Construction, min (ASTM D 3887) Wales 73 per 10 cm Courses 90 per 10 cm 5.1.3 Breaking Strength, min (ASTM D 751) Wales 170 N Courses 110 N