1、BSI Standards PublicationBS EN 754-2:2013Aluminium and aluminiumalloys Cold drawn rod/barand tubePart 2: Mechanical propertiesCopyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-BS E
2、N 754-2:2013 BRITISH STANDARDNational forewordThis British Standard is the UK implementation of EN 754-2:2013. Itsupersedes BS EN 754-2:2008 which is withdrawn.The UK participation in its preparation was entrusted to TechnicalCommittee NFE/35, Light metals and their alloys.A list of organizations re
3、presented on this committee can beobtained on request to its secretary.This publication does not purport to include all the necessaryprovisions of a contract. Users are responsible for its correctapplication. The British Standards Institution 2013. Published by BSI StandardsLimited 2013ISBN 978 0 58
4、0 82478 4ICS 77.150.10Compliance with a British Standard cannot confer immunity fromlegal obligations.This British Standard was published under the authority of theStandards Policy and Strategy Committee on 31 October 2013.Amendments issued since publicationDate Text affectedCopyright European Commi
5、ttee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-BS EN 754-2:2013EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 754-2 October 2013 ICS 77.150.10 Supersedes EN 754-2:2008English Version Aluminium an
6、d aluminium alloys - Cold drawn rod/bar and tube -Part 2: Mechanical properties Aluminium et alliages daluminium - Barres et tubes tirs -Partie 2: Caractristiques mcaniques Aluminium und Aluminiumlegierungen - Gezogene Stangen und Rohre - Teil 2: Mechanische Eigenschaften This European Standard was
7、approved by CEN on 22 August 2013. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such nati
8、onal standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own langu
9、age and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece,
10、 Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN
11、-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2013 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 754-2:2013: ECopyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo
12、 reproduction or networking permitted without license from IHS-,-,-BS EN 754-2:2013EN 754-2:2013 (E) 2 Contents Page Foreword 3 1 Scope 4 2 Normative references 4 3 Mechanical property limits .4 3.1 General 4 3.2 Elongation 4 3.3 Reference list of the tables of mechanical properties of the relevant
13、aluminium and aluminium alloys 5 3.4 Detailed tables of mechanical properties 6 Annex A (informative) List of tempers used in Tables 1 to 37 . 43 Bibliography . 45 Copyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permi
14、tted without license from IHS-,-,-BS EN 754-2:2013EN 754-2:2013 (E) 3 Foreword This document (EN 754-2:2013) has been prepared by Technical Committee CEN/TC 132 “Aluminium and aluminium alloys”, the secretariat of which is held by AFNOR. This European Standard shall be given the status of a national
15、 standard, either by publication of an identical text or by endorsement, at the latest by April 2014, and conflicting national standards shall be withdrawn at the latest by April 2014. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent right
16、s. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. CEN/TC 132 affirms its policy that if a patentee refuses to grant licenses on standardized products under reasonable and not discriminatory conditions, this product will be removed from the correspondi
17、ng document. This document supersedes EN 754-2:2008. CEN/TC 132 has decided to revise this European Standard as follows: addition of the alloys EN AW-6026 in a new Table 24 and EN AW-6064A in a new Table 31; EN 10002-1 was replaced by EN ISO 6892-1. EN 754 comprises the following parts under the gen
18、eral title “Aluminium and aluminium alloys Cold drawn rod/bar and tube“: Part 1: Technical conditions for inspection and delivery Part 2: Mechanical properties Part 3: Round bars, tolerances on dimensions and form Part 4: Square bars, tolerances on dimensions and form Part 5: Rectangular bars, toler
19、ances on dimensions and form Part 6: Hexagonal bars, tolerances on dimensions and form Part 7: Seamless tubes, tolerances on dimensions and form Part 8: Porthole tubes, tolerances on dimensions and form According to the CEN-CENELEC Internal Regulations, the national standards organisations of the fo
20、llowing countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands
21、, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. Copyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-BS EN 754-2:20
22、13EN 754-2:2013 (E) 4 1 Scope This European Standard specifies the mechanical property limits resulting from tensile testing applicable to aluminium and aluminium alloy cold drawn rod/bar and tube. Technical conditions for inspection and delivery, including product and testing requirements, are spec
23、ified in EN 754-1. Temper designations are defined in EN 515. The chemical composition limits for these materials are given in EN 573-3. 2 Normative references The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For dat
24、ed references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 754-1:2008, Aluminium and aluminium alloys Cold drawn rod/bar and tube Part 1: Technical conditions for inspection and delivery EN ISO 6892-1, M
25、etallic materials Tensile testing Part 1: Method of test at room temperature (ISO 6892-1) 3 Mechanical property limits 3.1 General The mechanical properties shall be in conformity with those specified in Table 1 to Table 37 or those agreed upon between supplier and purchaser and stated in the order
26、document. For all alloys the condition F (as fabricated) can be used, but without guaranteed mechanical properties. Table 1 to Table 37 contain limits of mechanical property values obtained by tensile testing according to EN ISO 6892-1 after sampling and test piece preparation according to EN 754-1.
27、 NOTE The mechanical properties refer to test pieces taken in the longitudinal direction. Mechanical properties of test pieces taken in other directions can differ from those for the longitudinal direction quoted in this standard. Brinell hardness values given in Table 1 to Table 37 expressed as HBW
28、 values are for information only. 3.2 Elongation If not otherwise agreed, the A value shall be used. The A value for elongation is the % elongation measured over a gauge length of 065,5 S (where S0is the initial cross-sectional area of the test-piece), and expressed in percent. For certain products
29、the supplier may choose (if not otherwise specified in the order documents) to use the elongation based on A50mm. Consequently, values for the A50mmare included in the following tables. The A50mm value is the elongation measured over a gauge length of 50 mm and expressed in percent. Test pieces and
30、their location in the specimen are given in EN 754-1. Copyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-BS EN 754-2:2013EN 754-2:2013 (E) 5 3.3 Reference list of the tables of mech
31、anical properties of the relevant aluminium and aluminium alloys Page Table 1 : Aluminium EN AW-1050A Al 99,5 6 Table 2 : Aluminium EN AW-1200 AI 99,0 7 Table 3 : Alloy EN AW-2007 Al Cu4PbMgMn 8 Table 4 : Alloy EN AW-2011 AI Cu6BiPb 9 Table 5 : Alloy EN AW-2011A AI Cu6BiPb(A) 10 Table 6 : Alloy EN A
32、W-2014 AI Cu4SiMg 11 Table 7 : Alloy EN AW-2014A AI Cu4SiMg(A) 12 Table 8 : Alloy EN AW-2017A AI Cu4MgSi(A) 13 Table 9 : Alloy EN AW-2024 AI Cu4Mg1 14 Table 10 : Alloy EN AW-2030 AI Cu4PbMg 15 Table 11 : Alloy EN AW-3003 AI Mn1Cu 16 Table 12 : Alloy EN AW-3103 AI Mn1 17 Table 13 : Alloy EN AW-5005 A
33、I Mg1(B) 18 Table 14 : Alloy EN AW-5005A AI Mg1(C) 19 Table 15 : Alloy EN AW-5019 AI Mg5 20 Table 16 : Alloy EN AW-5049 Al Mg2Mn0,8 21 Table 17 : Alloy EN AW-5251 AI Mg2Mn0,3 22 Table 18 : Alloy EN AW-5052 AI Mg2,5 23 Table 19 : Alloy EN AW-5154A AI Mg3,5(A) 24 Table 20 : Alloy EN AW-5754 AI Mg3 25
34、Table 21 : Alloy EN AW-5083 AI Mg4,5Mn0,7 26 Table 22 : Alloy EN AW-5086 AI Mg4 27 Table 23 : Alloy EN AW-6012 AI MgSiPb 28 Table 24 : Alloy EN AW-6026 AI MgSiBi 29 Table 25 : Alloy EN AW-6060 AI MgSi 30 Table 26 : Alloy EN AW-6061 AI Mg1SiCu 31 Table 27 : Alloy EN AW-6262 AI Mg1SiPb 32 Table 28 : A
35、lloy EN AW-6262A AI Mg1SiSn 33 Table 29 : Alloy EN AW-6063 AI Mg0,7Si 34 Table 30 : Alloy EN AW-6063A AI Mg0,7Si(A) 35 Table 31 : Alloy EN AW-6064A AI Mg1SiBi 36 Table 32 : Alloy EN AW-6065 AI Mg1Bi1Si 37 Table 33 : Alloy EN AW-6082 AI Si1MgMn 38 Table 34 : Alloy EN AW-7020 AI Zn4,5Mg1 39 Table 35 :
36、 Alloy EN AW-7022 AI Zn5Mg3Cu 40 Table 36 : Alloy EN AW-7049A AI Zn8MgCu 41 Table 37 : Alloy EN AW-7075 AI Zn5,5MgCu 42 Copyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-BS EN 754-
37、2:2013EN 754-2:2013 (E) 6 3.4 Detailed tables of mechanical properties Table 1 Aluminium EN AW-1050A Al 99,5 Drawn rod/bar Temper Dimensions mm RmMPa Rp0,2MPa A % min. A50 mm% min. HBW Typical value D aS bmin. max. min. max. O, H111 80 60 60 95 - - 25 22 20 H14 40 10 100 135 70 - 6 5 30 H16 15 5 120
38、 160 105 - 4 3 35 H18 10 3 145 - 125 - 3 3 43 Drawn tube Temper Wall thickness t mm RmMPa Rp0,2MPa A % min. A50 mm% min. HBW Typical value min. max. min. max. O, H111 20 60 95 - - 25 22 20 H14 10 100 135 70 - 6 5 30 H16 5 120 160 105 - 4 3 35 H18 3 145 - 125 - 3 3 43 aD = Diameter for round bar. bS
39、= Width across flats for square and hexagonal bar, thickness for rectangular bar. Copyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-BS EN 754-2:2013EN 754-2:2013 (E) 7 Table 2 Alum
40、inium EN AW-1200 Al 99,0 Drawn rod/bar Temper Dimensions mm RmMPa Rp0,2MPa A % min. A50 mm% min. HBW Typical value D aS bmin. max. min. max. O, H111 80 60 70 105 - - 20 16 23 H14 40 10 110 145 80 - 5 4 37 H16 15 5 135 170 115 - 3 3 45 H18 10 3 150 - 130 - 3 3 50 Drawn tube Temper Wall thickness t mm
41、 RmMPa Rp0,2MPa A % min. A50 mm% min. HBW Typical value min. max. min. max. O, H111 20 70 105 - - 20 16 23 H14 10 110 145 80 - 5 4 37 H16 5 135 170 115 - 3 3 45 H18 3 150 - 130 - 3 3 50 aD = Diameter for round bar. bS = Width across flats for square and hexagonal bar, thickness for rectangular bar.
42、Copyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-BS EN 754-2:2013EN 754-2:2013 (E) 8 Table 3 Alloy EN AW-2007 Al CuPbMgMn Drawn rod/bar Temper Dimensions mm RmMPa Rp0,2MPa A % min
43、. A50 mm% min. HBW Typical value D aS bmin. max. min. max. T3 c 30 30 D 80 30 30 S 80 370 340 - 240 220 - 7 6 5 - 95 95 T351 c 80 80 370 - 240 - 5 3 95 Drawn tube Temper Wall thickness t mm RmMPa Rp0,2MPa A % min. A50 mm% min. HBW Typical value min. max. min. max. T3 c 20 370 - 250 - 7 5 95 T3510 T3
44、511 c 20 370 - 240 - 5 3 95 aD = Diameter for round bar. bS = Width across flats for square and hexagonal bar, thickness for rectangular bar. cProperties may be obtained by press quenching. Copyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reprod
45、uction or networking permitted without license from IHS-,-,-BS EN 754-2:2013EN 754-2:2013 (E) 9 Table 4 Alloy EN AW-2011 Al Cu6BiPb Drawn rod/bar Temper Dimensions mm RmMPa Rp0,2MPa A % min. A50 mm% min. HBW Typical value D aS bmin. max. min. max. T3 40 40 D 50 50 D 80 40 40 S 50 50 S 80 320 300 280
46、 - - - 270 250 210 - - - 10 10 10 8 - - 90 90 90 T8 80 80 370 - 270 - 8 6 115 Drawn tube Temper Wall thickness t mm RmMPa Rp0,2MPa A % min. A50 mm% min. HBW Typical value min. max. min. max. T3 c 5 5 t 20 310 290 - - 260 240 - - 10 8 8 6 90 90 T8 20 370 - 275 - 8 6 115 aD = Diameter for round bar. b
47、S = Width across flats for square and hexagonal bar, thickness for rectangular bar. cProperties may be obtained by press quenching. Copyright European Committee for Standardization Provided by IHS under license with CENNot for ResaleNo reproduction or networking permitted without license from IHS-,-
48、,-BS EN 754-2:2013EN 754-2:2013 (E) 10 Table 5 Alloy EN AW-2011A Al Cu6BiPb(A) Drawn rod/bar Temper Dimensions mm RmMPa Rp0,2MPa A % min. A50 mm% min. HBW Typical value D aS bmin. max. min. max. T3 40 40 D 50 50 D 80 40 40 S 50 50 S 80 320 300 280 - - - 270 250 210 - - - 10 10 10 8 - - 90 90 90 T8 80 80 370 - 270 - 8 6 115 Drawn tu