1、BRITISH STANDARDBS EN 10277-2:2008Bright steel products Technical delivery conditions Part 2: Steels for general engineering purposesICS 77.140.20; 77.140.60g49g50g3g38g50g51g60g44g49g42g3g58g44g55g43g50g56g55g3g37g54g44g3g51g40g53g48g44g54g54g44g50g49g3g40g59g38g40g51g55g3g36g54g3g51g40g53g48g44g55
2、g55g40g39g3g37g60g3g38g50g51g60g53g44g42g43g55g3g47g36g58BS EN 10277-2:2008This British Standard was published under the authority of the Standards Policy and Strategy Committee on 30 April 2008 BSI 2008ISBN 978 0 580 52923 8National forewordThis British Standard is the UK implementation of EN 10277
3、-2:2008. It supersedes BS EN 10277-2:1999 which is withdrawn.The UK participation in its preparation was entrusted to Technical Committee ISE/31, Wrought steels.A list of organizations represented on this committee can be obtained on request to its secretary.This publication does not purport to incl
4、ude all the necessary provisions of a contract. Users are responsible for its correct application.Compliance with a British Standard cannot confer immunity from legal obligations.Amendments/corrigenda issued since publicationDate CommentsEUROPEAN STANDARDNORME EUROPENNEEUROPISCHE NORMEN 10277-2March
5、 2008ICS 77.140.20; 77.140.60 Supersedes EN 10277-2:1999 English VersionBright steel products - Technical delivery conditions - Part 2:Steels for general engineering purposesProduits en acier transforms froid - Conditionstechniques de livraison - Partie 2: Aciers dusage gnralBlankstahlerzeugnisse -
6、Technische Lieferbedingungen -Teil 2: Sthle fr allgemeine technische VerwendungThis European Standard was approved by CEN on 4 February 2008.CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this EuropeanStandard the status of a natio
7、nal standard without any alteration. Up-to-date lists and bibliographical references concerning such nationalstandards may be obtained on application to the CEN Management Centre or to any CEN member.This European Standard exists in three official versions (English, French, German). A version in any
8、 other language made by translationunder the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as theofficial versions.CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estoni
9、a, Finland,France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal,Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.EUROPEAN COMMITTEE FOR STANDARDIZATIONCOMIT EUROPEN DE NORMALISATIONEUROPISCHES
10、 KOMITEE FR NORMUNGManagement Centre: rue de Stassart, 36 B-1050 Brussels 2008 CEN All rights of exploitation in any form and by any means reservedworldwide for CEN national Members.Ref. No. EN 10277-2:2008: EEN 10277-2:2008 (E) 2 Content Page Foreword3 1 Scope 4 2 Normative references 4 3 Terms and
11、 definitions .4 4 Classification and designation.4 4.1 Classification4 4.2 Designation 4 5 Information to be supplied by the purchaser .4 6 Manufacturing process .4 7 Requirements.5 7.1 Chemical composition 5 7.2 Mechanical properties.5 7.3 Options .5 8 Inspection and testing.5 9 Marking .5 BS EN 10
12、277-2:2008EN 10277-2:2008 (E) 3 Foreword This document (EN 10277-2:2008) has been prepared by Technical Committee ECISS/TC 23 “Steels for heat treatment, alloy steels and free-cutting steels - Qualities and dimensions”, the secretariat of which is held by DIN. This European Standard shall be given t
13、he status of a national standard, either by publication of an identical text or by endorsement, at the latest by September 2008, and conflicting national standards shall be withdrawn at the latest by September 2008. Attention is drawn to the possibility that some of the elements of this document may
14、 be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 10277-2:1999. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to
15、implement this European Standard: Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzer
16、land and the United Kingdom. This European Standard EN 10277 Bright steel products - Technical delivery conditions is subdivided as follows: Part 1: General; Part 2: Steels for general engineering purposes; Part 3: Free-cutting steels; Part 4: Case hardening steels; Part 5: Steels for quenching and
17、tempering. During the preparation of the first edition of this European Standard there were not enough statistical data available concerning mechanical properties of bright bar products. Since then it has been recognized that the proof strength values in the cold drawn condition were too high. In ad
18、dition, cyclic stresses that occur during straightening can reduce the proof strength (Bauschingers effect), which was not taken into account when drafting the first edition of this standard. In this second edition the proof strength values of non-alloy and alloy grades in condition +QT+C in parts 3
19、 and 5 have been adjusted downwards compared to the first edition. Furthermore for this part the values for the tensile strength of grades S235JRC and S355J2C were adapted to EN 10025-2 in the table for mechanical properties. BS EN 10277-2:2008EN 10277-2:2008 (E) 4 1 Scope This part of EN 10277 appl
20、ies to bright steel bars for general engineering purposes in the drawn, turned or ground condition and in straight lengths. This EN 10277-2 is complemented by EN 10277-1. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated refer
21、ences, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 10025-2, Hot rolled products of structural steels Part 2: Technical delivery conditions for non-alloy structural steels EN 10083-2, Steels for quenching
22、 and tempering - Part 2: Technical delivery conditions for non alloy steels EN 10277-1, Bright steel products - Technical delivery conditions - Part 1: General 3 Terms and definitions For the purposes of this European Standard, the terms and definitions given in EN 10277-1 apply. 4 Classification an
23、d designation 4.1 Classification All steels specified in this European Standard are classified as non-alloy quality steels. 4.2 Designation See EN 10277-1. NOTE This Standard does not comprise impact requirements. 5 Information to be supplied by the purchaser See EN 10277-1. 6 Manufacturing process
24、See EN 10277-1. BS EN 10277-2:2008EN 10277-2:2008 (E) 5 7 Requirements 7.1 Chemical composition 7.1.1 Cast analysis The chemical composition of the steel according to the cast analysis shall be as specified in Table 1. 7.1.2 Product analysis The permissible deviations from the chemical composition a
25、s specified in Table 1 for cast analysis and the product analysis of the steel shall be as specified in Table 2. 7.2 Mechanical properties The mechanical properties of the steels shall be as specified in Table 3. The values found in EN 10025-2 and EN 10083-2 can be applied for a heat treatment after
26、 cold drawing, e.g. +C+N. 7.3 Options See Annex B of EN 10277-1. 8 Inspection and testing See EN 10277-1. 9 Marking See EN 10277-1. BS EN 10277-2:2008EN 10277-2:2008 (E) 6 Table 1 Steel grades and chemical composition (cast analysis)Designation Chemical composition, % by mass Steel name Steel number
27、 Steel grade according to C Si max. Mn P max. S max. Na max. Crmax. Mo max. Ni max. Cr+Mo+Nimax. Others S235JRC 1.0122 EN 10025-2 0,17b -c 1,40 0,040 0,040d0,012 - - - - Cu: e 0,55 E295GCf 1.0533fEN 10025-2 - -c - 0,045 0,045d0,012 - - - - - E335GC 1.0543 EN 10025-2 - -c- 0,045 0,045d0,012 - - - - -
28、 S355J2Cf1.0579fEN 10025-2 0,20g 0,55h 1,60 0,030 0,030d- - - - - Cu: e 0,55 C10 1.0301 - 0,07 to 0,13 0,40 0,30 to 0,60 0,045 0,045i- - - - - - jC15 1.0401 - 0,12 to 0,18 0,40 0,30 to 0,80 0,045 0,045I- - - - - - jC16 1.0407 - 0,12 to 0,18 0,40 0,60 to 0,90 0,045 0,045I- - - - - - jC35 1.0501 EN 10
29、083-2 0,32 to 0,39 0,40 0,50 to 0,80 0,045 0,045I- 0,40 0,10 0,40 0,63 - jC40 1.0511 EN 10083-2 0,37 to 0,44 0,40 0,50 to 0,80 0,045 0,045I- 0,40 0,10 0,40 0,63 - jC45 1.0503 EN 10083-2 0,42 to 0,50 0,40 0,50 to 0,80 0,045 0,045I- 0,40 0,10 0,40 0,63 - jC55 1.0535 EN 10083-2 0,52 to 0,60 0,40 0,60 t
30、o 0,90 0,045 0,045I- 0,40 0,10 0,40 0,63 - jC60 1.0601 EN 10083-2 0,57 to 0,65 0,40 0,60 to 0,90 0,045 0,045i- 0,40 0,10 0,40 0,63 - jNOTE Chemical composition is determined by cast analysis. aThe maximum value of nitrogen does not apply if the chemical composition shows a minimum total Al content o
31、f 0,020 % or alternatively min. 0,015 % acid soluble Al or if sufficient other N binding elements are present. In this case the N-binding elements shall be mentioned in the inspection document. bMaximum 0,20 % for C for nominal thickness 40 mm. cRimming steel not permitted. dFor long products the ma
32、ximum S-content can be increased for improved machinability for steel grades E295GC and E335GC by 0,010 % and for S235JRC and S355J2C by 0,015 % by agreement if the steel is treated to modify the sulphide morphology and the chemical composition shows min. 0,0020 % Ca. eCu content above 0,40 % may ca
33、use hot shortness during hot forming. fFor applications where weldability is necessary, steel S355J2C (1.0579) should be used instead of E295GC (1.0533). gMaximum 0,22 % C for nominal thickness 30 mm. hFully killed steel containing nitrogen binding elements in amounts sufficient to bind the availabl
34、e nitrogen (for example min. 0,020 % Al). The usual guideline is a minimum aluminium to nitrogen ratio of 2:1, when no other nitrogen binding elements are present. Such other elements shall be reported in the inspection document. iSteels with improved machinability as a result of the addition of hig
35、her sulphur contents up to around 0,10 % S (including resulphurized steels with controlled inclusion content (e.g. Ca-treatment) (modern method) or lead may be supplied on request. In the first case the upper limit for the manganese content may be increased by 0,15 %. j Elements not quoted in this t
36、able shall not be added intentionally to the steel without the agreement of the purchaser, other than forthe purpose of finishing the heat. All reasonable precautions shall be taken to prevent the addition of such elements from scrap orother material used in the manufacture which affect the hardenab
37、ility, mechanical properties and applicability. BS EN 10277-2:2008EN 10277-2:2008 (E) 7 Table 2 Permissible deviations between the product analysis and the limiting values given in Table 1 for the cast analysis Element Specified maximum content in the cast analysis % by mass Steel grades Permissible
38、 deviationsa % by mass 0,17 0,17 0,20 S235JRC + 0,02 + 0,03 0,20 0,20 0,22 S355J2C + 0,03 + 0,02 C 0,55 0,55 0,65 C10, C15, C16, C35, C40 C45, C55, C60 0,02 0,03 0,55 S355J2C + 0,05 Si 0,40 C10 to C60 + 0,03 1,60 S235JRC, S355J2C + 0,10 Mn 0,90 C10 to C60 0,04 0,045 S235JRC to S355J2C + 0,010 P and
39、S 0,045 C10 to C60 + 0,005 N 0,012 S335JRC to E335GC + 0,002 Cr 0,40 + 0,05 Mo 0,10 + 0,03 Ni 0,40 C35 to C60 + 0,05 Cu 0,55 S235JRC, S355J2C + 0,05 a means that in one cast, the deviation may occur over the upper value or under the lower value of the specified range in Table 1, but not both at the
40、same time. BS EN 10277-2:2008EN 10277-2:2008 (E) 8 Table 3 Mechanical propertiesDesignation Mechanical propertiesaAs rolled + turned (+SH)bCold drawn (+C) Steel name Steel number Thicknessamm Hardnessc HBW RmMPa Rp0,2dMPa min. RmdMPa Amin. 5 10 - - 355 470 to 840 8 10 16 - - 300 420 to 770 9 16 40 1
41、02 to 140 360 to 510 260 390 to 730 10 40 63 102 to 140 360 to 510 235 380 to 670 11 S235JRC 1.0122 63 100 102 to 140 360 to 510 215 360 to 640 11 5 10 - - 510 650 to 950 6 10 16 - - 420 600 to 900 7 16 40 140 to 181 470 to 610 320 550 to 850 8 40 63 140 to 181 470 to 610 300 520 to 770 9 E295GC 1.0
42、533 63 100 140 to 181 470 to 610 255 470 to 740 9 5 10 - - 540 700 to 1 050 5 10 16 - - 480 680 to 970 6 16 40 169 to 211 570 to 710 390 640 to 930 7 40 63 169 to 211 570 to 710 340 620 to 870 8 E335GC 1.0543 63 100 169 to 211 570 to 710 295 570 to 810 8 5 10 - - 520 630 to 950 6 10 16 - - 450 580 t
43、o 880 7 16 40 146 to 187 470 to 630 350 530 to 850 8 40 63 146 to 187 470 to 630 335 500 to 770 9 S355J2C 1.0579 63 100 146 to 187 470 to 630 315 470 to 740 9 5 10 - - 350 460 to 760 8 10 16 - - 300 430 to 730 9 16 40 92 to 163 310 to 550 250 400 to 700 10 40 63 92 to 163 310 to 550 200 350 to 640 1
44、2 C10 1.0301 63 100 92 to 163 310 to 550 180 320 to 580 12 5 10 - - 380 500 to 800 7 10 16 - - 340 480 to 780 8 16 40 98 to 178 330 to 600 280 430 to 730 9 40 63 98 to 178 330 to 600 240 380 to 670 11 C15 1.0401 63 100 98 to 178 330 to 600 215 340 to 600 12 5 10 - - 400 520 to 820 7 10 16 - - 360 50
45、0 to 800 8 16 40 105 to 184 350 to 620 300 450 to 750 9 40 63 105 to 184 350 to 620 260 400 to 690 11 C16 1.0407 63 100 105 to 184 350 to 620 235 360 to 620 12 BS EN 10277-2:2008EN 10277-2:2008 (E) 9 Table 3 Mechanical properties (continued)Designation Mechanical propertiesaAs rolled + turned (+SH)b
46、 Cold drawn (+C) Steel name Steel number Thicknessa mm HardnesscHBW Rm MPa Rp0,2d MPa min. RmdMPa A min. 5 10 - - 510 650 to 1 000 6 10 16 - - 420 600 to 950 7 16 40 154 to 207 520 to 700 320 580 to 880 8 40 63 154 to 207 520 to 700 300 550 to 840 9 C35 1.0501 63 100 154 to 207 520 to 700 270 520 to
47、 800 9 5 10 - - 540 700 to 1 000 6 10 16 - - 460 650 to 980 7 16 40 163 to 211 550 to 710 365 620 to 920 8 40 63 163 to 211 550 to 710 330 590 to 840 9 C40 1.0511 63 100 163 to 211 550 to 710 290 550 to 820 9 5 10 - - 565 750 to 1 050 5 10 16 - - 500 710 to 1 030 6 16 40 172 to 242 580 to 820 410 65
48、0 to 1 000 7 40 63 172 to 242 580 to 820 360 630 to 900 8 C45 1.0503 63 100 172 to 242 580 to 820 310 580 to 850 8 5 10 - - 590 770 to 1 100 5 10 16 - - 520 730 to 1 080 6 16 40 181 to 269 610 to 910 440 690 to 1 050 7 40 63 181 to 269 610 to 910 390 650 to 1 030 8 C55 1.0535 63 100 181 to 269 610 t
49、o 910 - - - 5 10 - - 630 800 to 1 150 5 10 16 - - 550 780 to 1 130 5 16 40 198 to 278 670 to 940 480 730 to 1 100 6 40 63 198 to 278 670 to 940 - - - C60 1.0601 63 100 198 to 278 670 to 940 - - - NOTE: This Standard does not include impact requirements. aFor thickness 5 mm, the mechanical properties may be agreed at the time of enquiry and order. bFor the rolled a