1、Designation:D695(Reapproved 2006)American Association StateHighway and Transportation Officials StandardAASHTO No.: T47Standard Test Method forLoss on Heating of Oil and Asphaltic Compounds1This standard is issued under the fixed designation D 6; the number immediately following the designation indi
2、cates the year of originaladoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscriptepsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies o
3、f the Department of Defense.1. Scope1.1 This test method covers the determination of the loss inmass (exclusive of water) of oil and asphaltic compounds whenheated as hereinafter prescribed.1.2 The values in SI units are to be regarded as standard.The values in parentheses are for information only.1
4、.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility and regulatory limitations prior to use.2. Referenced D
5、ocuments2.1 ASTM Standards:2D5 Test Method for Penetration of Bituminous MaterialsE1 Specification for ASTM Liquid-in-Glass ThermometersE 145 Specification for Gravity-Convection and Forced-Ventilation Ovens3. Summary of Test Method3.1 Fifty grams of material, spread out in a dish 55 mm indiameter,
6、is heated in moving air for 5 h at 163C (325F) andthe percent loss of mass determined along with a comparison,before and after, of any other desired characteristics. This testmethod provides only a relative measurement of the volatilityof a material under test conditions.4. Significance and Use4.1 T
7、his test method is useful in characterizing certainpetroleum products by the determination of their loss of massupon heating under standardized conditions.5. Apparatus5.1 OvenThe oven shall be electrically heated and shallconform to the performance requirements of SpecificationE 145 Type I, Grade B,
8、 for operating temperatures up to 180C(365F). During the tests for compliance to Specification E 145requirements, the oven shelf, properly placed, shall be in placeand rotating. In addition, it shall also comply with thefollowing requirements:5.1.1 Construction (Note 1)The oven shall be rectangularw
9、ith minimum interior dimensions of 330 mm (13 in.) in eachdirection. The oven shall have in front a tightly fitting hingeddoor, which shall provide a clear opening substantially thesame as the interior height and width of the oven. The doormay contain a window with dimensions of at least 100 by 100m
10、m (4 by 4 in.), and with two sheets of glass separated by anair space, through which a vertical thermometer located asspecified in Section 8, may be read without opening the door;or the oven may be provided with an inner glass door, throughwhich the thermometer may be observed on opening the outerdo
11、or momentarily. The oven shall be adequately ventilated byconvection currents of air and for this purpose shall beprovided with openings for the entrance of air and for the exitof heated air and vapors. Openings may be of any size andarrangement provided the requirements of Specification E 145,Type
12、I, Grade B, are met.5.1.2 Rotating ShelfThe oven shall be provided with acircular metal shelf having a minimum diameter of 250 mm(9.8 in.). (A recommended form of aluminum shelf is shown inFig. 1.) The shelf shall be suspended by a vertical shaft andcentered with respect to the horizontal interior d
13、imensions. Theshelf shall be provided with a mechanical means of rotating itat the rate of 5 to 6 rpm. The shelf shall be vertically locatedas close to the center of the oven as permitted by compliancewith the requirements of 7.2 regarding thermometer placement.NOTE 1Continued use of existing smalle
14、r ovens complying with therequirements of this test shall be permitted for an indefinite period toprovide for normal amortization of present equipment. However, all newovens purchased should comply with the minimum dimensions andrequirements of this test method.1This test method is under the jurisdi
15、ction ofASTM Committee D08 on Roofingand Waterproofing and is the direct responsibility of Subcommittee D08.03 onSurfacing and Bituminous Materials for Membrane Waterproofing and Built-upRoofing.Current edition approved Dec. 1, 2006. Published December 2006. Originallyapproved in 1910. Last previous
16、 edition approved in 2000 as D695(2000)e1.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM Int
17、ernational, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5.2 ThermometerAn ASTM Loss on Heat Thermometergraduated in Celsius degrees, having a range from 155 to170C and conforming to the requirements for Thermometer13C as prescribed in the Specification E1.5.3
18、ContainerThe container in which the sample is to betested shall be of metal or glass, cylindrical in shape, and shallhave a flat bottom. Its inside dimensions shall be substantiallyas follows: diameter, 55 mm (2.17 in.), depth, 35 mm (1.38in.).NOTE 2Containers known in the drug trade as seamless “oi
19、ntmentboxes” may be obtained in dimensions conforming to the above require-ments.6. Technical Hazards6.1 Under ordinary circumstances a number of sampleshaving about the same degree of volatility may be tested at thesame time. Samples varying greatly in volatility should betested separately. When ex
20、treme accuracy is required not morethan one material should be tested at one time and duplicatesamples of it should be placed simultaneously in the oven.Such duplicates shall check within the limits of accuracy givenin Section 9. Results obtained on samples showing evidencesof foaming during the tes
21、t shall be rejected.7. Preparation of Sample7.1 Thoroughly stir and agitate the sample as received,warming, if necessary, to obtain a complete mixture before theportion for analysis is removed.7.2 First test the material under examination for water and,if water is present, remove it by suitable meth
22、ods of dehydra-tion before subjecting the material to the loss on heating test;or, obtain another sample that is free of water.8. Procedure8.1 Place 50.0 6 0.5 g of the sample of the water-freematerial to be tested in a tared container conforming to therequirements of 5.3, and weigh to the nearest 0
23、.01 g. If thematerial has been heated to facilitate transfer, cool the sampleto room temperature before making this initial weighing. Bringthe oven to a temperature of 163C (325F), and place thecontainer with the weighed sample on and near the circumfer-ence of the circular shelf, in one of the rece
24、sses if therecommended shelf is used. Close the oven and rotate the shelfduring the entire test at a rate of 5 to 6 rpm. Maintain thetemperature at 163 6 1C (325 6 1.8F) for 5 h after thesample has been introduced and the oven has again reachedthat temperature. The 5-h period shall start when the te
25、mpera-ture reaches 162C (324F), and in no case shall the total timethat a sample is in the oven be more than 5 h and 15 min. Atthe conclusion of the heating period, remove the sample fromthe oven, cool to room temperature, weigh to the nearest 0.01g, and calculate the loss due to heating.8.2 Determi
26、ne temperatures by means of the specifiedthermometer, which shall be supported from the shaft of thecircular shelf in a vertical position approximately 19 mm (0.75in.) inside the periphery of the shelf, and with the bottom of thethermometer bulb 6 mm (0.25 in.) above the shelf.NOTE 3If additional pe
27、riods of heating are desired, it is recommendedthat they be made in successive increments of 5 h each.NOTE 4When it is required that the penetration or other characteris-tics of the sample after heating be determined, the residue should bemelted in the container at the lowest possible temperature an
28、d thoroughlyMetric Equivalentsin.mm1161.69643.6146.45167.923649.1153211.91212.73419.01153237.311238.12151674.6478123.8FIG. 1 Aluminum ShelfTABLE 1 Reproducibility of ResultsVolatilization Loss, % Numerical Correction True Volatilization Loss, %5.0 60.50 4.50 to 5.505.5 60.51 4.99 to 6.016.0 60.52 5.
29、48 to 6.5210.0 60.60 9.40 to 10.6015.0 60.70 14.30 to 15.7025.0 60.90 24.10 to 25.9040.0 61.20 38.80 to 41.20D695(2006)2mixed by stirring, taking care to avoid incorporating air bubbles in thematerial. For the penetration test, the well-mixed residue shall be broughtto standard temperature and teste
30、d as prescribed in Test Method D5. Forother tests, the well-mixed residue should be tested according to standardconditions as required by the test procedure involved.9. Precision and Bias9.1 Up to 5 % loss in mass, the results obtained may beconsidered as correct within 0.5. Above 5 % loss in mass,
31、thenumerical limit of error increases 0.01 for every 0.5 % increasein loss by volatilization as shown in Table 1.9.2 BiasThe procedure in Test Method D 6 has no biasbecause the value of the loss on heating of oil and asphalticcompounds test, is defined in terms of the test method.10. Keywords10.1 as
32、phalt; heating; oil; ovenASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infring
33、ement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard
34、or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views
35、known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).D695(2006)3