1、_ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there
2、 from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your written comments and suggestions. Copyright 2010 SAE International All rights reserved. No part of this publication
3、may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-4970 (outside
4、USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS3678/3AAEROSPACEMATERIALSPECIFICATIONAMS3678/3 REV. A Issued 1999-03 Reaffirmed 2006-06Re
5、vised 2010-11 Superseding AMS3678/3 Type 3 15% Glass, 5% Molybdenum Disulfide Filled Virgin Polytetrafluoroethylene (PTFE) Moldings or Extrusions RATIONALE This document is being revised to clear up some editorial issues and to maintain the same revision date for AMS3678 and all the accompanying sla
6、sh sheets. 1. SCOPE 1.1 Form This specification covers a polytetrafluoroethylene (PTFE) resin filled with 15% glass fiber and 5% molybdenum disulfide in the form of extruded or molded rods or tubes which are sintered after molding or, in the case of extrusions, sintered during the extrusion process.
7、 1.2 Application These products have been used typically for seal components requiring high temperature and pressure resistance and dimensional stability up to 450 F (232 C) with good wear resistance, but usage is not limited to such applications. Each application should be considered individually.
8、2. APPLICABLE DOCUMENTS See AMS3678. 3. TECHNICAL REQUIREMENTS 3.1 Basic Specification The complete requirements for procuring the products described herein shall consist of this document and the latest issue of the basic specification, AMS3678. Copyright SAE International Provided by IHS under lice
9、nse with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-SAE AMS3678/3A Page 2 of 23.2 Material All products shall be molded or extruded from virgin polytetrafluoroethylene (PTFE) powder conforming to ASTM D 4894, Type II or Type IV, uniformly blended with the s
10、pecified fillers. The blended powder shall consist of 15% 2 milled glass fibers, 5% 2 molybdenum disulfide, and the remainder virgin PTFE powder, filler percentages measured by weight. 3.2.1 Fillers 3.2.1.1 Glass It is recommended that the milled glass fiber should be E-glass produced through a 14 m
11、icron die, then hammer milled, and finally passed through a 0.032 inch screen. 3.2.1.2 Molybdenum Disulfide It is recommended that a commercial grade of molybdenum disulfide is used with a particle size range of 1 to 100 m, median particle size of 30 m. 3.3 Properties The product shall conform to th
12、e requirements shown in Table 1. TABLE 1 - MATERIAL PROPERTY REQUIREMENTS Property Requirement Test Method 3.3.1 Tensile Strength, min 2000 psi (13.8 MPa) ASTM D 4745 3.3.2 Elongation, min 180% ASTM D 4745 3.3.3 Specific Gravity 2.15 to 2.30 ASTM D 792 3.3.4 Dimensional Stability 0.002 inch per 1 in
13、ch, max measured on circumference 4.5.3.1 of AMS3678 3.3.5 Color Gray 4. QUALITY ASSURANCE PROVISIONS See AMS3678. 5. PREPARATION FOR DELIVERY See AMS3678. 6. ACKNOWLEDGMENT See AMS3678. 7. REJECTIONS See AMS3678. 8. NOTES See AMS3678. PREPARED BY AMS COMMITTEE “P” Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-