1、AECMA STANDARD prEN 4800-6 NORME AECMA Edition P 1 AECMA NORM September 2002 k!EJmbsTAm Gulledelle 94 - 8-1200 Brussels - Tel. + 32 2 775 81 10 - Fax. + 32 2 775 81 11 - www.aecma-stan.org PUBLISHED BY THE EUROPEAN ASSOCIATION OF AEROSPACE INDUSTRIES - STANDARDIZATION Edition approved for publicatio
2、n Comments should be sent within six months after the date of publication to Gulledelle 94 30 September 2002 AECMA-STAN 8-1200 BRUXELLES ICs: Descriptors: Material Domain ENGLISH VERSION Aerospace series Titanium and titanium alloys Technical specification Part 6: Pre-production and production forgi
3、ngs Srie arospatiale Luft- und Raumfahrt Titane et alliages de titane Partie 6: Pices types et pices de srie, forges et matrices Titan und Titanlegierungen Kneterzeugnisce Teil 6: Ausfallmuster- und Serienschmiedestcke Spcification technique Technische Lieferbedingungen This “Aerospace Series“ Prest
4、andard has been drawn up under the responsibility of AECMA-STAN (The European Association of Aerospace Industries - Standardization). It is published on green paper for the needs of the European Aerospace Industry. It has been technically approved by the experts of the concerned Domain following mem
5、ber comments. Subsequent to the publication of this Prestandard, the technical content shall not be changed to an extent that interchangeability .is affected, physically or functionally, without re-identification of the standard. After examination and review by users and formal agreement of AECMA-ST
6、AN it will be submitted as a draff European Standard to CEN (European Committee for Standardization) for formal vote. Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without licens
7、e from IHS-,-,-Page 2 prEN 4800-6: 2002 Contents Page O Introduction _. . . . . . . . . . . . . . . . . . . . . , . . . . . . . . . . . . . . . . . . . . , . , . , , . . . . . . . . . . . . . . . . . . . , , , . , . . . . , . . . , , , , , . , . . , . . . . . . . . . . . . . . . . . . . . . . . . .
8、, . . . . , ._. 3 1 Scope 3 2 Normative references 3 3 Definitions . 4 4 Wording of order _._._._. 4 5 Health and safety 5 6 Technical requirements . . . 5 . . . ._. , . . . , , . , . ._ _. Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with A
9、ECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-Page 3 prEN 4800-6: 2002 O Introduction This standard is part of the series of EN metallic material standards for aerospace applications. The general organization of this series is described in EN 4258. 1 Scope Th
10、is standard defines the requirements for the ordering, manufacture, testing, inspection and delivery of titanium and titanium alloy pre-production and production forgings. It shall be applied when referred to and in conjunction with the EN material standard unless otherwise specified on the drawing,
11、 order or inspection schedule. 2 Normative references This European Standard incorporates by dated or undated reference provisions from other publications. These normative references are cited at the appropriate places in the text and the publications are listed hereafter. For dated references, subs
12、equent amendments to or revisions of any of these publications apply to this European Standard only when incorporated in it by amendment or revision. For undated references the latest edition of the publication referred to applies. EN 2000 EN 2002-1 EN 2002-2 EN 2002-5 EN 2002-8 EN 2002-16 EN 2003-9
13、 EN 2032-1 EN 2032-2 EN 2078 EN 2954-2 EN 3042 EN 31 14-1 EN 31 14-2 Aerospace series - Quality assurance - EN aerospace products - Approval of the quality system of manufacturers Aerospace series - Test methods for metallic materials - Part 1 : Tensile testing at ambient temperature 1) Aerospace se
14、ries - Test methods for metallic materials - Part 2: Tensile testing at elevated temperature 1) Aerospace series - Test methods for metallic materials - Part 5: Uninterrupted creep and stress-rupture testing 1) Aerospace series - Metallic materials - Test methods - Part 8: Micrographic determination
15、 of grain size 1) Aerospace series - Metallic materials - Test methods - Part 16: Non-destructive testing - Penetrant testing 1) Aerospace series - Test methods - Titanium and titanium alloys - Part 9: Determination of surface contamination 1) Aerospace series - Metallic materials - Part 1 : Convent
16、ional designation Aerospace series - Metallic materials - Part 2: Coding of metallurgical condition in delivery condition Aerospace series - Metallic materials - Manufacturing schedule, inspection schedule, inspection and test report - Definition, general principles, preparation and approval Aerospa
17、ce series - Macrostructure of titanium and titanium alloy wrought products - Part 2: Macrostructure of bar, section, forging stock and forgings 2) Aerospace series - Quality assurance - EN aerospace products - Qualification procedure Aerospace series - Test method - Microstructure of (a + ) titanium
18、 alloy wrought products - Part I : General requirements 1) Aerospace series - Test method - Microstructure of (a + ) titanium alloy wrought products - Part 2: Microstructure of bars, sections, forging stock and forgings 1) Copyright Association Europeene des Constructeurs de Materiel Aerospatial Pro
19、vided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-Page 4 prEN 4800-6: 2002 EN 3683 EN 3874 EN 3976 EN 3987 EN 3988 EN 4050-1 EN 4050-4 EN 4258 EN 4259 EN 4268 EN 4800-5 TR 2410 Aerospace series - Test methods - Titanium alloy wrou
20、ght products - Determination of primary a content - Point count method and line intercept method 1) Aerospace series - Test methods for metallic materials - Constant amplitude force- controlled low cycle fatigue testing 1) Aerospace series - Titanium and titanium alloys - Test method - Chemical anal
21、ysis for the determination of hydrogen content 1) Aerospace series - Test method for metallic materials - Constant amplitude force- controlled high cycle fatigue testing 2) Aerospace series - Test methods for metallic materials - Constant amplitude strain- controlled low cycle fatigue testing 1) Aer
22、ospace series - Test method for metallic materials - Ultrasonic inspection of bars, plates, forging stock and forgings - Part 1 : General requirements 1) Aerospace series - Test method for metallic materials - Ultrasonic inspection of bars, plates, forging stock and forgings - Part 4: Acceptance cri
23、teria 1) Aerospace series - Metallic materials - General organization of standardization - Links between types of EN standards and their use Aerospace series - Metallic materials - Definition of general terms 1) Aerospace series - Metallic materials - Heat treatment facilities - General requirements
24、 2) Aerospace series - Titanium and titanium alloys - Technical specification - Part 5: Forging stock Aerospace series - Metallic materials - Relationship between dimensional standards and material standards 3) 3 Definitions General definition, see EN 4259. 4 Wording of order The order shall clearly
25、 indicate: - quantities to be supplied; - dates of delivery; - material standard number; - partnumber; - delivery condition and metallurgical code of products; - dimensions and tolerances or reference to an appropriate dimensional standard; - product designation, when required; - forwarding address;
26、 - nature and type of packing, if required; - definition and frequency of any special tests and their retest procedures, if required. 1) Published as AECMA Prestandard at the date of publication of this standard 2) In preparation at the date of publication of this standard 3) Published as AECMA Tech
27、nical Report at the date of publication of this standard Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-Page 5 prEN 4800-6: 2002 5 Health and safety P
28、roducts in the delivery condition shall fulfil the health and safety laws of the area of the country when and where it is to be delivered. A product safety data sheet shall be available. 6 Technical requirements 6.1 General The product shall satisfy the requirements of the order, drawing inspection
29、schedule or material standard: see table 1, line 5. The order, drawing or inspection schedule shall specify the tests to be performed upon (i) pre-forgings for qualification and/or requalification (i) serial production forgings for process control testing (Procedure X: see section 6.5) and (iii) bat
30、ch release when cut-up testing or forgings is required. Unless otherwise specified on the order, drawing or inspection schedule, acceptance criteria for the tests are stated in the material standard, the requirements for each line of which are detailed in tables 1 and 2 of this technical specificati
31、on. Table 1 related to lines 1 to 29 (inclusive) of the material standard and table 2 relates to lines 30 onwards in which the sub-line format is also used. If a particular test is needed but not shown in a specific line in tables 1 and 2, the requirement shall be specified on the order, drawing, in
32、spection schedule or material standard. 6.2 Qualification requirements See line 1 O0 in table 2 of this technical specification. Qualification shall normally comprise assessment of pre-production forgings. See table 1, section 4.2. 6.3 Re-qualification requirements Re-qualification of serial product
33、ion forgings may be required, at the purchasers discretion, in the following cases: - modification of the drawing; - use of forging stock from a different source; - modifications to the forging stock form and/or manufacturer route; - modifications to an existing die; - use of a new (replacement) die
34、; - modifications to the forging manufacturing route; - use of a new forging manufacturer; - when a significant time interval (usually several years) had elapsed between forging campaigns for a specific part number; - when required by the purchaser for any other reason. Re-qualification testing requ
35、irements, especially location of test pieces, shall be identical to those used for the initial qualification of the pre-production forgings unless otherwise specified on the order, drawing or inspection schedule. Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by I
36、HS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-Page 6 prEN 4800-6: 2002 Mass of forging (kg) II I mass I 2 2 25 6.4 Release requirements Release testing shall be the responsibility of the manufacturer. The sampling procedure for release
37、testing shall be one of the following, as specified on the order, drawing or inspection schedule. Where no procedure is specified, procedure A shall be used. - Procedure A: Separate forged test samples shall be produced from the same batch of forging stock as that used to make the serial production
38、forgings. Procedure A may be used alone unless denoted AX on the drawing, order or inspection schedule in which case it shall be applied only in conjunction with procedure X (See section 6.5). - Procedure B: Separate forged heat treatment control test samples shall be prepared which conform to the s
39、ame material standard as the production forgings, but may originate from a different batch of forging stock. Procedure B shall only be used when full heat treatment of the serial production forgings is carried out by the manufacturer and only in conjunction with procedure X (See section 6.5). - Proc
40、edure C: Integral test samples shall be removed from each forgings. The order, drawing of inspection schedule shall specify how many test samples shall be tested per batch. Procedure C may be used alone unless denoted CX on the drawing, order or inspection schedule in which case it shall be applied
41、only in conjunction with procedure X (See section 6.5). - Procedure D: Test samples shall be machined from forging(s) selected from each production batch and at locations specified on the order, drawing or inspection schedule. The purchaser reserves the right to perform any of the inspections and/or
42、 tests required by the material standard, drawing, order or inspection schedule. When required, the manufactured shall inform the purchaser of the planned dates for extraction of samples and release testing in order that these operations may be witnessed. Number of forgings 5 2 O00 I1 O00 I400 I 200
43、 As stated on the order, drawing, inspection schedule 6.5 Procedure X is process control procedure consisting of periodic “cut-up” testing to ensure that the serial production forgings continues to conform to the specified requirements. If procedure X is invoked by the order, drawing or inspection/m
44、anufacturing schedule and/or if procedures B, AX or CX are used for release tests (see section 6.4), forgings shall be selected from series production at the frequency stated therein. It is recommended that the maximum number of forgings manufactured between repeat “cut-up” testing conforming to pro
45、cedure X shall be as stated in the following table: Process control testing (Procedure X) The testing requirements, including the location, type and size of test pieces shall be identical to those used for qualification of the pre-production. 6.6 Re tests Retests shall be required if the specified a
46、cceptance criteria are not fully met during qualification testing of pre-production forgings, process control testing (procedure X) or batch release testing. If the test product or test piece preparation is faulty, testing shall be re-applied at the original frequency after rectification of the orig
47、inal cause of failure. At least one of the retests shall be from forgings from which the unsatisfactory result was obtained (unless already rejected by the manufacturer after suitable identification of the cause of failure). It insufficient material remains, the purchaser shall advise as to how to p
48、roceed. If all retest results fulfil the specified acceptance criteria, the pre-production forging qualification/process control test (procedure X) shall be deemed satisfactory or the batch shall be accepted, as appropriate. Copyright Association Europeene des Constructeurs de Materiel Aerospatial P
49、rovided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-Page 7 prEN 4800-6: 2002 If one or more retest results fail to fulfil the specified acceptance criteria, the following actions shall be taken: a) For qualification testing of pre-production forgings, advice shall be sought from the purchaser as to whether the retest results are acceptable for that part of the forging. If so,