1、BSI Standards PublicationFlexible insulating sleevingPart 3: Specifications for individual types of sleeving Sheet 284: Heat-shrinkable, sleevings, for oil barrier applicationsBS EN 60684-3-284:2014National forewordThis British Standard is the UK implementation of EN 60684-3-284:2014. Itis identical
2、 to IEC 60684-3-284:2014.The UK participation in its preparation was entrusted by TechnicalCommittee GEL/15, Solid electrical insulating materials, to SubcommitteeGEL/15/5, Flexible insulating sleeving for electrical purposes.A list of organizations represented on this committee can be obtained onre
3、quest to its secretary.This publication does not purport to include all the necessary provisions ofa contract. Users are responsible for its correct application. The British Standards Institution 2015Published by BSI Standards Limited 2015.ISBN 978 0 580 82387 9ICS 29.035.20Compliance with a British
4、 Standard cannot confer immunity fromlegal obligations.This British Standard was published under the authority of theStandards Policy and Strategy Committee on 31 January 2015.Amendments/corrigenda issued since publicationDate Text affectedBRITISH STANDARDBS EN 60684-3-284:2014EUROPEAN STANDARDNORME
5、 EUROPENNEEUROPISCHE NORMEN 60684-3-284 December 2014 ICS 29.035.20 English Version Flexible insulating sleeving - Part 3: Specifications for individual types of sleeving - Sheet 284: Heat-shrinkable, sleevings, for oil barrier applications (IEC 60684-3-284:2014) Gaines isolantes souples - Partie 3:
6、 Spcifications pourtypes particuliers de gaines - Feuille 284: Gaines thermortractables pour applications de barrire rsistant lhuile (CEI 60684-3-284:2014) Isolierschluche - Teil 3: Anforderungen fr einzelneSchlauchtypen - Blatt 284: Wrmeschrumpfschluche mitlsperrenden Eigenschaften (IEC 60684-3-284
7、:2014) This European Standard was approved by CENELEC on 2014-11-27. CENELEC members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliogra
8、phical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CENELEC member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the respons
9、ibility of a CENELEC member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions.CENELEC members are the national electrotechnical committees of Austria, Belgium, Bulgaria, Croatia, Cyprus, the Czech Republic, Denmark, Estonia, Finland,
10、 Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, the Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. European Committee for Electrote
11、chnical Standardization Comit Europen de Normalisation ElectrotechniqueEuropisches Komitee fr Elektrotechnische Normung CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2014 CENELEC All rights of exploitation in any form and by any means reserved worldwide for CENELEC Members. Ref. N
12、o. EN 60684-3-284:2014 E EN 60684-3-284:2014 - 2 - Foreword The text of document 15/693/CDV, future edition 1 of IEC 60684-3-284, prepared by IEC/TC 15 “Solid electrical insulating materials“ was submitted to the IEC-CENELEC parallel vote and approved by CENELEC as EN 60684-3-284:2014. The following
13、 dates are fixed: latest date by which the document has to be implemented at national level by publication of an identical national standard or by endorsement (dop) 2015-08-27 latest date by which the national standards conflicting with the document have to be withdrawn (dow) 2017-11-27 Attention is
14、 drawn to the possibility that some of the elements of this document may be the subject of patent rights. CENELEC and/or CEN shall not be held responsible for identifying any or all such patent rights. Endorsement notice The text of the International Standard IEC 60684-3-284:2014 was approved by CEN
15、ELEC as a European Standard without any modification. In the official version, for Bibliography, the following notes have to be added for the standards indicated: IEC 60684-3 (all sheets) NOTE Harmonized as EN 60684-3 (all sheets) (not modified). IEC 60757:1983 NOTE Harmonized as HD 457 S1:1985 (not
16、 modified). BS EN 60684-3-284:2014- 3 - EN 60684-3-284:2014 Annex ZA (normative) Normative references to international publications with their corresponding European publications The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its a
17、pplication. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. NOTE 1 When an International Publication has been modified by common modifications, indicated by (mod), the relevant EN/HD appli
18、es. NOTE 2 Up-to-date information on the latest versions of the European Standards listed in this annex is available here: www.cenelec.eu. Publication Year Title EN/HD Year IEC 60055-2 - Paper-insulated metal-sheathed cables for rated voltages up to 18/30 kV (with copper or aluminium conductors and
19、excluding gas-pressure and oil-filled cables - Part 2: General and construction requirements - - IEC 60296 - Fluids for electrotechnical applications - Unused mineral insulating oils for transformers and switchgear EN 60296 - IEC 60684-1 2003 Flexible insulating sleeving - Part 1: Definitions and ge
20、neral requirements EN 60684-1 2003 IEC 60684-2 2011 Flexible insulating sleeving - Part 2: Methods of test EN 60684-2 2011 BS EN 60684-3-284:2014 2 IEC 60684-3-284:2014 IEC 2014 CONTENTS INTRODUCTION . 5 1 Scope 6 2 Normative references 6 3 Designation . 7 4 Conditions of test 7 5 Requirements 7 6 S
21、leeving conformance . 7 (informative) Guide to the typical sizes and wall thicknesses . 11 Annex ABibliography 12 Table 1 Property requirements for Type A 7 Table 2 Property requirements for Type B 9 Table 3 Requirements for breakdown voltage, Types A and B 10 Table 4 Resistance to selected fluids .
22、 10 Table A.1 Dimensions Type A 11 Table A.2 Dimensions Type B 11 BS EN 60684-3-284:2014IEC 60684-3-284:2014 IEC 2014 5 INTRODUCTION This International Standard is one of a series which deals with flexible insulating sleeving for electrical purposes. The series consists of three parts: Part 1: Defin
23、itions and general requirements (IEC 60684-1) Part 2: Methods of test (IEC 60684-2) Part 3: Specifications for individual types of sleeving (IEC 60684-3) This standard gives one of the sheets comprising Part 3, as follows: Sheet 284: Heat-shrinkable sleevings, for oil barrier applications. BS EN 606
24、84-3-284:2014 6 IEC 60684-3-284:2014 IEC 2014 FLEXIBLE INSULATING SLEEVING Part 3: Specifications for individual types of sleeving Sheet 284: Heat-shrinkable sleevings, for oil barrier applications 1 Scope This part of IEC 60684 gives the requirements for heat-shrinkable sleevings for oil barrier, m
25、edium voltage cable jointing and termination applications, with nominal shrink ratios of up to 3:1. These sleevings have been found suitable for use up to temperatures of 80 C. Type A: polyolefin based. Type B: fluoropolymer based, enhanced oil resistance. These sleevings are normally supplied as tr
26、anslucent. Since these types of sleevings cover a significantly large range of sizes and wall thicknesses, Annex A, Tables A.1 and A.2, in this document, provide a guide to the range of sizes available. The actual size will be agreed between the purchaser and supplier. Materials which conform to thi
27、s standard meet established levels of performance. However, the selection of a material by a user for a specific application should be based on the actual requirements necessary for adequate performance in that application and not based on this standard alone. This sleeving is designed to be used in
28、 MV cable accessories and as such, electrical performance as defined as part of the assembly. Examples of this are described in HD 629 and IEC 60502 series. 2 Normative references The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its
29、application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. IEC 60055-2, Paper-insulated metal-sheathed cables for rated voltages up to 18/30 kV (with copper or aluminium conductors and e
30、xcluding gas-pressure and oil-filled cables) Part 2: General and construction requirements IEC 60296, Fluids for electrotechnical applications Unused mineral insulating oils for transformers and switchgear IEC 60684-1:2003, Flexible insulating sleeving Part 1: Definitions and general requirements IE
31、C 60684-2:2011, Flexible insulating sleeving Part 2: Methods of test BS EN 60684-3-284:2014IEC 60684-3-284:2014 IEC 2014 7 3 Designation The sleeving shall be identified by the following designation: Description IEC publication number IEC part number IEC sheet number Type Size (expanded and recovere
32、d internal diameter in mm) Sleeving IEC 60684 - 3 -284 -B - 51,0/19,0 NOTE This information is for package labelling only in accordance with IEC 60684-1. 4 Conditions of test Unless otherwise specified, the sleeving shall be shrunk in a forced air circulation oven for (10 1) min at 175 C 3 K for Typ
33、e A, and at 200 C 3 K for Type B, prior to testing. 5 Requirements In addition to the general requirements given in IEC 60684-1, the sleeving shall comply with the requirements of Tables 1, 2, 3, and 4 where applicable. 6 Sleeving conformance Conformance to the requirements of this standard shall no
34、rmally be based on the results from a typical size. Recovered ID 15 mm to 25 mm Table 1 Property requirements for Type A Property IEC 60684-2: 2011 Clause or Subclause Units Max. or Min. Requirements Remarks Dimensions Internal diameter Wall thickness Concentricity expanded recovered 3 3.1.2 3.3.2 3
35、.3.3 mm mm % Min. Min. To be agreed between purchaser and supplier 50 85 Longitudinal change 9 % Max. 10 + 5 Heat expanded sleeving at 175 C 5 K for (10 1 ) min Bending at low temperature 14 No cracking shall be visible Condition at 20 C 3 K For strips, the mandrel shall be no more than10 times the
36、wall thickness. Full section sleeving is tested unfilled and the mandrel shall be no more than 10 times the outer diameter. BS EN 60684-3-284:2014 8 IEC 60684-3-284:2014 IEC 2014 Property IEC 60684-2: 2011 Clause or Subclause Units Max. or Min. Requirements Remarks Heat shock Tensile strength Elonga
37、tion at break 6 19.1 and 19.2 19.1 and 19.2 MPa % Min. Min. 8 200 Heat at 200 C 5 K Dimensional stability on storage 16 The dimensions shall remain as agreed See Clause 1, (Scope) Tensile strength Elongation at break 19.1 and 19.2 19.1 and 19.2 MPa % Min. Min. 10 250 Use a jaw separation of 100 mm/m
38、in. Below 6,5 mm diameter test as sleeving, at 6,5 mm and above test as dumb-bells. Secant modulus at 2 % elongation 19.5 MPa Min. Max. 50 175 Breakdown voltage 21 kV Min. See Table 3 Volume Resistivity at room temperature 23 23.5.2 .m Min. 1012 Resistance to selected fluids Tensile strength Elongat
39、ion at break Change in mass 36 19.1 and 19.2 19.1 and 19.2 MPa % % Min. Min. Max. 7 200 10 Use the fluids and test temperatures specified in Table 4. Immersion time 24 1 h Test after recovery period of 1 h 15 min. Heat ageing Tensile strength Elongation at break 39 19.1 and 19.2 19.1 and 19.2 MPa %
40、Min. Min. 10 150 Heat at 150 C 3 K. Long term heat ageing (3 000 h) Elongation at break 50 19.2 % Min. 125 The ageing temperature shall be 135 C 3 K. BS EN 60684-3-284:2014IEC 60684-3-284:2014 IEC 2014 9 Table 2 Property requirements for Type B Property IEC 60684-2: 2011 Clause or Subclause Units Ma
41、x. or Min. Requirements Remarks Dimensions Internal diameter Wall thickness Concentricity Expanded Recovered 3 3.1.2 3.3.2 3.3.3 mm mm % Min. Min. To be agreed between purchaser and supplier. 60 85 Longitudinal change 9 % Max. 10 + 5 Heat expanded sleeving at 200 C 5 K for (10 1) min Bending at low
42、temperature 14 No cracking shall be visible Test at 20 C 3 K. For strips, the mandrel shall be no more than 10 times the wall thickness. Full section sleeving is tested unfilled and the mandrel shall be no more than 10 times the outer diameter. Heat shock Tensile strength Elongation at Break 6 No dr
43、ipping, flowing or cracking. Heat at 275 C 5 K. Dimensional stability on storage 16 The dimensions shall remain as agreed. See Scope. Tensile strength Elongation at break 19.1 and 19.2 19.1 and 19.2 MPa % Min. Min. 24 200 Use a jaw separation of 100 mm/min. Below 6,5 mm diameter test as sleeving, at
44、 6,5 mm and above test as dumb-bells. Secant modulus at 2% elongation 19.5 MPa Min. 170 Breakdown voltage 21 kV Min. See Table 3. Volume Resistivity at room temperature 23 23.5.2 m Min. 109 Resistance to selected fluids Tensile strength Elongation at break Change in mass 36 19.1 and 19.2 19.1 and 19
45、.2 MPa % % Min. Min. Max. 24 200 10 Use the fluids and test temperatures specified in Table 3. Immersion time (24 1) h Test after recovery period of 1 h 15 min. Heat ageing Elongation at break 39 19.1 and 19.2 % Min. 100 Heat at 225 C 5 K. Long term heat ageing (3 000 h) Elongation at break 50 19.2
46、% Min. 100 The ageing temperature shall be 150 0C 2 K. BS EN 60684-3-284:2014 10 IEC 60684-3-284:2014 IEC 2014 Table 3 Requirements for breakdown voltage, Types A and B Expanded wall thickness Electric strength a(mm) Min. All dimensions Expanded ID All sizes Electric strength kV/mm 12 aMeasure the e
47、xpanded wall thickness and calculate the electric strength by dividing the breakdown voltage by this value. The breakdown voltage shall be determined by the method described in 21.4 of IEC 60684-2:2011. The central value shall comply with the minimum value in the above Table 3. The sleeving shall be
48、 tested in the expanded condition. The rate of application of the voltage shall be 500 V/s. Care should be taken on selection of sizes based on these values. Refer to the manufacturer for actual values on installed conditions. Table 4 Resistance to selected fluids Test fluid No. Fluids Type Standard
49、 or symbol Type A; Immersion temperature C 2 K Type B; Immersion temperature C 2 K 1 Insulating oil Mineral based IEC 60296 Transformer oil Not suitable 110 2 Cleaning fluid Solvent Isopropyl alcohol 23 23 3 Water De-ionized 85 85 4 Insulating oil Synthetic Poly-isobutylene Not suitable 110 5 M.I.N.D Mineral based IEC 60055-2 60 60 Other fluids and/or temperatures may be specified for customer