1、February 2011 Translation by DIN-Sprachendienst.English price group 10No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).I
2、CS 25.220.20!$mP-“1744510www.din.deDDIN EN ISO 6719Anodizing of aluminium and its alloys Measurement of reflectance characteristics of aluminium surfaces usingintegrating-sphere instruments (ISO 6719:2010)English translation of DIN EN ISO 6719:2011-02Anodisieren von Aluminium und Aluminiumlegierunge
3、n Messung der Reflexionseigenschaften von Aluminiumoberflchen mit Hilfe UlbrichtscherKugeln (ISO 6719:2010)Englische bersetzung von DIN EN ISO 6719:2011-02Anodisation de laluminium et de ses alliages Mesurage des caractristiques de rflectivit des surfaces daluminium laidedinstruments sphre dintgrati
4、on (ISO 6719:2010)Traduction anglaise de DIN EN ISO 6719:2011-02SupersedesDIN EN 12373-12:2000-12www.beuth.deDocument comprises pagesIn case of doubt, the German-language original shall be considered authoritative.1602.11 DIN EN ISO 6719:2011-02 2 A comma is used as the decimal marker. National fore
5、word This standard has been prepared by Technical Committee ISO/TC 79 “Light metals and their alloys”, Subcommittee SC 2/WG 16 “Revisions for systematic reviewed TC 79/SC 2 ISO standards” (Secretariat: JISC, Japan) in collaboration with Technical Committee CEN/TC 132 “Aluminium and aluminium alloys”
6、, Working Group WG 15 “Aluminium anodisation” (Secretariat: BSI, United Kingdom). The responsible German body involved in its preparation was the Normenausschuss Nichteisenmetalle (Nonferrous Metals Standards Committee), Working Committee NA 066-01-09 AA Anodisch oxidiertes Aluminium. Amendments Thi
7、s standard differs from DIN EN 12373-12:2000-12 as follows: a) the standard has been adopted as DIN EN ISO 6719:2011-02, and the main title has been modified (see National Annex NA); b) the standard has been editorially revised. Previous editions DIN EN 12373-12: 2002-12 DIN EN ISO 6719:2011-02 3 Na
8、tional Annex NA (informative) Correspondence between the previous standards series DIN EN 12373 “Aluminium and aluminium alloys Anodizing” and the corresponding new ISO and DIN EN ISO Standards Table NA.1 Correspondence previous now DIN EN 12373 DIN EN ISO Anodizing of aluminium and its alloys Part
9、1 7599 General specifications for anodic oxidation coatings on aluminium The title has been slightly changed Part 2 2106 Determination of mass per unit area (surface density) of anodic oxidation coatings Gravimetric method Part 3 2128 Determination of thickness of anodic oxidation coatings Non-destr
10、uctive measurement by split-beam microscope Part 4 2143 Estimation of loss of absorptive power of anodic oxidation coatings after sealing Dye spot test with prior acid treatment Part 5 2931 Assessment of quality of sealed anodic oxidation coatings by measurement of admittance Part 6 Part 7 3210 Asse
11、ssment of quality of sealed anodic oxidation coatings by measurement of the loss of mass after immersion in phosphoric acid/chromic acid solution The title has been changed: with/without prior acid treatment Part 8 6581 Determination of the comparative fastness to ultra-violet light and heat of colo
12、ured anodic oxidation coatings Part 9 Part 10 8251 Measurement of abrasion resistance of anodic oxidation coatings The title has been changed Part 11 7668 Measurement of specular reflectance and specular gloss of anodic oxidation coating at angles of 20 degrees, 45 degrees, 60 degrees or 85 degrees
13、Part 12 6719 Measurement of reflectance characteristics of aluminium surfaces using integrating-sphere instruments Part 13 7759 Measurement of reflectance characteristics of aluminium surface using a goniophotometer or an abridged goniophotometer The German title has been slightly changed Part 14 10
14、215 Visual determination of image clarity of anodic oxidation coatings Chart scale method Part 15 3211 Assessment of resistance of anodic oxidation coatings to cracking by deformation Part 16 2085 Check for continuity of thin anodic oxidation coatings Copper sulphate test Part 17 2376 Determination
15、of electric breakdown potential Part 18 8993 Rating system for the evaluation of pitting corrosion Chart method Part 19 8994 Rating system for the evaluation of pitting corrosion Grid method DIN EN ISO 6719:2011-02 4 This page is intentionally blank EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM
16、EN ISO 6719 October 2010 ICS 25.220.20 Supersedes EN 12373-12:2000English Version Anodizing of aluminium and its alloys - Measurement of reflectance characteristics of aluminium surfaces using integrating-sphere instruments (ISO 6719:2010) Anodisation de laluminium et de ses alliages - Mesurage des
17、caractristiques de rflectivit des surfaces daluminium laide dinstruments sphre dintgration (ISO 6719:2010) Anodisieren von Aluminium und Aluminiumlegierungen - Messung der Reflexionseigenschaften von Aluminiumoberflchen mit Hilfe Ulbrichtscher Kugeln (ISO 6719:2010) This European Standard was approv
18、ed by CEN on 14 October 2010. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national
19、standards may be obtained on application to the CEN Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notif
20、ied to the CEN Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxemb
21、ourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2010 CEN All right
22、s of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN ISO 6719:2010: EContents DIN EN ISO 6719:2011-02 EN ISO 6719:2010 (E) 2 Page Foreword3 1 Scope 4 2 Normative references 4 3 Principle4 4 Apparatus .4 4.1 General4 4.2 Geometrical specifications of
23、 the apparatus5 4.3 Specular-included and specular-excluded determinations 5 4.4 Irradiation beam.5 4.5 Housing.6 5 Calibration and operation of the reflectometer 10 5.1 General10 5.2 Reference standards .11 6 Measurement11 7 Expression of results 11 7.1 Calculation of reflectance values.11 8 Test r
24、eport 12 Foreword The text of ISO 6719:2010 has been prepared by Technical Committee ISO/TC 79 “Light metals and their alloys” of the International Organization for Standardization (ISO) and has been taken over as EN ISO 6719:2010 by Technical Committee CEN/TC 132 “Aluminium and aluminium alloys” th
25、e secretariat of which is held by AFNOR. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by April 2011, and conflicting national standards shall be withdrawn at the latest by April 2011. Attention is
26、 drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 12373-12:2000. According to the CEN/CENELEC Internal Regulations, the
27、national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherla
28、nds, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. Endorsement notice The text of ISO 6719:2010 has been approved by CEN as a EN ISO 6719:2010 without any modification. DIN EN ISO 6719:2011-02 EN ISO 6719:2010 (E) 3 1 Scope This Internation
29、al Standard specifies a method of measuring the total and diffuse luminous reflectance characteristics of aluminium surfaces, using integrating-sphere instruments. The method described is also applicable to the measurement of specular reflectance (principal gloss value), specularity and diffuseness.
30、 The method is unsuitable for use with lighting reflectors. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (i
31、ncluding any amendments) applies. ISO 7724-2, Paints and varnishes Colorimetry Part 2: Colour measurement ISO 11664-2:2007, Colorimetry Part 2: CIE standard illuminants 3 Principle Measurement, using an integrating-sphere reflectometer, of the total and diffuse reflected light at different angles of
32、 incidence, close to the normal surface of a test specimen. 4 Apparatus 4.1 General The reflectometer, suitable for measuring the reflectance of metallic surfaces, consists of a suitable light source, an integrating sphere and a photometer comprising a photo-electric cell with a signal multiplier an
33、d recording, indicating, or computing equipment. Figures 1 to 5 show the optical systems and geometry of typical instruments. The incident light beam is allowed to fall onto the specimen and is reflected into the sphere, the interior of which is white, where it is automatically integrated. The avera
34、ge light flux, as measured by the photometer, is a measure of the quantity of the reflected light. The spectral product of the light source, spectral filters, and spectral response of the light detector shall closely simulate the spectral product of the CIE source C (or D65) and the spectral luminou
35、s efficiency V() for photopic vision, in accordance with ISO 11664-2. DIN EN ISO 6719:2011-02 EN ISO 6719:2010 (E) 4 4.2 Geometrical specifications of the apparatus 4.2.1 Integrating sphere The interior of the sphere, white-coated and fitted with a device to permit measurement of reflectance, either
36、 including or excluding specular reflectance, serves to collect the reflected light flux. Any diameter of sphere is satisfactory, provided that the total port area does not exceed 5 % of the total internal surface. The internal surface shall be diffusing and of a highly reflective white for the whol
37、e of the visible spectrum. The entrance and specimen ports of the instrument shall be centred on the same great circle with an arc of more than 170 between their centres. The specimen port shall subtend 8 1 of arc in relation to the centre of the entrance port. The irradiating beam shall pass throug
38、h the centreline of the entrance and specimen ports. A photometer shall be positioned on the sphere at 90 0,5 from the entrance port. 4.3 Specular-included and specular-excluded determinations 4.3.1 Pivotable sphere In the pivotable-sphere type of instrument (Figures 1 to 4), the sphere can turn abo
39、ut a vertical axis passing through the specimen port, rotating 9 1 to provide for the measurements of specular-included or total reflectance (Q) and specular-excluded or diffuse reflectance (Qd). 4.3.2 Fixed sphere (Type 1) In the fixed-sphere Type 1 instrument, the specimen is held so that the inci
40、dent beam falls on it at an angle of 9 1 to the normal. A port, of the same dimensions as the entrance port, is provided in order to accept the specular reflection. Interchangeable caps are provided for this port, a black one to absorb the specular reflection for diffuse reflectance (Qd) measurement
41、s and one coated with the same material as the inside of the sphere for total reflectance (Q) measurements. 4.3.3 Fixed sphere (Type 2) In the fixed-sphere Type 2 instrument (see Figure 5), the sphere is fixed and only the specimen can be inclined. A wedge, as shown in Figure 5, designed to exclude
42、ambient light, and white-coated like the sphere interior, allows adjustment of the angle of the specimen surface. For measurement of diffuse reflectance (Qd), the specimen surface is adjusted to be perpendicular to the incident beam. For measurement of total reflectance (Q), the specimen surface is
43、inclined at 9 1 from the normal incident beam by insertion of the wedge. 4.4 Irradiation beam The light beam shall be substantially unidirectional with a maximum angle of any ray being less than 3 from the axis of the beam. It shall not be vignetted at either port. The incident light beam shall have
44、 a circular cross-section concentric with the specimen port and shall have an annulus of 1,3 0,1 subtended at the entrance port. On reflection from a first surface mirror, the specular-excluded beam shall be concentric with the centre of the port when the sphere is in the specular-excluded position.
45、 The mirror-reflected beam shall have a concentric circle with the port and shall have an annulus of 0,6 0,2 subtended at the level of the exit port. The size of the exit port shall be not more than 0,1 greater than that of the annulus. NOTE The dimensions of this beam can be most easily measured at
46、 a point beyond the sphere at a distance corresponding to the diameter of the integrating sphere, with no obstruction at either port. However, this will not ensure alignment when specularly reflected. DIN EN ISO 6719:2011-02 EN ISO 6719:2010 (E) 5 4.5 Housing A housing shall be provided to prevent a
47、mbient light from entering the entrance port. Key 1 photoelectric cell 7 mirror 2 test piece 8 light source 3 lens 9 lens 4 0 incidence for diffuse reflectance 10 aperture 5 9 1 incidence for total reflectance 11 spectral filter 6 photoelectric cell for comparison aTo the amplifiers and recorders. F
48、igure 1 Schematic optical plan of one type of pivotable-sphere reflectometer DIN EN ISO 6719:2011-02 EN ISO 6719:2010 (E) 6 Key 1 sphere in axial position 8 light beam at exit port 2 sphere in pivoted position 9 source 3 test piece 10 convex lens 4 specular pivot 11 specular filter 5 specular beam s
49、phere in pivoted position 12 aperture 6 incoming light beam from the axial position 13 lens 7 incoming light beam at entrance port (axis positions) 14 receiver Figure 2 Schematic optical plan of another type of pivotable-sphere reflectometer DIN EN ISO 6719:2011-02 EN ISO 6719:2010 (E) 7 Key 1 spectral filter 6 lens 2 lens 7 in pivoted position 3 test piece 8 in axial position 4 sphere pivot 9 recorder 5 light source Figure 3 Geometry of typical pivotable-sphere re