1、 PERFORMANCE SPECIFICATION CLEANING COMPOUNDS, AIRCRAFT, EXTERIOR This specification is approved for use by all Departments and Agencies of the Department of Defense. 1. SCOPE 1.1 Scope. The cleaning compounds covered by this specification are used for cleaning the exterior surface of aircraft. 1.2
2、Classification. The cleaning compounds covered by this specification are furnished in the following types (see 6.2): Type I - General purpose, aromatic solvent base Type IA - General purpose, aromatic solvent base, aerosol Type IW - General purpose, aromatic solvent base, pre-saturated wipe Type II
3、- General purpose, non-solvent Type II RTU - General purpose, non-solvent, ready to use (RTU) Type III - Abrasive spot cleaner Type IV - Rubberized spot cleaner Type V - Gel-type wheel well degreaser, low solvent (less than 10 percent) Comments, suggestions, or questions on this document should be a
4、ddressed to: Commander, Naval Air Warfare Center Aircraft Division, Code 4L8000B120-3, Highway 547, Lakehurst, NJ 08733-5100 or emailed to michael.sikoranavy.mil. Since contact information can change, you may want to verify the currency of this address information using the ASSIST Online database at
5、 https:/assist.daps.dla.mil. AMSC N/A FSC 6850 NOT MEASUREMENT SENSITIVEMIL-PRF-85570E 27 March 2012 SUPERSEDING MIL-PRF-85570D 19 June 2002 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-PRF-85570E 2 2. APPLICABLE DOCUMENTS 2.1 General. The doc
6、uments listed in this section are specified in sections 3 and 4 of this specification. This section does not include documents cited in other sections of this specification or recommended for additional information or as examples. While every effort has been made to ensure the completeness of this l
7、ist, document users are cautioned that they must meet all specified requirements of documents cited in sections 3 and 4 of this specification, whether or not they are listed. 2.2 Government documents. 2.2.1 Specifications and standards. The following specifications and standards form a part of this
8、document to the extent specified herein. Unless otherwise specified, the issues of these documents are those cited in the solicitation or contract. FEDERAL STANDARDS FED-STD-595 - Colors Used in Government Procurement/ FED-STD-595 Color Numbers 17875, 36440, and 36495 DEPARTMENT OF DEFENSE SPECIFICA
9、TIONS MIL-C-1164 - Cloth, Terry, Cotton, Cotton and Polyester MIL-G-21164 - Grease, Molybdenum Disulfide, for Low and High Temperatures, NATO Code Number G-353 MIL-PRF-23377 - Primer Coatings: Epoxy, High Solids MIL-W-81381/11 - Wire, Electric, Fluorocarbon/Polyimide Insulated, Medium Weight, Silver
10、 Coated Copper Conductor, 600 Volts, 200 DEG C, NOMINAL 8.4 or 15.4 Mil Wall MIL-PRF-83282 - Hydraulic Fluid, Fire Resistant, Synthetic Hydrocarbon Base, Aircraft, Metric, NATO Code Number H-537 MIL-PRF-85285 - Coating, Polyurethane, High-Solids, Aircraft and Support Equipment (Copies of these docum
11、ents are available online at https:/assist.daps.dla.mil/quicksearch/ or https:/assist.daps.dla.mil or from the Standardization Document Order Desk, 700 Robbins Avenue, Building 4D, Philadelphia, PA 19111-5094.) 2.2.2 Other Government documents, drawings, and publications. The following other Governm
12、ent documents, drawings, and publications form a part of this document to the extent specified herein. Unless otherwise specified, the issues of these documents are those cited in the solicitation or contract. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from
13、IHS-,-,-MIL-PRF-85570E 3 CODE OF FEDERAL REGULATIONS 29 CFR 1910.1200 - Occupational Safety and Health Standards - Hazard Communications 40 CFR - Protection of Environment 40 CFR 796.3100 - Aerobic Aquatic Biodegradation (Copies of these documents are available online at http:/www.gpoaccess.gov or f
14、rom the Superintendent of Documents, U.S. Government Printing Office, Washington, DC 20402.) NAVAL AIR SYSTEMS COMMAND NAVAIR 01-1A-509 - Aircraft Weapons Systems Cleaning and Corrosion Control (This document has limited distribution. Requests for copies by U.S. Government agencies and their contrac
15、tors should be made to the Naval Air Systems Command, Code 4.3.4.2, Unit 5, Building 2188, 48066 Shaw Road, Patuxent River, MD 20670.) 2.3 Non-Government publications. The following documents form a part of this document to the extent specified herein. Unless otherwise specified, the issues of these
16、 documents are those cited in the solicitation or contract. ASTM INTERNATIONAL ASTM D93 - Standard Test Methods for Flash Point by Pensky-Martens Closed Cup Tester. (DoD Adopted) ASTM D95 - Standard Test Method for Water in Petroleum Products and Bituminous Materials by Distillation. (DoD Adopted) A
17、STM D523 - Standard Practice for Specular Gloss. (DoD Adopted) ASTM D1141 - Standard Practice for the Preparation of Substitute Ocean Water. (DoD Adopted) ASTM D3065 - Standard Test Methods for Flammability of Aerosol Products ASTM E70 - Standard Test Method for pH of Aqueous Solutions with the Glas
18、s Electrode. (DoD Adopted) ASTM E168 - Standard Practices For General Techniques of Infrared Quantitative Analysis. (DoD Adopted) ASTM F483 - Standard Practice for Total Immersion Corrosion Test for Aircraft Maintenance Chemicals. (DoD Adopted) ASTM F484 - Standard Test Method for Stress Crazing of
19、Acrylic Plastics in Contact with Liquid or Semi-liquid Compounds. (DoD Adopted) ASTM F485 - Standard Test Method For Effects of Cleaners on Unpainted Aircraft Surfaces ASTM F502 - Standard Test Method for Effects of Cleaning and Chemical Maintenance Materials on Painted Aircraft Surfaces. (DoD Adopt
20、ed) Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-PRF-85570E 4 ASTM F519 - Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments. (DoD Adopted) ASTM F1104 - Standard Test Met
21、hod for Preparing Aircraft Cleaning Compounds, Liquid type, Water Base, for Storage Stability Testing ASTM F1110 - Standard Test Method for Sandwich Corrosion Test. (DoD Adopted) ASTM F1111 - Standard Test Method for Corrosion of Low-Embrittling Cadmium Plate by Aircraft Maintenance Chemicals. (DoD
22、Adopted) (Copies of these documents are available from www.astm.org or ASTM International, 100 Barr Harbor Drive, West Conshohocken, PA 19428-2959.) SAE INTERNATIONAL SAE AMS4377 - Sheet and Plate, Magnesium Alloy, 3.0Al - 1.0Zn 0.20Mn (AZ31B-H24) Cold Rolled, Partially Annealed - UNSM11311. (DoD Ad
23、opted) SAE AMS4911 - Titanium Alloy, Sheet, Strip, and Plate 6Al - 4V Annealed - UNSR56400. (DoD Adopted) SAE AMS5046 - Sheet Strip and Plate, Carbon Steel (SAE 1020 and 1025), Annealed. (DoD Adopted) SAE AMS-M-3171 - Magnesium Alloy, Processes for Pretreatment and Prevention of Corrosion on. (DoD A
24、dopted) SAE AMS-QQ-A-250/4 - Aluminum Alloy 2024, Plate and Sheet. (DoD Adopted) SAE AMS-QQ-A-250/12 - Aluminum Alloy 7075, Plate and Sheet. (DoD Adopted) (Copies of these documents are available from http:/www.sae.org or from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001.) 2.
25、4 Order of precedence. Unless otherwise noted herein or in the contract, in the event of a conflict between the text of this document and the references cited herein, the text of this document takes precedence. Nothing in this document, however, supersedes applicable laws and regulations unless a sp
26、ecific exemption has been obtained. 3. REQUIREMENTS 3.1 Qualification. The cleaning compounds furnished under this specification shall be products that are authorized by the qualifying activity for listing on the applicable qualified products list before contract award (see 4.3 and 6.3). Cleaning co
27、mpounds shall meet the requirements in table I. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-PRF-85570E 5 TABLE I. Physical properties. Property Requirement Test Method Dilution COMPOSITION Composition No carcinogens1/, toxic pollutants2/ or o
28、zone depleting substances3/. Type IA shall be a 1:4 dilution of a qualified type I product in an aerosol package. Type II RTU shall be a 1:4 dilution of a qualified Type II product in a 32oz pump spray or 5 gallon can. Manufacturer Certification pH Type II RTU 7.0 to 10.0 ASTM E70 As received and 9/
29、 As received Non-volatile content Record value 4.5.9 As received Water content Record value ASTM D95 As received Infrared spectrogram Record spectrogram of non-volatile matter ASTM E168 Rubber content (type IV only) 10.0 to 15.0 percent by weight particulate rubber Manufacturer certification Solvent
30、 content, maximum weight percent type I, IA, and IV type II type V 10.0 percent aromatic, 32.0 percent total solvent 1.0 percent total solvent 10.0 percent total solvent, no aromatics Manufacturer certification As received Net weight (Type IA) Type II RTU Net weight for a 16 and 20 fluid ounce can s
31、hall be no less than 13 and 17 ounces respectively. Nominal 32 ounces 4.5.16 SAFETY & ENVIRONMENTAL Toxicity No adverse effect on the health of personnel when used for its intended purpose Manufacturer certification Flash point, Pensky-Martens 140 F (60 C), minimum ASTM D93 As received Biodegradabil
32、ity (types II and V) 85 percent in 28 days, minimum 40CFR 796.3100 Flame extension (type IA only) Less than 6 inches ASTM D3065 As received MATERIAL COMPATIBILITY Sandwich corrosion Type II RTU Rating of 1 or less ASTM F1110 As received and 9/ As received Cadmium corrosion Type II RTU 0.20 mg/sq. cm
33、/24hrs wt change, maximum ASTM F1111 As received and 9/ As received Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-PRF-85570E 6 TABLE I. Physical properties Continued. Property Requirement Test Method Dilution Total immersion corrosion Al 4/ , T
34、i5/ , Steel 6/ Mg 7/ Type II RTU No visible corrosion and 0.04 mg/sq. cm/24hrs wt. change, maximum 0.20 mg/sq. cm/24hrs wt. change, maximum ASTM F483 As received and 9/ As received Hydrogen embrittlement Type II RTU No failures in less than 150 hours when specimens are loaded to 45 percent of fractu
35、re strength and immersed in cleaner. ASTM F519, type 1A specimens. Cadmium plated in accordance with (IAW) Table II, Treatment B. As received and 9/ As received Unpainted surfaces, effect on No streaks or stains ASTM F485 9/ Painted surfaces, effect on No softening in excess of 1 pencil hardness AST
36、M F502 As received and 9/ Plastics, effect on Acrylic, type A (Cleaner types I, IA,II,II RTU, III, and IV only) Acrylic, type A (type V) Acrylic, type C Type II RTU & Type III No crazing after 8 hours No crazing after 4 hours No crazing after 8 hours 4.5.10 and ASTM F484 Diluted 1:1 with distilled w
37、ater As received Polyimide insulated wire, effect on No dielectric leakage, no visual effect greater than that of distilled water 4.5.11 As received Abrasiveness type III type IV No more than 10 percent gloss reduction 0.5 increase in gloss, maximum 4.5.1 As received PERFORMANCE Cleaning efficiency
38、type I, II, and IV type II RTU type I and IV Not less than 5% of a freshly made control formula cleaning efficiency on hydraulic fluid and grease soils Not less than 5% of a freshly made control formula cleaning efficiency on wire rope lubricant soil 8/ 4.5.4 9/ As received Cleaning efficiency, type
39、 IA only Not less than 5% of a freshly made type I control formula diluted 1:4, on hydraulic fluid and grease soils 8/ 4.5.4 As ReceivedProvided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-PRF-85570E 7 TABLE I. Physical properties Continued. Property
40、Requirement Test Method Dilution Embedded soil cleaning efficiency, type III Complete removal of embedded carbon black 4.5.15 As received Cleaning of vertical surfaces, type V Complete removal of wire rope lubricant soil or comparable to control 4.5.5 As received Foaming properties, type I and II 80
41、 ml liquid after 6 minutes, maximum 4.5.7 9/ Consistency type IV type V 10 to 20 cm flow in 10 seconds 13 to 23 cm flow in 10 seconds 4.5.6 As received Sprayability, type I and V Uniform spray when applied from finger pump spray bottle or aerosol. Type V clings to vertical panel Visual As received S
42、ervice evaluation (when required) Satisfactory 4.5.13 Leakage, type IA only Aerosol cans shall not leak nor become distorted 4.5.17 STABILITY Appearance Homogeneous, no foreign matter Visual As received Low temperature stability No separation 4.5.8 As received Accelerated storage stability No separa
43、tion or effect on steel strip. Cleaning efficiency shall be no less than 5% of a freshly made control formula. 8/ Particulate matter in types III and IV shall not settle or float appreciably. 4.5.2 As received Storage stability After one years storage: No cleaner separation, crystallization, or dete
44、rioration. No container incompatibility, corrosion, distortion, or leakage. Shall meet qualification requirements for cleaning efficiency, sandwich corrosion, cadmium corrosion, total immersion corrosion, hydrogen embrittlement, pH, foaming properties, and appearance. 4.5.14 & ASTM F1104 As received
45、 1/ As specified by the National Toxicology Programs Annual Report on Carcinogens2/ As specified in 40 CFR 4013/ As specified in 40 CFR 82. 4/ Aluminum alloy: SAE AMS-QQ-A-250/12 5/ Titanium: SAE AMS4911(6Al-4V alloy) 6/ Steel: SAE AMS5046 (1020 alloy) 7/ Magnesium alloy: SAE AMS4377, Chrome Pickled
46、: SAE AMS-M-3171, type VI 8/ Freshly made control formula is not more than six weeks old. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-PRF-85570E 8 9/ Unless otherwise specified dilute with distilled water (volume concentrate: volume water): t
47、ype I (1:9), type II (1:14), type III (not diluted), type IV (not diluted), type V (not diluted) 3.2 Product identification and instructions for use. All containers of cleaning compound shall be clearly labeled with the manufacturers name and product designation, date of manufacture, and pH of the c
48、leaning compound. Labels containing direction for use shall be on each container. Labels shall contain the following instructions as applicable: 3.2.1 Type I. EXTERIOR AIRCRAFT CLEANER, GENERAL PURPOSE, AROMATIC SOLVENT, MIL-PRF-85570, TYPE I Directions for use: Light soils: Mix 1 part cleaner in 14
49、 parts water Moderate soils: Mix 1 part cleaner in 9 parts water Heavy soils: Mix 1 part cleaner in 4 parts water Apply with foam generator (see NAVAIR 01-1A-509, Section 2), spray, sponge, brush, or cloth. Scrub, then rinse with fresh water. 3.2.2 Type IA. EXTERIOR AIRCRAFT CLEANER, GENERAL PURPOSE, AROMATIC SOLVENT, AEROSOL, MIL-PRF-85570, TYPE IA Directions for use: