1、BS EN 4632-002:2008ICS 49.025.01NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBRITISH STANDARDAerospace series Welded and brazed assemblies for aerospace constructions Weldability and brazeability of materialsPart 002: Homogeneous assemblies aluminium and aluminium alloysThis
2、 British Standardwas published underthe authority of theStandards Policy andStrategy Committee on 30September 2009 BSI 2009ISBN 978 0 580 60592 5Amendments/corrigenda issued since publicationDate CommentsBS EN 4632-002:2008National forewordThis British Standard is the UK implementation of EN 4632-00
3、2:2008.The UK participation in its preparation was entrusted to TechnicalCommittee ACE/61, Metallic materials for aerospace purposes.A list of organizations represented on this committee can be obtained onrequest to its secretary.This publication does not purport to include all the necessary provisi
4、onsof a contract. Users are responsible for its correct application.Compliance with a British Standard cannot confer immunityfrom legal obligations.BS EN 4632-002:2008EUROPEAN STANDARDNORME EUROPENNEEUROPISCHE NORMEN 4632-002April 2008ICS 49.025.01English VersionAerospace series - Welded and brazed
5、assemblies foraerospace constructions - Weldability and brazeability ofmaterials - Part 002: Homogeneous assemblies aluminium andaluminium alloysSrie arospatiale - Assemblages souds et brass pourconstructions arospatiales - Soudabilit et brasabilit desmatriaux - Partie 002 : Assemblages homognes del
6、aluminium et des alliages daluminiumLuft- und Raumfahrt - Schwei- und Ltverbindungen frdie Luft- und Raumfahrt - Schweibarkeitsgrad undLtbarkeitsgrad von Werkstoffen - Teil 002: GleichartigeVerbingungen Aluminium und AluminiumlegierungenThis European Standard was approved by CEN on 7 March 2008.CEN
7、members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this EuropeanStandard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such nationalstandards may be obtained on applica
8、tion to the CEN Management Centre or to any CEN member.This European Standard exists in three official versions (English, French, German). A version in any other language made by translationunder the responsibility of a CEN member into its own language and notified to the CEN Management Centre has t
9、he same status as theofficial versions.CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland,France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal
10、,Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.EUROPEAN COMMITTEE FOR STANDARDIZATIONCOMIT EUROPEN DE NORMALISATIONEUROPISCHES KOMITEE FR NORMUNGManagement Centre: rue de Stassart, 36 B-1050 Brussels 2008 CEN All rights of exploitation in any form and by any means reserv
11、edworldwide for CEN national Members.Ref. No. EN 4632-002:2008: EBS EN 4632-002:2008EN 4632-002:2008 (E) 2 Contents Page Foreword3 1 Scope 4 2 Normative references 4 3 Terms, definitions, symbols and abbreviations .5 4 Use of this standard 5 5 Updating this standard5 6 Index of aluminium and alumini
12、um alloy sheets6 7 Material sheets.7 Bibliography 31 BS EN 4632-002:2008EN 4632-002:2008 (E) 3 Foreword This document (EN 4632-002:2008) has been prepared by the Aerospace and Defence Industries Association of Europe - Standardization (ASD-STAN). After enquiries and votes carried out in accordance w
13、ith the rules of this Association, this Standard has received the approval of the National Associations and the Official Services of the member countries of ASD, prior to its presentation to CEN. This European Standard shall be given the status of a national standard, either by publication of an ide
14、ntical text or by endorsement, at the latest by October 2008, and conflicting national standards shall be withdrawn at the latest by October 2008. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be hel
15、d responsible for identifying any or all such patent rights. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland
16、, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. BS EN 4632-002:2008EN 4632-002:2008 (E) 4 1 Scope This standard defines degrees of
17、 weldability and brazeability for materials or families of materials used in the aerospace industry. It comprises a series of sheets, by materials or by material family which: indicate the main titles, the typical chemical composition and the main characteristics, contain recommendations for welding
18、 and brazing, indicate a degree of weldability or brazeability for a given process under defined conditions. indicate a value of the mechanical strength coefficient of the welded joint for each welding process, when it could be extracted from bibliographic references referring to it. The joint coeff
19、icient is expressed as a ratio of the tensile strength of the welded joint to the tensile strength of the base alloy. It is applicable without restriction for the manufacturing of new parts or for repair. 2 Normative references The following referenced documents are indispensable for the application
20、 of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 485-1, Aluminium and aluminium alloys Sheet, strip and plate Part 1: Technical conditions for inspection and delivery.
21、 EN 485-2, Aluminium and aluminium alloys Sheet, strip and plate Part 2: Mechanical properties. EN 515, Aluminium and aluminium alloys Wrought products Temper designations. EN 573-2, Aluminium and aluminium alloys Chemical composition and form of wrought products Part 2: Chemical symbol based design
22、ation system. EN 573-3, Aluminium and aluminium alloys Chemical composition and form of wrought products Part 3: Chemical composition and form of products. EN 1011-4, Welding Recommendations for welding of metallic materials Part 4: Arc welding of aluminium and aluminium alloys. EN 1706, Aluminium a
23、nd aluminium alloys Castings Chemical composition and mechanical properties. EN 2032-1, Aerospace series Metallic materials Part 1: Conventional designation. EN 2726, Aerospace series Aluminium alloy AL-C42201 T6 Sand casting a 20 mm. 1)EN 2728, Aerospace series Aluminium alloy AL-C42101 T6 Sand cas
24、ting a 20 mm. 1)EN 4632-001, Aerospace series Welded and brazed assemblies for aerospace constructions Weldability and brazeability of materials Part 001: General requirements. EN ISO 18273, Welding consumables Wire electrodes, wires and rods for welding of aluminium and aluminium alloys Classificat
25、ion. 1) Published as ASD Prestandard at the date of publication of this standard. BS EN 4632-002:2008EN 4632-002:2008 (E) 5 ANSI/AWS A5.10-80, Specification for bare aluminum and aluminum alloy welding electrodes and rods. 2)ASTM/ANSI B209, Standard specification for aluminum and aluminium alloy she
26、et and plate. SAE-AMS 4031, Aluminum alloy, sheet and plate 6.3Cu - 0.30Mn - 0.18Zr - 0.10V - 0.06Ti (2219-0) annealed. 3)SAE-AMS 4191, Aluminum alloy, welding wire 6.3Cu - 0.30Mn - 0.18Zr - 0.15Ti - 0.10V (2319). 3)SAE-AMS-QQ-A-250/30, Aluminum alloy 2219, plate and sheet. 3)SAE-AMS-A-21180, Alumin
27、um-alloy casting, high strength. 3)3 Terms, definitions, symbols and abbreviations For the purposes of this document, the terms and definitions given in EN 4632-001 apply. PWHT: Post-Welding Heat Treatment F: Foil p: powder w: wire AFB: Air Furnace Brazing FLB: Flame Brazing VFB: Vacuum Furnace Braz
28、ing 4 Use of this standard The index of material sheets contained in this standard, classified by family based on the main element used in the chemical composition and on the alloy structure, is given in Clause 6 in this standard. The degree of weldability or brazeability to be used is the value ind
29、icated by the material sheet considered for the process chosen. In the operating cycle, choose thermal states that give the lowest degree in preference. If two degrees are indicated, the responsible person must select the degree that is most appropriate for the definition of the assembly. 5 Updating
30、 this standard See EN 4632-001. 2) Published by: AWS, 550 N.W. LeJeune Road, Miami, Florida 33126. 3) Published by: Society of Automotive Engineers, Inc. (SAE), 400 Commonwealth Drive, Warrendale, PA 15096-0001, USA. BS EN 4632-002:2008EN 4632-002:2008 (E) 6 6 Index of aluminium and aluminium alloy
31、sheets 6.1 Index by material family family 1000: sheet 7.1 family 2000: sheets 7.2 to 7.7 family 5000: sheets 7.8 and 7.9 family 6000: sheet 7.10 family 7000: sheets 7.11 and 7.12 foundry alloys family: sheet 7.13 6.2 Numeric index Sheet Material 7.1 1050A - 1060 7.2 7.3 7.4 7.5 7.6 7.7 2001 2014 20
32、17A 2024 2219 2618A 7.8 7.9 5056A, 5083, 5086, 5182, 5456 5754 7.10 6005A, 6013, 6016, 6056, 6060, 6061, 6063, 6081, 6082, 6181 7.11 7.12 7020, 7051 7050, 7075, 7175, 7475 7.13 Al Si 7 Mg 0,3 and Al Si 7 Mg 0,6 BS EN 4632-002:2008EN 4632-002:2008 (E) 7 7 Material sheets 7.1 Designation: EN 573-2 : E
33、N AW-1050A; EN AW-1060 Old designation : A5, A6 EN 2032-1 : AL-P1050A; AL-P1060 ISO : Al 99,5; Al 99,6 Other standards : Typical composition: See EN 573-3. Grade Al Si Fe Cu Mn Mg Zn Ti 1050A base 0,25 0,40 0,05 0,05 0,05 0,07 0,05 1060 base 0,25 0,35 0,05 0,03 0,03 0,05 0,05 Structure: Without stru
34、ctural hardening Particular characteristics: Recommendations for welding and filling with EN AW-1050A and EN AW-1060 Process Thickness range in mm State before welding PWHT Degree of weldabilityJoint coefficient Comments and bibliographic references OA O or H111 none 1 TIG 2 O or H111 none 1 1 Fille
35、r metal same grade 1050 or 1080 45 EBW O or H111 none 1 1 RSEW, RSW O or H111 or H24 none 2 BS EN 4632-002:2008EN 4632-002:2008 (E) 8 7.2 Designation: EN 573-2 : EN AW-2001 Old designation : AU6 MGT EN 2032-1 : AL-P2001- ISO : Al Cu 5,5 Mg Mn Other standards : Typical composition: See EN 573-3. Grad
36、e Al Si Fe Cu Mn Mg Cr Zn Ti Ni Zr 2001- base 0,20 0,20 5,2 to 6,0 0,15 to 0,50 0,20 to 0,45 0,10 0,10 0,20 0,05 0,05 Structure: With structural hardening Particular characteristics: Recommendations for welding and filling with EN AW-2001 Process Thickness range in mm State before welding PWHT Degre
37、e of weldabilityJoint coefficientComments and bibliographic references T4 T 2 Micro-porosity in the weld 49 1 T6 none 2 No porosity Area with large grains in the base metal T4 T 2 Micro-porosity in the weld 49 8 T6 none 2 No porosity EBW 30 T4 T6 T none 2 2 No porosity 49 RSEW, RSW T6 2 BS EN 4632-0
38、02:2008EN 4632-002:2008 (E) 9 7.3 Designation: EN 573-2 : EN AW-2014 Old designation : AU4 SG EN 2032-1 : AL-P2014- ISO : Al Cu 4 Si Mg Other standards: Typical composition: See EN 573-3. Grade Al Si Fe Cu Mn Mg Cr Zn Ti Ni 2014- base 0,50 to 1,2 0,7 3,9 to 5,0 0,40 to 1,2 0,20 to 0,8 0,10 0,25 0,15
39、 0,10 Al Ti + Zr base 0,20 only for extruded or forged products with agreement between supplier and customer Structure: With structural hardening Particular characteristics: BS EN 4632-002:2008EN 4632-002:2008 (E) 10 Recommendations for welding and filling with EN AW-2014 Process Thickness range in
40、mm State before welding PWHT Degree of weldabilityJoint coefficientComments and bibliographic references OA 4 TIG 4 T4 T4 2 Porosity in the weld 1 T6 none 2 No porosity and area with large grains in the base metal 50 T4 T6 Micro-porosity 8 T6 none 2 No porosity 50 EBW 30 T4 T6 T6 none 2 to 3 2 to 3
41、No porosity 50 RSEW, RSW T6 2 FSW 22 6,35 T6 T651 none none 2 2 0,68 43 44 BS EN 4632-002:2008EN 4632-002:2008 (E) 11 7.4 Designation: EN 573-2 : EN AW-2017A Old designation : AU4G EN 2032-1 : AL-P2017A ISO : Al Cu 4 Mg 1 Other standards : Typical composition: See EN 573-3. Grade Al Si Fe Cu Mn Mg C
42、r Zn Ti + Zr 2017A base 0,2 to 0,8 0,7 3,5 to 4,5 0,4 to 1,0 1,2 to 1,8 0,10 0,25 0,25 Structure: With structural hardening Particular characteristics: Recommendations for welding and filling with EN AW-2017A Process Thickness range in mm State before welding PWHT Degree of weldabilityJoint coeffici
43、ent Comments and bibliographic references CDFW 10 T4 none 2 0,87 3 DW 10 T4 none 2 0,65 11 Diffusion temperature starting from 550 C BS EN 4632-002:2008EN 4632-002:2008 (E) 12 7.5 Designation: EN 573-2 : EN AW-2024 Old designation : AU4 G1 EN 2032-1 : AL-P2024- ISO : Al Cu 4 Mg 1 Other standards : T
44、ypical composition: See EN 573-3. Grade Al Si Fe Cu Mn Mg Cr Zn Ti 2024 base 0,50 0,50 3,8 to 4,9 0,30 to 0,9 1,2 to 1,8 0,10 0,25 0,15 Al Ti + Zr base 0,20 Only for extruded or forged products with agreement between supplier and customer Structure: With structural hardening Particular characteristi
45、cs: BS EN 4632-002:2008EN 4632-002:2008 (E) 13 Recommendations for welding and filling with EN AW-2024 Process Thickness range in mm State before welding PWHT Degree of weldabilityJoint coefficient Comments and bibliographic references TIG T3 none 4 C.A 1,6 T3 none 2 0,78 Filler metal 2219 55 5 30 T
46、4 T4 none T4 0,65 to 0,8 EBW 100 T351 none 2 to 3 0,82 Micro-cracks (liquation cracking) along the grain boundaries in the heat affected zone metal 79 SLW continuous 3 2 T351 T4 none 2 0,72 0,53 Filler metal 5356 68 Filler metal 5356 14 SLW Pulsed frequency 100 Hz to 500 Hz 2 T4 none 2 0,8 Filler me
47、tal 4043 14 SLW pulsed frequency 60 C and exposed in a corrosive environment. b24 h desensitization treatment at 250 C if parts must be exposed to a corrosive environment and if welding conditions (very high energies) or forming conditions (hot) could have made them sensitive to corrosion. cElectron
48、 beam welds are not sensitive to stress corrosion for magnesium contents of the order of 4,1 % Mg 76 BS EN 4632-002:2008EN 4632-002:2008 (E) 19 7.9 Designation: EN 573-2 : EN AW-5754 Old designation : AG3M EN 2032-1 : AL-P5754- ISO : Al Mg 3 Other standards : Typical composition: See EN 573-3. Grade Al Si Fe Cu Mg Mn Cr Zn Ti Mn + Cr 5754 base 0,40 0,40 0,10 2,6 to 3,6 0,50 0,30 0,20 0,15 0,10 to 0,6Structure: Particular characteristics: Recommendations for welding and filling with EN AW-5754 Process Thickness range in mm S