1、Designation: D7349/D7349M 11Standard Test Method forDetermining the Capability of Roofing and WaterproofingMaterials to Seal around Fasteners1This standard is issued under the fixed designation D7349/D7349M; the number immediately following the designation indicates theyear of original adoption or,
2、in the case of revision, the year of last revision. A number in parentheses indicates the year of lastreapproval. A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This qualitative test method determines the capability ofasphalt-based roofing or
3、 waterproofing material to seal arounda fastener that penetrates the material and prevent transmissionof liquid water through the material at the penetration underdefined conditions.1.2 This test method is provided for adoption by ASTM orother consensus-based roofing and waterproofing productspecifi
4、cations as a standardized means to evaluate capability toseal around a fastener. Performance of this test method aftersubjecting the product to conditioning intended to simulateenvironmental stresses and strains is not prohibited.1.3 The text of this test method references notes andfootnotes which p
5、rovide explanatory material. These notes andfootnotes (excluding those in tables and figures) shall not beconsidered as requirements of the standard.1.4 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard. The values stated ineach system may not be exact
6、 equivalents; therefore, eachsystem shall be used independently of the other. Combiningvalues from the two systems may result in non-conformancewith the standard.1.5 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the u
7、ser of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2D1079 Terminology Relating to Roofing and WaterproofingD3462 Specification for Asphalt Shingles Made from Glas
8、sFelt and Surfaced with Mineral GranulesD5147 Test Methods for Sampling and Testing ModifiedBituminous Sheet MaterialF1667 Specification for Driven Fasteners: Nails, Spikes,and Staples3. Terminology3.1 DefinitionsFor definitions of terms used in this testmethod, refer to Terminology D1079.4. Summary
9、 of Test Method4.1 The capability of asphalt-based roofing or waterproofingmaterials to seal around a penetrating fastener and prevent thepassage of liquid water at the fastener/material interface isdetermined by penetrating the material with a fastener, erectinga water column over that penetration,
10、 and monitoring theassembly for water passage for a period of time.4.2 The test method includes protocols that establish levelsfor the test method parameters. The protocol used to evaluatea material is designated in a standard specification for thematerial or by the user of this test method.5. Signi
11、ficance and Use5.1 In some situations, penetration through asphalt-basedroofing or waterproofing materials by fasteners is a requiredpart of the material installation process or occurs duringinstallation of other system components. When fasteners pen-etrate the material as a purposeful and planned p
12、art of theconstruction process, it is reasonable to expect that materialsdesigned to limit migration of liquid water at the interfacebetween the penetrating fastener and the material will do so.This qualitative test method provides a means to evaluate theability of a material to limit water migratio
13、n at fastenerpenetrations when tested under defined conditions.6. Apparatus6.1 Specimen RollerA roller having a mass of 11.8 kg 26lb 60.5 %, diameter of 125 mm 5 in. 65 %, and width of125 mm 5 in. 65%.1This test method is under the jurisdiction ofASTM Committee D08 on Roofingand Waterproofing and is
14、 the direct responsibility of Subcommittee D08.02 on SteepRoofing Products and Assemblies.Current edition approved May 1, 2011. Published May 2011. Originallyapproved in 2008. Last previous edition approved in 2010 as D7349/D7349M 10.DOI: 10.1520/D7349_D7349M-11.2For referenced ASTM standards, visit
15、 the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-295
16、9, United States.6.2 Water Column ContainerA4 L 1 gal can with thebottom cut out.6.3 SealantAny commercially-available sealant suitablefor sealing the water column container to the roofing orwaterproofing material that will not adversely affect the roofingor waterproofing material.6.4 FastenerThe it
17、em that penetrates the test specimen.Use one fastener for each test specimen. Refer to Table 1.6.5 SubstrateThe material to which the test specimen isattached prior to penetration with the fastener. One piece 255by 255 mm 10 by 10 in. 65 % is required for each testspecimen. Refer to Table 1.6.6 Inte
18、rvening MaterialA material placed between thetest specimen and the fastener. Refer to Table 1.7. Sampling7.1 From each lot of roofing or waterproofing material,select sample rolls in accordance with Test Methods D5147.7.2 The rolls so selected shall constitute the representativesample used for all t
19、ests pertaining to the lot of material beingexamined.8. Test Specimens8.1 Each test specimen shall consist of one piece of roofingor waterproofing material, 255 by 255 mm 10 by 10 in. 65% in size, selected at random from a sample roll.8.2 At least one test specimen shall be selected from eachsample
20、roll.8.3 Condition test specimens at 23 6 2C 73.4 6 3.6Fand 50 6 10 % relative humidity for at least four hours prior totest assembly preparation.9. Test Assembly Preparation9.1 Select a protocol from Table 1 for the material to beevaluated (see Appendix X1) or use the protocol designated bythe stan
21、dard specification for the material. Specify the numberof specimens to be selected from each sample roll.9.2 Prepare one test assembly for each test specimen,assembling the materials in accordance with these instructionsand as illustrated in Fig. 1. Use the substrate, interveningmaterial, fastener,
22、and fastener driving method specified by theselected protocol (see Table 1).9.3 Apply the test specimen to the substrate specified in theselected protocol (see Table 1, Substrate) as follows:9.3.1 Self-adhesive materialsPeel the release paper orfilm off the roofing or waterproofing specimen and ligh
23、tly placethe specimen on the substrate, centering the specimen on thesubstrate with the edges of the specimen and substrate aligned.Press down the edges of the specimen just hard enough to keepthe edges from lifting. Roll the specimen to promote adhesionto the substrate using the specimen roller, co
24、mpleting a total ofthree back-and-forth cycles. Each cycle shall be completed in4to6s.9.3.2 Non-self-adhesive materialsPlace the specimen onthe substrate, centering the specimen on the substrate with theedges of the specimen and substrate aligned.9.4 Place two pieces of lumber, oriented parallel to
25、eachother and spaced 50 6 10 mm 2 6 0.5 in. apart, underneaththe substrate for support.9.5 Place the intervening material specified in the selectedprotocol (see Table 1, Intervening Material) on top of the testspecimen, centering it in both directions.9.6 Drive one fastener specified in the selected
26、 protocol(see Table 1, Fastener) through the intervening material (ifpresent), test specimen, and substrate near the center of thespecimen in the area between the two pieces of supportinglumber in the manner specified in the selected protocol (seeTable 1, Fastener Driving Method).9.7 Place the water
27、 column container on the specimen,centered over the fastener. Applya6to10-mm 0.25 to0.375-in. bead of sealant completely around the outside rim ofthe water column container to bond it to the specimen. Allowa minimum of 2 h for the sealant to set, then apply another beadaround the inside rim of the w
28、ater column container.9.8 Maintain the test assembly at 23 6 2C 73.4 6 3.6Fand 50 6 10 % relative humidity for 24 hours to allow thesealant to cure.9.9 After the sealant has cured, condition the test assemblyas specified in the selected protocol (see Table 1, Test Assem-bly Conditioning).10. Procedu
29、re10.1 Conduct the test using the water depth, test tempera-ture, and test period specified in the selected protocol (seeTable 1).10.2 Place the test assembly atopa4L1-gal can fromwhich the lid has been removed.10.3 Fill the water column container to the depth specifiedin the selected protocol (see
30、Table 1, Water Depth) withdeionized or distilled water.10.4 Place the test assembly and 4 L 1-gal bottom can ina temperature controlled chamber maintained at the tempera-ture specified by the selected protocol (see Table 1, TestTemperature).10.5 Maintain the test assembly at the test temperature for
31、the test period specified by the selected protocol (see Table 1,Test Period).10.6 At the conclusion of the test period, remove the testassembly from the 4 L 1-gal bottom can, carefully pour thewater from the water column container without splashing ontothe substrate, and blot the inside of the water
32、 column containerdry. Examine the assembly and note any water in the 4 L1-gal bottom can, on the shank of the fastener, or on theunderside of the substrate.10.7 Carefully remove the water column container from theroofing or waterproofing material. Peel the roofing or water-proofing material back to
33、the fastener and inspect the undersideof the material and top side of the substrate for any signs ofwater.11. Interpretation of Results11.1 A specimen is considered to pass the test if no water ispresent in the 4 L 1-gal bottom can, on the underside of thesubstrate, on the shank of the fastener, or
34、between the materialand the substrate.12. Report12.1 Report the following information:D7349/D7349M 112TABLE 1 ProtocolsPROTOCOL 1Substrate APA Rated Sheathing,3216 , Exposure 1 plywood,12 mm 1532 in. thickIntervening Material NoneFastener ASTM F1667 NLRFSS-53Z smooth shank steel roofing nail32 mm 1.
35、25 in. long with a shank diameter of 3.05 mm0.120 in., a head diameter of 9.52 mm 0.375 in.,and a zinc coatingFastener Driving Method With a hammer, perpendicular to the specimen, until the fastenerhead is flush with the surface of the specimenTest Assembly Conditioning 4 6 0.25 h at 40 6 2C 104 6 3
36、.6F, followed by20 6 0.25 h at 23 6 2C 73.4 6 3.6FWater Depth 125 6 6mm56 0.25 in.Test Temperature 4 6 2C 39.2 6 3.6FTest Period 72 6 0.25 hPROTOCOL 2Substrate APA Rated Sheathing,3216 , Exposure 1 plywood,12 mm 1532 in. thickIntervening Material NoneFastener ASTM F1667 NLRFSS-53Z smooth shank steel
37、 roofing nail32 mm 1.25 in. long with a shank diameter of 3.05 mm0.120 in., a head diameter of 9.52 mm 0.375 in.,and a zinc coatingFastener Driving Method With a hammer, perpendicular to the specimen, until the fastenerhead is flush with the surface of the specimenTest Assembly Conditioning 4 6 0.25
38、 h at 40 6 2C 104 6 3.6F, followed by20 6 0.25 h at 23 6 2C 73.4 6 3.6FWater Depth 25 6 1mm1.06 0.05 in.Test Temperature 4 6 2C 39.2 6 3.6FTest Period 8 6 0.25 hPROTOCOL 3Substrate APA Rated Sheathing,3216 , Exposure 1 oriented strand board,12 mm 1532 in. thickIntervening Material 75 by 75 mm 3 by 3
39、 in. single-thickness piece ofD3462-labeled asphalt shingleFastener ASTM F1667 NLRFSR-53Z ring shank steel roofing nail32 mm 1.25 in. long with a shank diameter of 3.05 mm0.120 in., a head diameter of 9.52 mm 0.375 in.,and a zinc coatingFastener Driving Method With a hammer, perpendicular to the spe
40、cimen, until the fastenerhead is flush with the surface of the intervening materialTest Assembly Conditioning 24 6 0.25 h at 23 6 2C 73.4 6 3.6FWater Depth 125 6 6mm56 0.25 in.Test Temperature 4 6 2C 39.2 6 3.6FTest Period 72 6 0.25 hPROTOCOL 4Substrate APA Rated Sheathing,3216 , Exposure 1 plywood,
41、12 mm 1532 in. thickIntervening Material 75 by 75 mm 3 by 3 in. single-thickness piece ofD3462-labeled asphalt shingleFastener ASTM F1667 NLRFSS-53Z smooth shank steel roofing nail32 mm 1.25 in. long with a shank diameter of 3.05 mm0.120 in., a head diameter of 9.52 mm 0.375 in.,and a zinc coating;
42、hot dipped galvanizedFastener Driving Method With a hammer, perpendicular to the specimen, until the fastenerhead is flush with the surface of the intervening materialTest Assembly Conditioning 24 6 0.25 h at 23 6 2C 73.4 6 3.6FWater Depth 125 6 6mm56 0.25 in.Test Temperature 4 6 2C 39.2 6 3.6FTest
43、Period 72 6 0.25 hD7349/D7349M 113TABLE 1 ContinuedPROTOCOL 5Substrate APA Rated Sheathing,3216 , Exposure 1 oriented strand board,12 mm 1532 in. thickIntervening Material 75 by 75 mm 3 by 3 in. single-thickness piece ofD3462-labeled asphalt shingleFastener ASTM F1667 NLRFSS-53Z smooth shank steel r
44、oofing nail32 mm 1.25 in. long with a shank diameter of 3.05 mm0.120 in., a head diameter of 9.52 mm 0.375 in.,and a zinc coating; electrogalvanized; coil gun nailFastener Driving Method With a coil-fed pneumatic tool (nail gun), perpendicularto the specimen, pneumatic tool pressure set to ensurethe
45、 fastener head is flush with the surface ofthe intervening materialTest Assembly Conditioning 24 6 0.25 h at 23 6 2C 73.4 6 3.6FWater Depth 125 6 6mm56 0.25 in.Test Temperature 4 6 2C 39.2 6 3.6FTest Period 72 6 0.25 hNoteThere is a possibility of increased variability in test results when pneumatic
46、ally-driven coil nails are used instead of hand-driven nails.FIG. 1 Test ArrangementD7349/D7349M 11412.1.1 Identifying information about the roofing or water-proofing material being tested, including the manufacturer andproduct name.12.1.2 The number of sample rolls.12.1.3 The number of specimens te
47、sted per sample roll.12.1.4 The protocol used in the evaluation of the material.12.1.5 For each specimen, the presence of water in the 4 L1-gal bottom can, on the underside of the substrate, on theshank of the fastener, or between the material and the substrate,separately noting each area in which w
48、ater is found.12.1.6 The number of specimens that pass the test.13. Precision and Bias13.1 No information is presented about either the precisionor bias of this test method for measuring the capability ofroofing or waterproofing materials to seal around fastenersbecause the test result is not quanti
49、tative.14. Keywords14.1 fastener seal; roofing; waterproofingAPPENDIXES(Nonmandatory Information)X1. EXPLANATORY INFORMATIONX1.1 This test method was developed to have broadapplicability for evaluating roofing and waterproofing productsemployed in a variety of end uses. Therefore, it does notcontain a single set of test parameters that apply to all producttypes. Instead, the method is designed to be referenced b