1、April 2010 Translation by DIN-Sprachendienst.English price group 7No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS 5
2、9.080.50!$aA“1626130www.din.deDDIN EN ISO 10572Mixed polyolefin fibre ropes (ISO 10572:2009)English translation of DIN EN ISO 10572:2010-04Polyolefingemisch-Faserseile (ISO 10572:2009)Englische bersetzung von DIN EN ISO 10572:2010-04Cordages en fibres de polyolfines mlanges (ISO 10572:2009)Traductio
3、n anglaise de DIN EN ISO 10572:2010-04SupersedesDIN EN 14687:2005-02www.beuth.deIn case of doubt, the German-language original shall be considered authoritative.Document comprises 12 pages04.10 DIN EN ISO 10572:2010-04 2 A comma is used as the decimal marker. National foreword This standard has been
4、 prepared by Technical Committee ISO/TC 38 “Textiles” (Secretariat: BSI, United Kingdom), Working Group WG 21 “Ropes, cordage and netting (Secretariat: AFNOR, France) in collaboration with Technical Committee CEN/TC 248 “Textiles and textile products” (Secretariat: BSI, United Kingdom), Working Grou
5、p WG 3 “Ropes and agricultural twines and fishing nets”. The responsible German body involved in its preparation was the Normenstelle Schiffs- und Meerestechnik (Shipbuilding and Marine Technology Standards Committee), Working Committee NA 132-01-08 AA Faser-seile. The DIN Standards corresponding to
6、 the International Standards referred to in clause 2 of this document are as follows: ISO 1968 DIN EN ISO 1968 ISO 2307 DIN EN ISO 2307 ISO 9554 DIN EN ISO 9554 Amendments This standard differs from DIN EN 14687:2005-02 as follows: a) EN 14687 has been adopted as EN ISO 10572. b) The standard has be
7、en editorially revised. Previous editions DIN EN 14687: 2005-02 National Annex NA (informative) Bibliography DIN EN ISO 1968, Fibre ropes and cordage Vocabulary DIN EN ISO 2307, Fibre ropes Determination of certain physical and mechanical properties DIN EN ISO 9554, Fibre ropes General specification
8、s EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN ISO 10572 December 2009 ICS 59.080.50 Supersedes EN 14687:2004English Version Mixed polyolefin fibre ropes (ISO 10572:2009) Cordages en fibres de polyolfines mlanges (ISO 10572:2009) Polyolefingemisch-Faserseile (ISO 10572:2009) This European St
9、andard was approved by CEN on 4 November 2009. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerni
10、ng such national standards may be obtained on application to the CEN Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own l
11、anguage and notified to the CEN Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania
12、, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2009 CEN A
13、ll rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN ISO 10572:2009: EContents Page Foreword3 1 Scope 4 2 Normative references 4 3 Terms and definitions .4 4 Designation 4 5 Materials .5 6 General requirements5 7 Physical properties6 8 Marki
14、ng 10 EN ISO 10572:2009 (E) DIN EN ISO 10572:2010-04 2 Foreword collaboration with Technical Committee CEN/TC 248 “Textiles and textile products” the secretariat of which is held by BSI. This European Standard shall be given the status of a national standard, either by publication of an identical te
15、xt or by endorsement, at the latest by June 2010, and conflicting national standards shall be withdrawn at the latest by June 2010. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible f
16、or identifying any or all such patent rights. This document supersedes EN 14687:2004. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Cyprus, Czech Republic,
17、Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. Endorsement notice The text of ISO 10572:2009 has been ap
18、proved by CEN as a EN ISO 10572:2009 without any modification. This document (EN ISO 10572:2009) has been prepared by Technical Committee ISO/TC 38 “Textiles” in EN ISO 10572:2009 (E) DIN EN ISO 10572:2010-04 3 1 Scope This International Standard specifies requirements for 3-strand hawser-laid, 4-st
19、rand shroud-laid, 8-strand braided and 12-strand braided ropes made of mixed polyolefin fibres, and gives rules for their designation. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applie
20、s. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 1968, Fibre ropes and cordage Vocabulary ISO 2307, Fibre ropes Determination of certain physical and mechanical properties ISO 9554:2005, Fibre ropes General specifications 3 Terms and de
21、finitions For the purposes of this document, the terms and definitions given in ISO 1968 apply. 4 Designation Fibre ropes shall be designated by the following: the words “fibre rope”; the number of this International Standard; the construction or type of rope (see Clause 6); the reference number of
22、the rope; the material from which the rope is made. EXAMPLE Designation of a 3-strand hawser-laid rope, reference number 20 (Type A), corresponding to a linear density of 181 ktex made of mixed polyolefin fibre (PO): Fibre rope ISO 10572 - A - 20 - PO EN ISO 10572:2009 (E) DIN EN ISO 10572:2010-04 4
23、 5 Materials The rope shall be constructed using bi-component fibres made of a blend during extrusion of polypropylene and of polyethylene, with a minimum of 15 % and a maximum of 50 % of polyethylene. 6 General requirements 6.1 Mixed polyolefin fibre ropes shall be constructed in one of the followi
24、ng ways: type A: 3-strand hawser-laid rope (see Figure 1); type B: 4-strand shroud-laid rope (see Figure 2); type L: 8-strand braided rope (see Figure 3); type T: 12-strand braided rope (see Figure 4). Figure 1 Shape of a 3-strand hawser-laid rope (type A) Figure 2 Shape of an 4-strand shroud-laid r
25、ope (type B) EN ISO 10572:2009 (E) DIN EN ISO 10572:2010-04 5 Figure 3 Shape of an 8-strand braided rope (type L) Figure 4 Shape of a 12-strand braided rope (type T) 6.2 Construction, manufacture, lay, labelling, packaging, invoicing and delivery lengths shall conform to ISO 9554. 7 Physical propert
26、ies The linear density and minimum breaking force shall conform to Tables 1, 2 and 3. Table 1 Linear density and minimum breaking force of 3-strand hawser-laid mixed polyolefin fibre ropes (type A) Linear densitybcMinimum breaking forcedekN Reference numberaNominal ktex Tolerance % Unspliced ropes R
27、opes with eye-spliced terminations 6 16,3 6,76 6,08 8 29,0 10 11,7 10,5 10 45,3 18,0 16,2 12 65,2 8 25,4 22,9 14 88,8 34,0 30,6 16 116 43,5 39,2 18 147 54,5 49,0 20 181 66,2 59,6 22 219 79,1 71,2 24 261 92,8 83,5 26 306 107 96,3 28 355 123 111 30 408 5 140 126 EN ISO 10572:2009 (E) DIN EN ISO 10572:
28、2010-04 6 Table 1 (continued) Linear densitybcMinimum breaking forcedekN Reference numberaNominal ktex Tolerance % Unspliced ropes Ropes with eye-spliced terminations 32 464 157 141 36 587 194 175 40 725 234 211 44 877 277 249 48 1 040 325 293 52 1 220 376 338 56 1 420 429 386 60 1 630 486 437 64 1
29、860 544 490 68 2 100 609 548 72 2 350 677 609 80 2 900 818 736 88 3 510 985 887 96 4 170 5 1 170 1 050 aThe reference number corresponds to the approximate diameter, in millimetres. bThe linear density, in kilotex, corresponds to the net mass per length of the rope, expressed in grams per metre or i
30、n kilograms per kilometre. cThe linear density is obtained under reference tension and is measured as specified in ISO 2307.dThe breaking forces relate to new, dry and wet ropes.eA force determined by the test methods specified in ISO 2307 is not necessarily an accurate indication of the force at wh
31、ich that rope might break in other circumstances and situations. The type and quality of terminations, the rate of force application, prior conditioning and previous force applications to the rope can significantly influence the breaking force. A rope bent around a post, capstan, pulley or sheave ma
32、y break at a significantly lower force. A knot or other distortion in a rope may significantly reduce the breaking force. EN ISO 10572:2009 (E) DIN EN ISO 10572:2010-04 7 Table 2 Linear density and minimum breaking force of 4-strand shroud-laid mixed polyolefin ropes (type B) Linear densitybcMinimum
33、 breaking forcedekN Reference numberaNominal ktex Tolerance % Unspliced ropes Ropes with eye-spliced terminations 6 16,3 6,08 5,47 8 29,0 10 10,5 9,45 10 45,3 16,2 14,6 12 65,2 8 22,9 20,6 14 88,8 30,6 27,5 16 116 39,2 35,2 18 147 49,1 44,2 20 181 59,6 53,6 22 219 71,2 64,1 24 261 83,5 75,2 26 306 9
34、6,3 86,7 28 355 111 100 30 408 126 113 32 464 141 127 36 587 175 158 40 725 5 211 190 44 877 249 224 48 1 040 293 264 52 1 220 338 304 56 1 420 386 347 60 1 630 437 393 64 1 860 490 441 68 2 100 548 493 72 2 350 609 548 80 2 900 736 662 88 3 510 887 798 96 4 170 1 050 945 aThe reference number corre
35、sponds to the approximate diameter, in millimetres. bThe linear density, in kilotex, corresponds to the net mass per length of the rope, expressed in grams per metre or in kilograms per kilometre. cThe linear density is obtained under reference tension and is measured as specified in ISO 2307.dThe b
36、reaking forces relate to new, dry and wet ropes.eA force determined by the test methods specified in ISO 2307 is not necessarily an accurate indication of the force at which that rope might break in other circumstances and situations. The type and quality of terminations, the rate of force applicati
37、on, prior conditioning and previous force applications to the rope can significantly influence the breaking force. A rope bent around a post, capstan, pulley or sheave may break at a significantly lower force. A knot or other distortion in a rope may significantly reduce the breaking force. EN ISO 1
38、0572:2009 (E) DIN EN ISO 10572:2010-04 8 Table 3 Linear density and minimum breaking force of 8-strand braided mixed polyolefin fibre rope (type L) and 12-strand braided mixed polyolefin fibre rope (type T) Linear densitybcMinimum breaking forcedekN Reference numberaNominal ktex Tolerance % Unsplice
39、d ropes Ropes with eye-spliced terminations 6 16,3 6,9 6,2 8 29,0 10 12,1 10,9 10 45,3 18,8 16,9 12 65,2 8 26,9 24,2 14 88,8 36,4 32,7 16 116 47,2 42,5 18 147 59,3 53,4 20 181 72,8 65,5 22 219 87,4 78,7 24 261 104 93,6 26 306 121 109 28 355 139 125 30 408 158 142 32 464 179 161 36 587 224 202 40 725
40、 274 247 44 877 327 294 48 1 040 385 347 52 1 220 5 448 403 56 1 420 514 463 60 1 630 583 525 64 1 860 657 591 68 2 100 737 663 72 2 350 820 738 80 2 900 995 896 88 3 510 1 190 1 070 96 4 170 1 400 1 260 104 4 900 1 620 1 460 112 5 680 1 880 1 690 120 6 520 2 130 1 920 128 7 420 2 420 2 180 136 8 38
41、0 2 720 2 450 144 9 390 3 040 2 740 EN ISO 10572:2009 (E) DIN EN ISO 10572:2010-04 9 Table 3 (continued) Linear densitybcMinimum breaking forcedekN Reference numberaNominal ktex Tolerance % Unspliced ropes Ropes with eye-spliced terminations 152 10 500 3 380 3 040 160 11 600 5 3 740 3 370 aThe refer
42、ence number corresponds to the approximate diameter, in millimetres. bThe linear density, in kilotex, corresponds to the net mass per length of the rope, expressed in grams per metre or in kilograms per kilometre. cThe linear density is obtained under reference tension and is measured as specified i
43、n ISO 2307.dThe breaking forces relate to new, dry and wet ropes.eA force determined by the test methods specified in ISO 2307 is not necessarily an accurate indication of the force at which that rope might break in other circumstances and situations. The type and quality of terminations, the rate o
44、f force application, prior conditioning and previous force applications to the rope can significantly influence the breaking force. A rope bent around a post, capstan, pulley or sheave may break at a significantly lower force. A knot or other distortion in a rope may significantly reduce the breaking force. 8 Marking The marking shall be carried out in accordance with Clause 6 of ISO 9554:2005. EN ISO 10572:2009 (E) DIN EN ISO 10572:2010-04 10