1、Designation: D2837 13 An American National StandardStandard Test Method forObtaining Hydrostatic Design Basis for Thermoplastic PipeMaterials or Pressure Design Basis for Thermoplastic PipeProducts1This standard is issued under the fixed designation D2837; the number immediately following the design
2、ation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This test method describes two
3、essentially equivalentprocedures: one for obtaining a long-term hydrostatic strengthcategory based on stress, referred to herein as the hydrostaticdesign basis (HDB); and the other for obtaining a long-termhydrostatic strength category based on pressure, referred toherein as the pressure design basi
4、s (PDB). The HDB is basedon the materials long-term hydrostatic strength (LTHS),andthe PDB is based on the products long-term hydrostaticpressure-strength (LTHSP). The HDB is a material propertyand is obtained by evaluating stress rupture data derived fromtesting pipe made from the subject material.
5、 The PDB is aproduct specific property that reflects not only the properties ofthe material(s) from which the product is made, but also theinfluence on product strength by product design, geometry, anddimensions and by the specific method of manufacture. ThePDB is obtained by evaluating pressure rup
6、ture data. TheLTHS is determined by analyzing stress versus time-to-rupture(that is, stress-rupture) test data that cover a testing period ofnot less than 10 000 h and that are derived from sustainedpressure testing of pipe made from the subject material. Thedata are analyzed by linear regression to
7、 yield a best-fitlog-stress versus log time-to-fail straight-line equation. Usingthis equation, the materials mean strength at the 100 000-hintercept (LTHS) is determined by extrapolation. The resultantvalue of the LTHS determines the HDB strength category towhich the material is assigned. The LTHSP
8、is similarlydetermined except that the determination is based on pressureversus time data that are derived from a particular product. Thecategorized value of the LTHSPis the PDB. An HDB/PDB isone of a series of preferred long-term strength values. This testmethod is applicable to all known types of
9、thermoplastic pipematerials and thermoplastic piping products. It is also appli-cable for any practical temperature and medium that yieldsstress-rupture data that exhibit an essentially straight-linerelationship when plotted on log stress (pound-force per squareinch) or log pressure (pound-force per
10、 square in. gage) versuslog time-to-fail (hours) coordinates, and for which this straight-line relationship is expected to continue uninterrupted throughat least 100 000 h.1.2 Unless the experimentally obtained data approximate astraight line, when calculated using log-log coordinates, it isnot poss
11、ible to assign an HDB/PDB to the material. Data thatexhibit high scatter or a “knee” (a downward shift, resulting ina subsequently steeper stress-rupture slope than indicated bythe earlier data) but which meet the requirements of this testmethod tend to give a lower forecast of LTHS/LTHSP.Inthecase
12、of data that exhibit excessive scatter or a pronounced“knee,” the lower confidence limit requirements of this testmethod are not met and the data are classified as unsuitable foranalysis.1.3 A fundamental premise of this test method is that whenthe experimental data define a straight-line relationsh
13、ip inaccordance with this test methods requirements, this straightline may be assumed to continue beyond the experimentalperiod, through at least 100 000 h (the time intercept at whichthe materials LTHS/LTHSPis determined). In the case ofpolyethylene piping materials, this test method includes asupp
14、lemental requirement for the “validating” of this assump-tion. No such validation requirements are included for othermaterials (see Note 1). Therefore, in all these other cases, it isup to the user of this test method to determine based on outsideinformation whether this test method is satisfactory
15、for theforecasting of a materials LTHS/LTHSPfor each particularcombination of internal/external environments and tempera-ture.NOTE 1Extensive long-term data that have been obtained on com-mercial pressure pipe grades of polyvinyl chloride (PVC), polybutlene(PB), and cross linked polyethlene (PEX) ma
16、terials have shown that thisassumption is appropriate for the establishing of HDBs for thesematerials for water and for ambient temperatures. Refer to Note 2 andAppendix X1 for additional information.1.4 The experimental procedure to obtain individual datapoints shall be as described in Test Method
17、D1598, whichforms a part of this test method. When any part of this test1This test method is under the jurisdiction of ASTM Committee F17 on PlasticPiping Systems and is the direct responsibility of Subcommittee F17.40 on TestMethods.Current edition approved Nov. 15, 2013. Published December 2013. O
18、riginallyapproved in 1969. Last previous edition approved in 2011 as D2837 11. DOI:10.1520/D2837-13.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1method is not in agre
19、ement with Test Method D1598, theprovisions of this test method shall prevail.1.5 General references are included at the end of this testmethod.1.6 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standa
20、rd to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.1.7 The values stated in inch-pound units are to be regardedas the standard. The values given in parentheses are forinformation only and are not considered the standard.NO
21、TE 2Over 3000 sets of data, obtained with thermoplastic pipe andpiping assemblies tested with water, natural gas, and compressed air, havebeen analyzed by the Plastic Pipe Institutes (PPI) Hydrostatic StressBoard2. None of the currently commercially offered compounds includedin PPI TR-4, “PPI Listin
22、g of Hydrostatic Design Basis (HDB), Hydro-static Design Stress (HDS), Strength Design Basis (SDB), PressureDesign Basis (PDB) and Minimum Required Strength (MRS) Ratings forThermoplastic Piping Materials or Pipe” exhibit knee-type plots at thelisted temperature, that is, deviate from a straight lin
23、e in such a mannerthat a marked drop occurs in stress at some time when plotted onequiscalar log-log coordinates. Ambient temperature stress-rupture datathat have been obtained on a number of the listed materials and that extendfor test periods over 120 000 h give no indication of “knees.” However,s
24、tress-rupture data which have been obtained on some thermoplasticcompounds that are not suitable or recommended for piping compoundshave been found to exhibit a downward trend at 23C (73F) in which thedeparture from linearity appears prior to this test methods minimumtesting period of 10 000 h. In t
25、hese cases, very low results are obtained orthe data are found unsuitable for extrapolation when they are analyzed bythis test method.Extensive evaluation of stress-rupture data by PPI and others has alsoindicated that in the case of some materials and under certain testconditions, generally at high
26、er test temperatures, a departure fromlinearity, or “down-turn”, may occur beyond this test methods minimumrequired data collection period of 10 000 h.APPI study has shown that inthe case of polyethylene piping materials that are projected to exhibit a“down-turn” prior to 100 000 h at 73F, the long-
27、term field performanceof these materials is prone to more problems than in the case of materialswhich have a projected “down-turn” that lies beyond the 100 000-hintercept. In response to these observations, a supplemental “validation”requirement for PE materials has been added to this test method in
28、 1988.This requirement is designed to reject the use of this test method for theestimating of the long-term strength of any PE material for whichsupplemental elevated temperature testing fails to validate this testmethods inherent assumption of continuing straight-line stress-rupturebehavior through
29、 at least 100 000 h at 23C (73F).When applying this test method to other materials, appropriate consid-eration should be given to the possibility that for the particular grade ofmaterial under evaluation and for the specific conditions of testing,particularly, when higher test temperatures and aggre
30、ssive environmentsare involved, there may occur a substantial “down-turn” at some pointbeyond the data collection period. The ignoring of this possibility maylead to an overstatement by this test method of a materials actualLTHS/LTHSP. To obtain sufficient assurance that this test methodsinherent as
31、sumption of continuing linearity through at least 100 000 h isappropriate, the user should consult and consider information outside thistest method, including very long-term testing or extensive field experiencewith similar materials. In cases for which there is insufficient assurance ofthe continua
32、nce of the straight-line behavior that is defined by theexperimental data, the use of other test methods for the forecasting oflong-term strength should be considered (see Appendix X1).2. Referenced Documents2.1 ASTM Standards:3D1243 Test Method for Dilute Solution Viscosity of VinylChloride Polymer
33、sD1598 Test Method for Time-to-Failure of Plastic PipeUnder Constant Internal PressureE29 Practice for Using Significant Digits in Test Data toDetermine Conformance with Specifications2.2 ISO Standard:ISO 9080 Plastic Piping and Ducting Systems, Determina-tion of Long-Term Hydrostatic Strength ofThe
34、rmoplasticsMaterials in Pipe Form by Extrapolation42.3 Plastics Pipe Institute:2PPI TR-3 Policies and Procedures for Developing Hydro-static Design Basis (HDB), Hydrostatic Design Stresses(HDS), Pressure Design Basis (PDB), Strength DesignBasis (SDB), and Minimum Required Strength (MRS)Ratings for T
35、hermoplastic Piping Materials or PipePPI TR-4 PPI Listing of Hydrostatic Design Basis (HDB),Hydrostatic Design Stress (HDS), Strength Design Basis(SDB), Pressure Design Basis (PDB) and Minimum Re-quired Strength (MRS) Ratings for Thermoplastic PipingMaterials or Pipe3. Terminology3.1 Definitions:3.1
36、.1 failurebursting, cracking, splitting, or weeping(seepage of liquid) of the pipe during test.3.1.2 hoop stressthe tensile stress in the wall of the pipe inthe circumferential orientation due to internal hydrostaticpressure.3.1.3 hydrostatic design basis (HDB)one of a series ofestablished stress va
37、lues for a compound. It is obtained bycategorizing the LTHS in accordance with Table 1.3.1.4 hydrostatic design stress (HDS)the estimated maxi-mum tensile stress the material is capable of withstandingcontinuously with a high degree of certainty that failure of thepipe will not occur. This stress is
38、 circumferential when internalhydrostatic water pressure is applied.3.1.5 long-term hydrostatic strength (LTHS)the estimatedtensile stress in the wall of the pipe in the circumferentialorientation that when applied continuously will cause failure ofthe pipe at 100 000 h. This is the intercept of the
39、 stressregression line with the 100 000-h coordinate.3.1.6 long-term hydrostatic pressure-strength (LTHSP)the estimated internal pressure that when applied continu-ously will cause failure of the pipe at 100 000 h. This is theintercept of the pressure regression line with the 100 000-hinterce2Availa
40、ble from Plastics Pipe Institute (PPI), 105 Decker Court, Suite 825,Irving, TX 75062, http:/www.plasticpipe.org.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the
41、standards Document Summary page onthe ASTM website.4Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036, http:/www.ansi.orgD2837 1323.1.7 pressurethe force per unit area exerted by themedium in the pipe.3.1.8 pressure rating (PR)the estimated max
42、imum waterpressure the pipe is capable of withstanding continuously witha high degree of certainty that failure of the pipe will not occur.3.1.8.1 The PR and HDS/HDB are related by the followingequation.PR 5 2 HDB!DF!/SDR 2 1! 5 2 HDS!/SDR 2 1! (1)3.1.8.2 The PR and PDB are related by the followinge
43、quation:PR 5 PDB!DF! (2)3.1.9 pressure design basis (PDB)one of a series ofestablished pressure values for plastic piping components(multilayer pipe, fitting, valve, etc.) obtained by categorizingthe LTHSPin accordance with Table 2.3.1.10 service (design) factor (DF)a number less than1.00 (which tak
44、es into consideration all the variables anddegree of safety involved in a thermoplastic pressure pipinginstallation) which is multiplied by the HDB to give the HDS,or multiplied by the PDB to give the pressure rating.3.1.11 The following equations shall be used for the relationbetween stress and pre
45、ssure:S 5 PD 2 t!/2t for outside diameter controlled pipe (3)orS 5 Pd1t!/2t for inside diameter controlled pipe (4)where:S = stress,P = pressure,D = average outside diameter,d = average inside diameter, andt = minimum wall thickness.4. Significance and Use4.1 The procedure for estimating long-term h
46、ydrostaticstrength or pressure-strength is essentially an extrapolationwith respect to time of a stress-time or pressure-time regressionline based on data obtained in accordance with Test MethodD1598. Stress or pressure-failure time plots are obtained forthe selected temperature and environment: the
47、 extrapolation ismade in such a manner that the long-term hydrostatic strengthor pressure strengthis estimated for these conditions.NOTE 3Test temperatures should preferably be selected from thefollowing: 40C; 50C; 60C; 80C; 100C. It is strongly recommendedthat data also be generated at 23C for comp
48、arative purposes.4.2 The hydrostatic or pressure design basis is determinedby considering the following items and evaluating them inaccordance with 5.4.4.2.1 Long-term hydrostatic strength or hydrostaticpressure-strength at 100 000 h,4.2.2 Long-term hydrostatic strength or hydrostaticpressure-streng
49、th at 50 years, and4.2.3 Stress that will give 5 % expansion at 100 000 h.4.2.4 The intent is to make allowance for the basic stress-strain characteristics of the material, as they relate to time.4.3 Results obtained at one temperature cannot, with anycertainty, be used to estimate values for other temperatures.Therefore, it is essential that hydrostatic or pressure designbases be determined for each specific kind and type of plasticcompound and each temperature. Estimates of long-termstrengths of materials can be made for a specific t