1、raising standards worldwideNO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBSI Standards PublicationBS EN ISO 2702:2011Heat-treated steel tappingscrews Mechanicalproperties (ISO 2702:2011)BS EN ISO 2702:2011 BRITISH STANDARDNational forewordThis British Standard is the UK imple
2、mentation of EN ISO 2702:2011.It supersedes BS EN ISO 2702:1995 which is withdrawn.The UK participation in its preparation was entrusted to TechnicalCommittee FME/9/3, Fasteners - Product Standards.A list of organizations represented on this committee can beobtained on request to its secretary.This
3、publication does not purport to include all the necessaryprovisions of a contract. Users are responsible for its correctapplication. BSI 2011ISBN 978 0 580 68775 4ICS 21.060.10Compliance with a British Standard cannot confer immunity fromlegal obligations.This British Standard was published under th
4、e authority of theStandards Policy and Strategy Committee on 31 May 2011.Amendments issued since publicationDate Text affectedEUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN ISO 2702 May 2011 ICS 21.060.10 Supersedes EN ISO 2702:1994English Version Heat-treated steel tapping screws - Mechanical
5、 properties (ISO 2702:2011) Vis tle en acier trait thermiquement - Caractristiques mcaniques (ISO 2702:2011) Wrmebehandelte Blechschrauben aus Stahl - Mechanische Eigenschaften (ISO 2702:2011) This European Standard was approved by CEN on 28 April 2011. CEN members are bound to comply with the CEN/C
6、ENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centr
7、e or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the
8、official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania,
9、 Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2011 CEN All rights of exploitation in any form and by any means reserved worl
10、dwide for CEN national Members. Ref. No. EN ISO 2702:2011: EBS EN ISO 2702:2011EN ISO 2702:2011 (E) 3 Foreword This document (EN ISO 2702:2011) has been prepared by Technical Committee ISO/TC 2 “Fasteners“ in collaboration with Technical Committee CEN/TC 185 “Fasteners” the secretariat of which is h
11、eld by DIN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by November 2011, and conflicting national standards shall be withdrawn at the latest by November 2011. Attention is drawn to the possibili
12、ty that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN ISO 2702:1994. According to the CEN/CENELEC Internal Regulations, the national standards orga
13、nizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Po
14、rtugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. Endorsement notice The text of ISO 2702:2011 has been approved by CEN as a EN ISO 2702:2011 without any modification. BS EN ISO 2702:2011ISO 2702:2011(E) ISO 2011 All rights reserved iiiForeword ISO (the Internat
15、ional Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has bee
16、n established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical stand
17、ardization. International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standards adopted by the technical committees are circulated to the member bodies for
18、 voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all
19、 such patent rights. ISO 2702 was prepared by Technical Committee ISO/TC 2, Fasteners, Subcommittee SC 13, Fasteners with non-metric thread. This third edition cancels and replaces the second edition (ISO 2702:1992), which has been technically revised. In particular, the following modifications have
20、 been carried out: a) the Scope was expended to ST9,5; b) the maximum core hardness was reduced from 390 HV to 370 HV (see 4.1.3); c) reference to ISO 898-7 concerning torque-measuring device was added (see 6.2.2). BS EN ISO 2702:2011ISO 2702:2011(E) iv ISO 2011 All rights reservedIntroduction The p
21、rimary objective of this International Standard is to ensure that tapping screws form mating threads in materials into which they are normally driven without deforming their own thread and without breaking during assembly or service. BS EN ISO 2702:2011INTERNATIONAL STANDARD ISO 2702:2011(E) ISO 201
22、1 All rights reserved 1Heat-treated steel tapping screws Mechanical properties 1 Scope This International Standard specifies the characteristics of heat-treated steel tapping screws, with tapping screw thread from ST2,2 to ST9,5 inclusive according to ISO 1478, together with the corresponding test m
23、ethods. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 898-7:1992, Me
24、chanical properties of fasteners Part 7: Torsional test and minimum torques for bolts and screws with nominal diameters 1 mm to 10 mm ISO 6507-1, Metallic materials Vickers hardness test Part 1: Test method 3 Materials Tapping screws shall be made from cold heading, case hardening quality steel. 4 R
25、equirements 4.1 Metallurgical requirements 4.1.1 Surface hardness The minimum surface hardness after heat treatment shall be 450 HV 0,3 (see ISO 6507-1). 4.1.2 Case depth The case depth shall conform to the values given in Table 1. Table 1 Case depth Dimensions in millimetres Thread Case depth min.
26、max. ST2,2, ST2,6 0,04 0,10 ST2,9, ST3,3, ST3,5 0,05 0,18ST3,9, ST4,2, ST4,8, ST5,5 0,10 0,23 ST6,3, ST8, ST9,5 0,15 0,28BS EN ISO 2702:2011ISO 2702:2011(E) 2 ISO 2011 All rights reserved4.1.3 Core hardness The core hardness after heat treatment shall be 270 HV 5 to 370 HV 5 for threads ST3,9, and 2
27、70 HV 10 to 370 HV 10 for threads ST4,2. 4.1.4 Microstructure The microstructure shall show no band of free ferrite between the case and core. 4.2 Mechanical requirements 4.2.1 Thread-forming capability Tapping screws shall form a mating thread without deforming their own thread when driven into a t
28、est plate, in accordance with 6.2.1. 4.2.2 Torsional strength Tapping screws shall have a torsional strength such that the torque necessary to cause failure, when tested in accordance with 6.2.2, shall equal or exceed the minimum torque values given in Table 3 for the applicable screw threads. 5 Acc
29、eptance For routine acceptance tests, the drive test, torsional test and core hardness test may be used, but for referee purposes all requirements specified in this International Standard shall be satisfied. 6 Test methods 6.1 Test methods for the metallurgical requirements 6.1.1 Surface hardness te
30、st The Vickers hardness test shall be carried out in accordance with ISO 6507-1. The impression of the pyramid shall be made on a flat face, preferably on the screw head. 6.1.2 Case depth Microscopic test Case depth shall be measured at the thread flank mid-point between crest and root or, in the ca
31、se of smaller tapping screws up to ST3,9, in the root of the thread. For referee purposes, a micro hardness plot shall be made using a Vickers indenter and a 300 g load on the thread profile of a properly prepared metallographic specimen. The case depth shall be the point at which the hardness recor
32、ded is 30 HV above the actual core hardness. 6.1.3 Core hardness test The Vickers core hardness test shall be carried out in accordance with ISO 6507-1 at the mid-radius of a transverse section through the screw taken at a distance sufficiently behind the point of the screw to be through the full mi
33、nor diameter. BS EN ISO 2702:2011ISO 2702:2011(E) ISO 2011 All rights reserved 36.1.4 Microstructure test The microstructure test shall be carried out by metallographic examination. 6.2 Test methods for the mechanical requirements 6.2.1 Drive test The sample screw (coated or uncoated, as received) s
34、hall be driven into a test plate until a thread of full diameter is completely through the test plate. The test plate shall be made from low carbon steel with a carbon content not exceeding 0,23 %. The hardness of the plate shall be 130 HV to 170 HV measured in accordance with ISO 6507-1. The thickn
35、ess of the plate shall conform to the values given in Table 2. The test hole shall be drilled, or punched and redrilled, or reamed to the hole diameter specified in Table 2 for the size of screw being tested. Table 2 Standard test plate thickness and hole diameter for drive test Dimensions in millim
36、etres Thread Plate thickness Hole diameter min. max. min. max. ST2,2 1,17 1,30 1,905 1,955 ST2,6 1,17 1,30 2,185 2,235 ST2,9 1,17 1,30 2,415 2,465 ST3,3 1,17 1,30 2,68 2,73 ST3,5 1,85 2,06 2,92 2,97 ST3,9 1,85 2,06 3,24 3,29 ST4,2 1,85 2,06 3,43 3,48 ST4,8 3,10 3,23 4,015 4,065 ST5,5 3,10 3,23 4,735
37、 4,785 ST6,3 4,67 5,05 5,475 5,525 ST8 4,67 5,05 6,885 6,935 ST9,5 4,67 5,05 8,270 8,330 In cases where screws are plated subsequent to delivery to the purchaser (or where plating of screws is otherwise under the control of the purchaser), the producer is not responsible for failure due to plating.
38、In such cases, the screw manufacturer can only be held responsible if it is proved that the failure is not due to any post-treatment. Screws from which the plating has been stripped off cannot be considered as samples. BS EN ISO 2702:2011ISO 2702:2011(E) 4 ISO 2011 All rights reservedKey 1 split thr
39、eaded die or threaded insert 2 threaded insert with a blind hole 3 split threaded die Figure 1 Torsional test apparatus 6.2.2 Torsional strength test The shank of the sample screw (coated or uncoated, as received) shall be clamped in a mating, split, threaded die or other device so that the clamped
40、portion of the screw is not damaged and at least two full threads project above the clamping device and at least two full-form threads exclusive of point are held within the clamping device. A threaded insert with a blind hole may be used in place of the clamping device (see Figure 1) provided the h
41、ole depth is such as to ensure that breakage occurs beyond the point. By means of a suitable calibrated torque-measuring device (in accordance with ISO 898-7:1992, 3.2.2), torque shall be applied to the screw until failure occurs. The screw shall meet the minimum torsional strength requirements give
42、n in Table 3. BS EN ISO 2702:2011ISO 2702:2011(E) ISO 2011 All rights reserved 5Table 3 Torsional strength Thread Minimum torsional strength Nm ST2,2 0,45 ST2,6 0,9 ST2,9 1,5 ST3,3 2,0 ST3,5 2,7 ST3,9 3,4 ST4,2 4,4 ST4,8 6,3 ST5,5 10,0 ST6,3 13,6 ST8 30,5 ST9,5 68,0 BS EN ISO 2702:2011ISO 2702:2011(
43、E) 6 ISO 2011 All rights reservedBibliography 1 ISO 1478, Tapping screws thread BS EN ISO 2702:2011This page deliberately left blankThis page deliberately left blankBSI is the independent national body responsible for preparing British Standardsand other standards-related publications, information a
44、nd services. It presents the UK view on standards in Europe and at the international level. It is incorporated by Royal Charter.British Standards Institution (BSI)raising standards worldwideBSI Group Headquarters389 Chiswick High Road London W4 4AL UKTel +44 (0)20 8996 9001Fax +44 (0)20 8996 Standa
45、rds are updated by amendment or revision. Users of British Stan-dards should make sure that they possess the latest amendments or editions.It is the constant aim of BSI to improve the quality of our products and serv-ices. We would be grateful if anyone finding an inaccuracy or ambiguity whileusing
46、this British Standard would inform the Secretary of the technical com-mittee responsible, the identity of which can be found on the inside frontcover.Tel: +44 (0)20 8996 9001 Fax: +44 (0)20 8996 7001BSI offers Members an individual updating service called PLUS which ensuresthat subscribers automatic
47、ally receive the latest editions of standards.Tel: +44 (0)20 8996 7669 Fax: +44 (0)20 8996 7001Email: Buying standardsYou may buy PDF and hard copy versions of standards directly using acredit card from the BSI Shop on the website addition all orders for BSI, international and foreign standards pub
48、licationscan be addressed to BSI Customer Services.Tel: +44 (0)20 8996 9001 Fax: +44 (0)20 8996 7001Email: In response to orders for international standards, it is BSI policy tosupply the BSI implementation of those that have been publishedas British Standards, unless otherwise requested.Information
49、 on standardsBSI provides a wide range of information on national, Europeanand international standards through its Knowledge Centre.Tel: +44 (0)20 8996 7004 Fax: +44 (0)20 8996 7005Email: Various BSI electronic information services are also available whichgive details on all its products and services. Tel: +44 (0)20 8996 7111 Fax: +44 (0)20 8996 7048Email: BSI Subscri