1、 ENGINEERING MATERIAL SPECIFICATION FABRIC, VINYL COATED (PVC), COTTON BACKED, WSS-M2F210-A1 FLOOR MAT BINDING NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is vinyl coated cotton based fabric of uniform construction. 2. APPLICATION This specification was released
2、 originally for floor mat binding. 3. REQUIREMENTS In addition to the requirements listed herein, the material must also meet the requirements of WSS-M8P24-A/ Latest, Performance, Floor Mat Edging. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform
3、to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1.1 Materials used in interior applications must meet the requirements outlined in WSSM99P2222-C1/Latest, Performance, Vehicle Interior Environment Quality Material/Component Requirements. Data must be included in mat
4、erial submission package. 3.2 FABRIC CONSTRUCTION - BACKING 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3887) Warp 10 yarn/cm Fill 10 yarn/cm 3.2.2 Weight (FLTM BN 106-01) Fabric 75 +/- 5 g/m2Coating 300 +/- 10 g/m2Total 375 +/- 15 g/m23.2.3 Thickness 0.70 +/- 15 mm 3.3 COMPOSITION (ASTM D 629) Fab
5、ric 100% Cotton Coating 100% PVC Date Action Revisions Rev. 0 2015 08 05 N Status No longer in use L. Sinclair, NA 2011 12 13 Active New specification L. Sinclair, NA Controlled document at www.MATS Copyright 2015, Ford Global Technologies, LLC Page 1 of 2 ENGINEERING MATERIAL SPECIFICATION WSS-M2F2
6、10-A1 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 100% cotton, Nm 50Fill 100% cotton, Nm 50 3.5 METHOD OF DYING Piece 4. GENERAL INFORMATION This information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Eng
7、ineering Material Specifications. 4.1 PHYSICAL PROPERTIES 4.4.1 Tensile Strength (ISO 1421) Warp 20 daN/5 cm Fill 14 daN/5 cm 4.4.2 Elongation (ISO 1421) Warp 30 % Fill 206% 4.4.3 Tear Strength (ISO 4674) Warp 0.9 daN Fill 0.8 daN 4.4.4 Stretch and Set (SAE J855) Warp 15 % Fill 45 % 4.4.5 Adhesion (PVC to Fabric) 7.5 daN/5 cm (ISO 2411) 5. SUMMARY OF REVISIONS Controlled document at www.MATS Copyright 2015, Ford Global Technologies, LLC Page 2 of 2