1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions 2014 11 24 N Status No replacement named D. Murtonen, NA 2010 06 21 Revised Completely Revised L. Sinclair, NA 2001 06 07 Activated M. Dumitrescu Copyright 2014, Ford Global Technologies, LLC Page 1 of 2 FABRIC, SUEDE EFFECT, CARPET BINDING W
2、SS-M2F198-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is 100% polyester. 2. APPLICATION This specification was released originally for material used as sewn edge binding for automotive floor mats 3. REQUIREMENTS Material specification requirements are to be us
3、ed for initial qualification of materials. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1.1 Vehicle Interior Environment Quality Materials/Component Performance
4、 Requirements Materials used in interior applications must meet the requirements outlined in WSS-M99P2222-B1. Data must be included in material submission package. 3.2 APPEARANCE (FLTM BI 109-01) The color, pattern, gloss level and finish shall match the approved Corporate Design master sample, or s
5、hall be as specified on the engineering drawing. 3.3 BACKING FABRIC The fabric shall be knitted from a good grade of polyester yarn Construction 100% Polyester 3.4 WEIGHT 220 +/- 3% g/m2 (ASTM D 3776) 3.5 BREAKING STRENGTH (ASTM D 5034) WMD 475 N min. AMD 950 N min. ENGINEERING MATERIAL SPECIFICATIO
6、N WSS-M2F198-A Copyright 2014, Ford Global Technologies, LLC. Page 2 of 2 3.6 RESISTANCE TO TEAR TRAPAZOID (ASTM D 1424) WMD 49 N +/- 10% AMD 64 N +/- 10% 3.7 TABER ABRASION (SAE J948, 500g load, H-18 wheels) 500 cycles The abraded area shall be compatible with the adjacent unabraded area. 3.8 RESISTANCE TO FADE (FLTM BO 116-01, ISO 105-02/ AATCC Evaluation Procedure 1) 225.6 kJ/m2 Rating 4 min. 3.9 ODOR (FLTM BO 131-03) Rating 3 max. 3.10 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate 100mm/min max