1、raising standards worldwideNO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBSI Standards PublicationFlexible insulating sleevingPart 3: Specifications for individual types of sleeving Sheet 282: Heat-shrinkable, polyolefin sleeving Stress controlBS EN 60684-3-282:2010Licensed C
2、opy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:51, Uncontrolled Copy, (c) BSINational forewordThis British Standard is the UK implementation of EN 60684-3-282:2010. It isidentical to IEC 60684-3-282:2010.The UK participation in its preparation was entrusted by Technical CommitteeGEL/15,
3、Solid electrical insulating materials, to Subcommittee GEL/15/5,Flexible insulating sleeving for electrical purposes.A list of organizations represented on this committee can be obtained onrequest to its secretary.This publication does not purport to include all the necessary provisions of acontract
4、. Users are responsible for its correct application. BSI 2011ISBN 978 0 580 65791 7ICS 29.035.20Compliance with a British Standard cannot confer immunity fromlegal obligations.This British Standard was published under the authority of the StandardsPolicy and Strategy Committee on 28 February 2011.Am
5、endments issued since publicationAmd. No. Date Text affectedBRITISH STANDARDBS EN 60684-3-282:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:51, Uncontrolled Copy, (c) BSIEUROPEAN STANDARD EN 60684-3-282 NORME EUROPENNE EUROPISCHE NORM September 2010 CENELEC European Commit
6、tee for Electrotechnical Standardization Comit Europen de Normalisation Electrotechnique Europisches Komitee fr Elektrotechnische Normung Management Centre: Avenue Marnix 17, B - 1000 Brussels 2010 CENELEC - All rights of exploitation in any form and by any means reserved worldwide for CENELEC membe
7、rs. Ref. No. EN 60684-3-282:2010 E ICS 29.035.20 English version Flexible insulating sleeving - Part 3: Specifications for individual types of sleeving - Sheet 282: Heat-shrinkable, polyolefin sleeving - Stress control (IEC 60684-3-282:2010) Gaines isolantes souples - Partie 3: Spcifications pour ty
8、pes particuliers de gaines - Feuille 282: Gaines thermortractables en polyolfine - Contrle de fatigue (CEI 60684-3-282:2010) Isolierschluche - Teil 3: Anforderungen fr einzelne Schlauchtypen - Blatt 282: Polyolefin-Wrmeschrumpfschluche mit Feldsteuerung (IEC 60684-3-282:2010) This European Standard
9、was approved by CENELEC on 2010-09-01. CENELEC members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning s
10、uch national standards may be obtained on application to the Central Secretariat or to any CENELEC member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CENELEC member into its own
11、 language and notified to the Central Secretariat has the same status as the official versions. CENELEC members are the national electrotechnical committees of Austria, Belgium, Bulgaria, Croatia, Cyprus, the Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Irela
12、nd, Italy, Latvia, Lithuania, Luxembourg, Malta, the Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. BS EN 60684-3-282:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:51, Uncontrolled Copy, (c) BSIEN 6068
13、4-3-282:2010 Foreword The text of document 15/564/FDIS, future edition 1 of IEC 60684-3-282, prepared by IEC TC 15, Solid electrical insulating materials, was submitted to the IEC-CENELEC parallel vote and was approved by CENELEC as EN 60684-3-282 on 2010-09-01. Attention is drawn to the possibility
14、 that some of the elements of this document may be the subject of patent rights. CEN and CENELEC shall not be held responsible for identifying any or all such patent rights. The following dates were fixed: latest date by which the EN has to be implemented at national level by publication of an ident
15、ical national standard or by endorsement (dop) 2011-06-01 latest date by which the national standards conflicting with the EN have to be withdrawn (dow) 2013-09-01 Annex ZA has been added by CENELEC. _ Endorsement notice The text of the International Standard IEC 60684-3-282:2010 was approved by CEN
16、ELEC as a European Standard without any modification. _ BS EN 60684-3-282:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:51, Uncontrolled Copy, (c) BSIEN 60684-3-282:2010 Annex ZA (normative) Normative references to international publications with their corresponding Europe
17、an publications The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. NOTE When an international public
18、ation has been modified by common modifications, indicated by (mod), the relevant EN/HD applies. Publication Year Title EN/HD Year - - Test requirements on accessories for use on power cables of rated voltage from 3,6/6(7,2) kV up to 20,8/36(42) kV - Part 1: Cables with extruded insulation HD 629.1
19、S2 2006 IEC 60296 2003 Fluids for electrotechnical applications - Unused mineral insulating oils for transformers and switchgear EN 60296 + corr. September 2004 2004 IEC 60502 Series Power cables with extruded insulation and their accessories for rated voltages from 1 kV (Um = 1,2 kV) up to 30 kV (U
20、m = 36 kV) - - IEC 60684-1 2003 Flexible insulating sleeving - Part 1: Definitions and general requirements EN 60684-1 2003 IEC 60684-2 + A1 + A2 1997 2003 2005 Flexible insulating sleeving - Part 2: Methods of test EN 60684-2 + A1 + A2 1997 2003 2005 IEC 60757 1983 Code for designation of colours H
21、D 457 S1 1985 BS EN 60684-3-282:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:51, Uncontrolled Copy, (c) BSI60684-3-282 IEC:2010 CONTENTS INTRODUCTION.5 1 Scope.6 2 Normative references .6 3 Designation 7 4 Conditions of test .7 5 Requirements .7 6 Sleeving conformance 7 A
22、nnex A (informative) Guidance on the available sizes and wall thicknesses .9 Table 1 Property requirements .7 Table 2 Resistance to selected fluids .8 Table A.1 Type A, medium wall9 Table A.2 Type B, thick wall.9 BS EN 60684-3-282:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011
23、 08:51, Uncontrolled Copy, (c) BSI60684-3-282 IEC:2010 5 INTRODUCTION This International Standard is one of a series which deals with flexible insulating sleeving for electrical purposes. The series consists of three parts: Part 1: Definitions and general requirements (IEC 60684-1) Part 2: Methods o
24、f test (IEC 60684-2) Part 3: Specifications for individual types of sleeving (IEC 60684-3) This standard comprises one of the sheets of Part 3 as follows: Sheet 282: Heat-shrinkable, polyolefin sleeving Stress control BS EN 60684-3-282:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04
25、/2011 08:51, Uncontrolled Copy, (c) BSI 6 60684-3-282 IEC:2010 FLEXIBLE INSULATING SLEEVING Part 3: Specifications for individual types of sleeving Sheet 282: Heat-shrinkable, polyolefin sleeving Stress control 1 Scope This part of IEC 60684 gives the requirements for two types of heat-shrinkable, p
26、olyolefin sleeving, stress control, not flame retarded, with a nominal shrink ratio up to 3:1. This sleeving has been found suitable for use up to temperatures of 100 C. Type A : Medium wall Internal diameter up to 65,0 mm typically Type B : Thick wall Internal diameter up to 95,0 mm typically These
27、 sleevings are normally supplied in colour black. Since these types of sleevings cover a significantly large range of sizes and wall thicknesses, Tables A.1 and A.2 in this standard provides guidance to the range of sizes available. The actual size shall be agreed between the user and the supplier.
28、Materials which conform to this specification meet established levels of performance. However, the selection of a material by a user for a specific application should be based on the actual requirements necessary for adequate performance in that application and not based on this specification alone.
29、 This sleeving is designed to be used in MV cable accessories and as such electrical performance must be proven as part of the assembly. Examples of this are described in HD 629 and the IEC 60502 series. 2 Normative references The following referenced documents are indispensable for the application
30、of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. IEC 60296:2003, Fluids for electrotechnical applications Unused mineral insulating oils for transformers and switchgear IE
31、C 60502 (all parts), Power cables with extruded insulation and their accessories for rated voltages from 1 kV (Um = 1,2 kV) up to 30 kV (Um = 36 kV) IEC 60684-1:2003, Flexible insulating sleeving Part 1: Definitions and general requirements IEC 60684-2:1997, Flexible insulating sleeving Part 2: Meth
32、ods of test Amendment 1 (2003) Amendment 2 (2005) IEC 60757:1983, Code for designation of colours BS EN 60684-3-282:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:51, Uncontrolled Copy, (c) BSI60684-3-282 IEC:2010 7 HD 629, Test requirements on accessories for use on power
33、cables of rated voltages from 3,6/6(7,2)KV up to 20,8/36 (42)KV Part 1: Cables with extruded insulation 3 Designation The sleeving shall be identified by the following designation: Description IEC publication number IEC part number IEC sheet number Type Size (expanded and recovered internal diameter
34、 in millimetres) Colour Sleeving IEC 60684 - 3 -282 - A - 45,0/20,0 - BK Colour abbreviation shall comply with IEC 60757. NOTE This information is for labelling only in accordance with IEC 60684-1. 4 Conditions of test Unless otherwise specified, the sleeving shall be shrunk in a forced air circulat
35、ion oven for (10 1) min at 200 C 3 K prior to testing. 5 Requirements In addition to the general requirements given in IEC 60684-1, the sleeving shall comply with the requirements of Tables 1 and 2. 6 Sleeving conformance Conformance to the requirements of this specification shall normally be based
36、on the results from typical sizes. Type A : Recovered ID 25 mm - 30 mm Type B : Recovered ID 25 mm - 30 mm Table 1 Property requirements Property IEC 60684-2 clause or subclause Units Max. or min. Requirements Remarks Dimensions Internal diameter Wall thickness Concentricity expanded recovered 3 3.1
37、.2 3.3.2 3.3.3 mm mm % Min. Min. To be agreed between the purchaser and the supplier 60 85 Heat shock Tensile strength Elongation at break 6 19.1 and 19.2 19.1 and 19.2 MPa % Min. Min. 8 175 Heat at 150 C 5 K. Longitudinal change 9 % Max. +5 -10 Bending at low temperature 14 No cracking shall be vis
38、ible. Test at 40 C. For strips, the mandrel shall be between 20 BS EN 60684-3-282:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:51, Uncontrolled Copy, (c) BSI 8 60684-3-282 IEC:2010 Property IEC 60684-2 clause or subclause Units Max. or min. Requirements Remarks and 22 tim
39、es the wall thickness. Full section sleeving is tested unfilled and the mandrel shall be between 20 and 22 times the outer diameter. Dimensional stability on storage 16 The dimensions shall remain as agreed. See Clause 1 Scope. Tensile strength Elongation at break 19.1 and 19.2 19.1 and 19.2 MPa % M
40、in. Min. 10 200 Use a jaw separation rate of 100 mm/min Below 6,5 mm as sleeving. At 6,5 mm and above as dumbbells. Secant modulus at 2 % elongation 19.4 MPa Max. 100 Resistance to selected fluids Tensile strength Elongation at break 36 19.1 and 19.2 19.1 and 19.2 MPa % Min. Min. 4 150 Use the fluid
41、s and test temperatures specified in Table 2. Heat ageing Tensile strength Elongation at break 39 19.1 and 19.2 19.1 and 19.2 MPa % Min. Min. 5 200 Heat at 135 C 3 K. Relative permittivity 24 Min. 5 or as agreed between user and supplier Volume resistivity at room temperature 23 23.4.2 m Min. 108or
42、as agreed between user and supplier See note. Long term ageing Elongation at break 50 19.2 % Min. 100 The ageing temperature shall be 100 C 3 K. NOTE These values are set so as to define the tube as stress controlling and do not indicate any guarantee of suitable performance in an accessory. Further
43、 testing by the supplier will be needed to prove this. Note also that the values may change with applied voltage. Table 2 Resistance to selected fluids Test fluid No. Fluids Type Standard or symbol Immersion temperature C 2 K 1 Insulating oil Mineral based IEC 60296 23 2 Isopropyl alcohol 23 3 - Wat
44、er De-ionized 85 Other fluids and/or temperatures may be specified for customers with specific needs. These additional fluids and/or temperatures shall be applicable when incorporated into agreements between the supplier and the customer. BS EN 60684-3-282:2010Licensed Copy: Wang Bin, ISO/EXCHANGE C
45、HINA STANDARDS, 21/04/2011 08:51, Uncontrolled Copy, (c) BSI60684-3-282 IEC:2010 9 Annex A (informative) Guidance on the available sizes and wall thicknesses Table A.1 Type A, medium wall Internal diameter Wall Expanded Min. mm Recovered Max. mm Recovered wall thickness mm 16,0 8,0 1,8 20,0 10,0 1,8
46、 26,0 12,0 2.5 30,0 15,0 2,9 45,0 20,0 3,0 50,0 25,0 3,3 65,0 30,0 3,3 Table A.2 Type B, thick wall Internal diameter Wall Expanded Min. mm Recovered Max. mm Recovered wall thickness mm 30,0 10,0 2,5 36,0 12,0 3,0 45,0 15,0 3,0 55,0 22,0 3,0 66,0 22,0 3,0 75,0 28,0 3,0 85,0 28,0 3,0 95,0 45,0 3,6 _
47、BS EN 60684-3-282:2010Licensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:51, Uncontrolled Copy, (c) BSIThis page deliberately left blankLicensed Copy: Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:51, Uncontrolled Copy, (c) BSIThis page deliberately left blankLicensed Copy:
48、 Wang Bin, ISO/EXCHANGE CHINA STANDARDS, 21/04/2011 08:51, Uncontrolled Copy, (c) BSIBSI is the independent national body responsible for preparing British Standards. It presents the UK view on standards in Europe and at the international level. It is incorporated by Royal Charter.British Standards
49、Institution (BSI)raising standards worldwideBSI Group Headquarters389 Chiswick High Road London W4 4AL UKTel +44 (0)20 8996 9001Fax +44 (0)20 8996 Standards are updated by amendment or revision. Users of BritishStandards should make sure that they possess the latest amendments oreditions.It is the constant aim of BSI to improve the quality of our pr