1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions 2006 08 30 Revised Inserted 3.0; Deleted 3.1, 3.2, 3.3, 3.11 & 4 1996 05 13 Revised Added WSS-M96D30-A2 B. Hennessey 1990 02 12 Released C10059230 B. Hennessey Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page
2、 1 of 3 HOSE, ETHYLENE/ACRYLIC (AEM) RUBBER REINFORCED, WSD-M96D30-A LOW PRESSURE, ENGINE OIL RESISTANT, 75 IRHD HOSE, ETHYLENE/ACRYLIC (AEM) RUBBER REINFORCED, WSS-M96D30-A2 LOW PRESSURE, ENGINE OIL RESISTANT, 65 IRHD 1. SCOPE The material described by these specifications is a hose of Ethylene/Acr
3、ylic Rubber, (75 IRHD-A, 65 IRHD-A2) internally reinforced with a single ply of braided textile and resistant to engine oils. 2. APPLICATION The material was released originally for use as crankcase drain hoses and turbo charger air hoses where resistance to long term exposure to engine oils up to 1
4、50 C and air temperatures up to 150 C are required. The hose is also capable of withstanding short term oil temperatures up to 175 C and maintaining flexibility down to -40 C. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the
5、 Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 HOSE CONSTRUCTION The hose shall consist of an Ethylene/Acrylic rubber inner tube and outer cover with a single layer of suitable braided reinforcing textile. The hose will usually be shaped. 3.5 MATERIAL TESTING Whenever
6、 possible, all test specimens shall be die-cut from the finished parts. When not feasible, specimens cut from molded test sheets manufactured from the same material and with equivalent cure to molded parts are recommended. The test sheets shall have the following dimensions: 150 x 150 mm, min x 2.0
7、/- 0.2 mm 3.6 ORIGINAL PROPERTIES: TUBE AND COVER MATERIAL A A2 3.6.1 Hardness, International 70 - 80 60 - 70 (ISO 48/ASTM D 1415) 3.6.2 Hardness, Durometer A 70 - 80 60 - 70 (ISO 868/ASTM D 2240, instantaneous, plied-up specimens. Hand held durometers shall not be used.) ENGINEERING MATERIAL SPECI
8、FICATION WSD-M96D30-A WSS-M96D30-A2 Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 3 A A2 3.6.3 Tensile Strength, MPa, min 10 12 (ISO 37/ASTM D 412, Die C) 3.6.4 Elongation at break, %, min 200 275 (Test method according to 3.6.3) 3.6.5 Modulus at 100% Elonga
9、tion, MPa 5.0 2.5 (Test method according to 3.6.3) to 8.5 to 5.0 3.6.6 Tear Strength, kN/m, min 40 15 (ISO 34, Method B, Procedure (a)/ ASTM D 624, Die C) 3.6.7 Compression Set, %, max 50 25 (ISO 815/ASTM D 395 Method B, except 25% compression, plied-up specimens, 70 h at 150 +/- 2 C) 3.6.8 Ozone Re
10、sistance, max Rating 0 0 (FLTM BP 101-01) 3.7 HEAT AGED (ISO 188/ASTM D 573, 150 +/- 50 air changes/h, 1000 h at 150 +/-2 C) Hardness Change, max +15 Tensile Strength Change, max -20% Elongation at Break Change, max -60% Visual Evaluation No surface tackiness or cracks when folded flat against itsel
11、f. 3.8 IMMERSION IN CURRENTLY RELEASED PRODUCTION ENGINE OIL (ISO 1817/ASTM D 471, 1000 h at 150 +/- 2 C, see para 5.1) Hardness Change, max -30 Tensile Strength Change, max -30% Elongation at Break Change, max -35% Volume Change, max +60% ENGINEERING MATERIAL SPECIFICATION WSD-M96D30-A WSS-M96D30-A
12、2 Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 3 of 3 3.9 IMMERSION IN CURRENTLY RELEASED PRODUCTION ENGINE OIL (ISO 1817/ASTM D 471, 168 h at 175 +/- 2 C, see para 5.1) Hardness Change, max -25 Tensile Strength Change, max -20% Elongation at Break Change, max -
13、20% Volume Change, max +30% 3.10 FINISHED PART REQUIREMENTS 3.10.1 Burst Pressure, min (ASTM D 380) 25 mm ID 1.0 MPa 3.10.2 Flexibility at -40 C No breaks or cracks (FLTM BN 102-01, except Burst test per 3.10.1 use mandrel 10 x nominal I.D.) 5. GENERAL INFORMATION The information given below is prov
14、ided for clarification and assistance in meeting the requirements of these specifications. 5.1 For information on currently approved engine oils for use in these specifications contact: Materials Laboratory 15/GM-DO1-D Fluids Materials Section Research and Engineering Center Coolants/Greases Ford Motor Company Ltd Engine Engineering Laindon, Basildon P.O. Box 2053 Essex SS15 6EE, England 21500 Oakwood Boulevard Dearborn, MI 48121, USA Materials Engineering Product Engineering Office Ford Motor Co. of Australia Ltd Princes Highway, Norlane Victoria 3214, Australia 5.2 Recycling Code AEM