1、ASD STANDARD NORME ASD ASD NORM prEN 4800-005 Edition P 2 September 2009 PUBLISHED BY THE AEROSPACE AND DEFENCE INDUSTRIES ASSOCIATION OF EUROPE - STANDARDIZATIONAvenue de Tervuren, 270 - B-1150 Brussels - Tel. + 32 2 775 8126 - Fax. + 32 2 775 8131 - www.asd-stan.orgICS: Supersedes edition P 1 of S
2、eptember 2002 Descriptors: ENGLISH VERSION Aerospace series Titanium and titanium alloys Technical specification Part 005: Forging stock Srie arospatiale Titane et alliages de titane Spcification technique Partie 005 : Produits destins la forge Luft- und Raumfahrt Titan und Titanlegierungen Kneterze
3、ugnisse Technische Lieferbedingungen Teil 005: Schmiedevormaterial This “Aerospace Series“ Prestandard has been drawn up under the responsibility of ASD-STAN (The AeroSpace and Defence Industries Association of Europe - Standardization). It is published for the needs of the European Aerospace Indust
4、ry. It has been technically approved by the experts of the concerned Domain following member comments. Subsequent to the publication of this Prestandard, the technical content shall not be changed to an extent that interchangeability is affected, physically or functionally, without re-identification
5、 of the standard. After examination and review by users and formal agreement of ASD-STAN, it will be submitted as a draft European Standard (prEN) to CEN (European Committee for Standardization) for formal vote and transformation to full European Standard (EN). The CEN national members have then to
6、implement the EN at national level by giving the EN the status of a national standard and by withdrawing any national standards conflicting with the EN. Edition approved for publication 30 September 2009 Comments should be sent within six months after the date of publication to ASD-STAN Metallic Mat
7、erial Domain Copyright 2009 by ASD-STAN prEN 4800-005:2009 (E) 2 Contents Page Foreword2 Introduction .3 1 Scope 3 2 Normative references 3 3 Terms and definitions .4 4 Wording of order5 5 Health and safety .5 6 Technical requirements 5 Foreword This standard was reviewed by the Domain Technical Coo
8、rdinator of ASD-STANs Metallic Material Domain. After inquiries and votes carried out in accordance with the rules of ASD-STAN defined in ASD-STANs General Process Manual, this standard has received approval for Publication. prEN 4800-005:2009 (E) 3 Introduction This standard is part of the series o
9、f EN metallic material standards for aerospace applications. The general organization of this series is described in EN 4258. 1 Scope This standard defines the requirements for the ordering, manufacture, testing, inspection and delivery of titanium and titanium alloy forging stock. It shall be appli
10、ed when referred to and in conjunction with the EN material standard unless otherwise specified on the drawing, order or inspection schedule. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited
11、 applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 2002-001, Aerospace series Metallic materials Test methods Part 001: Tensile testing at ambient temperature EN 2002-002, Aerospace series Metallic materials Test methods Part 002: T
12、ensile testing at elevated temperature EN 2002-005, Aerospace series Test methods for metallic materials Part 005: Uninterrupted creep and stress-rupture testing EN 2002-8, Aerospace series Metallic materials Test methods Part 8: Micrographic determination of grain size 1)EN 2003-009, Aerospace seri
13、es Test methods Titanium and titanium alloys Part 009: Determination of surface contamination EN 2032-1, Aerospace series Metallic materials Part 1: Conventional designation. EN 2032-2, Aerospace series Metallic materials Part 2: Coding of metallurgical condition in delivery condition. EN 2078, Aero
14、space series Metallic materials Manufacturing schedule, inspection schedule, inspection and test report Definition, general principles, preparation and approval. EN 2954-002, Aerospace series Macrostructure of titanium and titanium alloy wrought products Part 002: Macrostructure of bar, section, for
15、ging stock and forgings EN 2955, Aerospace series Recycling of titanium and titanium alloy scrap EN 2957, Aerospace series Method of preparation of forged samples 1) Published as ASD Prestandard at the date of publication of this standard. prEN 4800-005:2009 (E) 4 EN 3114-001, Aerospace series Test
16、method Microstructure of ( + ) titanium alloy wrought products Part 001: General requirements EN 3114-002, Aerospace series Test method Microstructure of ( + ) titanium alloy wrought products Part 002: Microstructure of bars, sections, forging stock and forgings EN 3683, Aerospace series Test method
17、 Titanium alloy wrought products Determination of primary content Point count method and line intercept method EN 3684, Aerospace series Test method Titanium alloy wrought products Determination of transus temperature Metallographic method EN 3874, Aerospace series Test methods for metallic material
18、s Constant amplitude force-controlled low cycle fatigue testing 1)EN 3976, Aerospace series Titanium and titanium alloys Test method Chemical analysis for the determination of hydrogen content EN 3987, Aerospace series Test method for metallic materials Constant amplitude force-controlled high cycle
19、 fatigue testing 1)EN 3988, Aerospace series Test methods for metallic materials Constant amplitude strain-controlled low cycle fatigue testing 1) EN 4050-1, Aerospace series Test method for metallic materials Ultrasonic inspection of bars, plates, forging stock and forgings Part 1: General requirem
20、ents 1) EN 4050-4, Aerospace series Test method for metallic materials Ultrasonic inspection of bars, plates, forging stock and forgings Part 4: Acceptance criteria 1) EN 4258, Aerospace series Metallic materials General organization of standardization Links between types of EN standards and their u
21、se EN 4259, Aerospace series Metallic materials Definition of general terms 1)EN 9100, Aerospace series Quality management systems Requirements (based on ISO 9001:2000) and Quality systems Model for quality assurance in design, development, production, installation and servicing (based on ISO 9001:1
22、994) EN 9133, Aerospace series Quality management systems Qualification Procedure for aerospace standard parts EN ISO 12737, Metallic materials Determination of plane-strain fracture toughness TR 2410, Aerospace series Metallic materials Relationship between dimensional standards and material standa
23、rds 2)ASTM E 647, Standard test method for measurement of fatigue crack growth rates 3) AMS 2750, Pyrometry 3)2) Published as ASD Technical Report at the date of publication of this standard. 3) Published by: American Society for Testing and Materials (ASTM), 100 Barr Harbor Drive, PO Box C700, West
24、 Conshohocken, PA, 19428-2959 USA. prEN 4800-005:2009 (E) 5 3 Terms and definitions For the purposes of this document, the terms and definitions given in EN 4259 apply. 4 Wording of order The order shall clearly indicate: quantities to be supplied; dates of delivery; material standard number; delive
25、ry condition and metallurgical code of products; dimensions and tolerances or reference to an appropriate dimensional standard; product designation, when required; forwarding address; nature and type of packing, if required; definition and frequency of any special tests and their retest procedures,
26、if required. 5 Health and safety Products in the delivery condition shall fulfil the health and safety laws of the area of the country when and where it is to be delivered. A product safety data sheet shall be available. 6 Technical requirements 6.1 General The product shall be manufactured in accor
27、dance with the requirements of the relevant material standard and the applicable requirements of this specification. A manufacturing schedule shall be established and applied in accordance with EN 2078. Product shall satisfy the requirements of the material standard and/or order and shall be free fr
28、om irregularities prejudicial to the subsequent manufacture or use of this product. Not with standing previous acceptance complying with this material standard, any product that is found, at a later stage, to contain such defects shall be rejected. Unless otherwise specified, the requirements in Tab
29、les 1 and 2 shall apply in conjunction with those of the relevant material standard. Table 1 relates to lines 1 to 29 (inclusive) of the material standard and Table 2 relates to lines 30 onwards in which the subline format is also used. Lines 2 to 98 may also be opened in line 100 if the material st
30、andard details specific qualification requirements. If a specific line number is not shown in Tables 1 and 2, the requirement is stated in the material standard and/or order. The requirements of the order and/or material standard shall over-ride the requirements of the technical specification. prEN
31、4800-005:2009 (E) 6 6.2 Qualification requirements Qualification requirements when invoked by the material standard and/or order are detailed in Tables 1 and 2. Unless otherwise agreed between the manufacturer and purchaser the qualification phase shall be run on the first 3 batches. 6.3 Release req
32、uirements 6.3.1 Release tests Release testing shall be the responsibility of the manufacturer. The purchaser reserves the right to perform any of the inspections and/or tests required by the material standard and/or order. The test samples shall be representative of the product. When required the ma
33、nufacturer shall inform the purchaser of the planned dates for extraction of samples and release testing in order that these operations may be witnessed. Tables 1 and 2 detail the requirements for each line of the material standard. Unless otherwise specifically requested by the purchaser, a particu
34、lar inspection and/or test for release shall be carried out if corresponding acceptance criteria and/or values are stated in the applicable material standard, but see also in 6.3.5. 6.3.2 Retests If the test procedure or test piece preparation is faulty, testing shall be re-applied at the original f
35、requency after rectification of the original cause of failure. When failure cannot be attributed to faulty testing, or test piece preparation, further test samples shall be selected at twice the original frequency from the product, one of which shall be that on which the original results were obtain
36、ed unless already withdrawn by the manufacturer after suitable identification of the cause of failure. If all retest results are satisfactory, the batch shall be accepted. If one or more tests are unsatisfactory, the batch shall be: rejected, or 100 % retested and the conforming products accepted, o
37、r partially or fully re-heat treated if heat treatment can rectify the cause of the failure and tested as a completely new batch except for chemical composition, for which redetermination of hydrogen content is required. No product or test sample shall be re-heat treated more than twice, or cut back
38、 and 100 % retested. 6.3.3 Rejection Any failure to meet the requirements of the material standard shall be cause for rejection. 6.3.4 Special tests Special tests may be required by the purchaser. In such cases, the nature of the test, method, frequency and technical requirements shall be specified
39、on the order or inspection schedule and shall be mutually agreed by the manufacturer and purchaser. prEN 4800-005:2009 (E) 7 6.3.5 Capability clause Where capability clause is invoked and where sufficient statistical evidence exists, the test need not be carried out (unless specifically requested by
40、 the purchaser). However, this in no way reduces the obligations of the manufacturer to fulfil the requirements. If subsequent testing indicates that the product does not comply with the requirements, the batch shall be rejected. If sufficient statistical evidence does not exist, the test shall be c
41、arried out at a frequency agreed between the manufacturer and the purchaser. 6.3.6 Statistical process control Reduction in the extent of release testing, other than that defined in 6.3.5 above, may be negotiated with the purchaser on the basis of appropriate statistical process control and/or stati
42、stical data. 6.3.7 Inspection and test report The manufacturer shall furnish, with each delivery, a report conforming to the requirements of EN 2078 stating the following: manufacturers name and address and, if appropriate, identification of the plant; order number; material standard number; deliver
43、y condition and metallurgical code of the product; quantity and dimensions; manufacturing and inspection schedule reference; cast and batch number; batch and/or test samples heat treatment conditions; results of the tests and retests if any. 6.4 Traceability Each product shall be traceable to the ca
44、st, production batch and/or heat treatment batch at all stages of manufacture, testing and delivery. prEN 4800-005:2009 (E) 8 Table 1 Technical requirements for lines 1 to 29, where appropriate Frequency of testing Material standard line reference No Title Requirements Qualification Release 1 Materi
45、al designation See EN 2032-1. The test samples used for chemical analysis shall be representative of the product and shall be taken from location corresponding to top and bottom of each ingot produced after the final melting stage. The method of chemical analysis shall be at the discretion of the ma
46、nufacturer unless otherwise stated in the material standard or order. In cases of dispute, the method of chemical analysis shall be agreed between the manufacturer and purchaser preferably using existing chemical analysis standards. The measured chemical composition shall be stated on the inspection
47、 certificate. 2 per cast 2 per cast 2 Chemical composition Specific requirements for hydrogen content: The hydrogen content shall be determined on each batch in the delivery condition in accordance with EN 3976. 1 per batch 1 per batch 3 Method of melting Method of melting shall consist of Cold Hear
48、th (Electron Beam or Plasma Arc) and/or Consumable Electrode Vacuum Arc Melting. An initial non-consumable electrode melt is allowed provided a water cooled electrode is used. Some of the following requirements depend on whether the melting method includes Cold Hearth. 1 Raw material: Raw materials
49、shall be purchased only from suppliers approved by the manufacturer and registered in his list of approved suppliers. Approval of suppliers shall be made in accordance with written procedures contained within the quality assurance system of the manufacturer. Titanium sponge and alloying elements: The requirements shall be specified by the manufacturer who shall also establish the following proc