1、 MS27638E 22 October 2009 SUPERSEDING MS27638D 29 September 2000 DETAIL SPECIFICATION SHEET MANDREL SLEEVE SETTING This specification is approved for use by all Departments and Agencies of the Department of Defense. The requirements for acquiring the product described herein shall consist of this sp
2、ecification sheet and MIL-DTL-83296. FIGURE 1. Mandrel sleeve setting dimensions and configuration. AMSC N/A FSC 4730 INCH-POUND Inches mm .005 .02 .06 .44 .50 .62 1.25 1.50 0.13 0.51 1.52 11.18 12.70 15.75 31.75 38.10 Provided by IHSNot for ResaleNo reproduction or networking permitted without lice
3、nse from IHS-,-,-MS27638E 2 PIN A .02 inches (cm) B .02 inches (mm) C .005 inches (mm) D .005 inches (mm) E min inches (mm) max inches (mm) MS27638-4C 3.37 (8.56) 1.12 (28.45) .325 (8.26) .475 (12.07) .225 (5.72) .230 (5.84) MS27638-6C 3.75 (9.53) 1.50 (38.10) .300 (7.62) .605 (15.37) .322 (8.18) .3
4、34 (8.48) MS27638-8C 4.25 (10.80) 2.00 (50.80) .355 (9.02) .705 (17.91) .440 (11.18) .445 (11.30) MS27638-10C 4.25 (10.80) 2.00 (50.80) .295 (7.49) .870 (22.10) .575 (14.61) .580 (14.73) NOTES: 1. Dimensions are in inches. 2. Metric equivalents are given for information only. 3. Unless otherwise spe
5、cified, tolerances shall be .005 inch (0.13 mm). 4. Surface roughness, in accordance with ASME B46.1, shall not exceed 125 in Ra, unless otherwise specified. 5. For hex, use commercial stock size tolerance in accordance with SAE-AMS2241. 6. Dimensioning and tolerancing are in accordance with ASME Y1
6、4.5M. 7. Unless otherwise specified, radius or break all corners to .005 +.005/-.000 inch (0.13 +0.13/-0.00 mm). 8. All burrs and slivers shall be removed. FIGURE 1. Mandrel sleeve setting dimensions and configuration - Continued. REQUIREMENTS: Dimensions and configurations: The design, construction
7、, and physical dimensions shall be in accordance with MIL-DTL-83296 and figure 1, in case of conflict between this specification sheet and MIL-DTL-83296, this specification sheet shall govern. This part for use with hose assemblies in accordance with MIL-DTL-32330. Material: Material shall be tool s
8、teel alloy UNS T41902, type 2 in accordance with ASTM A681. Hardness: Hardness shall be Rockwell C 58 to 60. Finish: Finish shall be black oxide in accordance with SAE-AMS2485. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MS27638E 3 PIN example: M
9、S27638 -4 C PIN example: MS27638-4C indicates a sleeve setting mandrel 1/4 inch, tool steel alloy. Changes from previous issue. Marginal notations are not used in this revision to identify changes due to the extent of the changes. Referenced documents. In addition to MIL-DTL-83296, this document ref
10、erences the following: MIL-DTL-32330 ASME B46.1 ASME Y14.5M ASTM A681 SAE-AMS2241 SAE-AMS2485 CONCLUDING MATERIAL Custodians: Preparing activity: Army - AV DLA - CC Navy - AS Air Force - 99 (Project 4730-2008-069) DLA - CC Review activities: Navy - MC, SA Air Force - 71 NOTE: The activities listed a
11、bove were interested in this document as of the date of this document. Since organizations and responsibilities can change, you should verify the currency of the information above using the ASSIST Online database at http:/assist.daps.dla.mil. Specification sheet number Dash size (see figure 1) Material (C for CRES) MS prefix Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-