1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions 2011 06 28 Revised See summary or revisions, paragraph 5 K. Cosgrave 1995 09 29 Activated M.V. Swain Controlled document at www.MATS Copyright 2011, Ford Global Technologies, LLC Page 1 of 3 GREASE, SYNTHETIC ESTER, FUEL RESISTANT, NLGI 0 WSS
2、M1C253-A GREASE, SYNTHETIC ESTER, FUEL RESISTANT, NLGI 1-2 WSS-M1C253-A2 1. SCOPE The material defined by this specification is a grease consisting of synthetic ester, non-soap thickener and other additives to give the desired characteristics. 2. APPLICATION This specification was released original
3、ly for grease used to prevent corrosion in fuel filler cap locks. It is also suitable for corrosion protection in other lock mechanisms and where noise damping is required on interior and exterior systems. The material has good resistance to water, fuel and hydrocarbon solvent washout. Use of this m
4、aterial with polymers other than polyoxymethylene (acetal) or polyamide is not recommended. A: This specification was released originally for grease used to prevent corrosion in fuel filler cap locks. It is also suitable for corrosion protection in other lock mechanisms. The validated material is ma
5、rketed by Ford Customer Service Division in Europe as part of a Squeak & Rattle Repair Kit, Part No. 5U7J 000A94 AA. Operating temperature range -40 C to 200 C. A2: This specification was released originally for grease used to lubricated and prevent corrosion in window regulators, latches, catches a
6、nd hinges. It is also suitable for lubrication and corrosion protection in similar mechanisms. Operating temperature range -40 C to 200 C (-15 C to 200 C dynamic). 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys St
7、andard Requirements for Production Materials (WSS-M99P1111-A). 3.1 COLOR Translucent (Visual) 3.2 WORKED PENETRATION, tenths of a millimeter A 355 - 385 (ASTM D 217, DIN ISO 2137, 60 strokes, 25 C) A2 290 - 320 3.3 WATER RESISTANCE, WATER WASHOUT 1 max (ASTM D 1264, DIN 51807 T2, 80 C) 3.4 CORROSION
8、 PROTECTION 3.4.1 Emcor Corrosion 0 max (ASTM D 6138, DIN 51802, 168hrs) 3.4.2 Copper Corrosion (Copper Strip) 1a max (ASTM D130, DIN 51811, 24, 100 C) ENGINEERING MATERIAL SPECIFICATION WSS-M1C253-A/A2 Controlled document at www.MATS Copyright 2011, Ford Global Technologies, LLC Page 2 of 3 3.5 FLO
9、W PRESSURE 1400 mbar max (DIN 51805, -35 C) 3.6 OIL SEPARATION DURING STORAGE 2.5% max (ASTM D 1742, DIN 51817 18hr at 40 C) 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions conce
10、rning Engineering Material Specifications. Grease approved to this specification should have the following typical properties. 4.1 COMPOSITION A A2 4.1.1 Base Oil Synthetic Ester 96% 92% (According to formulation) 4.1.2 Gel Thickener 4% 7% (According to formulation) 4.2 BASE OIL PROPERTIES 4.2.1 Kin
11、ematic Viscosity (ASTM D 445, DIN 51562 T01) Viscosity at 100 C 120 150 mm2/s Viscosity at 40 C 1200 1600 mm2/s 4.2.2 Flash Point 272 C 281 C (ASTM D 92, DIN ISO 2592) 4.2.3 Pour Point -30 C -27 C (ASTM D 97, DIN ISO 3016) 4.3 PENETRATION, tenths of a millimeter (ASTM D 217, ISO 2137) 4.3.1 Worked P
12、enetration, 60 strokes 359 300 4.3.2 Prolonged Worked Penetration, 100,000 strokes 2% 5% 4.4 DROPPING POINT Infusible Infusible (ASTM D 2265, DIN ISO 2176) 4.5 FOUR BALL WELD LOAD 4000N 4200N (ASTM D 2596, DIN 51350) 4.6 INTERFACE COMPATIBITY 4.6.1 Chemical Attack to Painted Surfaces (FLTM BJ 126-01
13、) Note: Not tested for initial application of this grease. Grease must be tested for chemical attack to painted surfaces for applications that come in contact with paint surfaces, ex. E-coat and powder coat. ENGINEERING MATERIAL SPECIFICATION WSS-M1C253-A/A2 Controlled document at www.MATS Copyright
14、 2011, Ford Global Technologies, LLC Page 3 of 3 4.6.2 Resistance to Stress Cracking (FLTM BO 127-03) Note: Not tested for initial application of this grease. Grease must be tested for resistance to stress cracking when used for additional applications that come in contact with polymers such as PC,
15、ABS, PC+ABS, ASA or acrylic. 4.6.3 Elastomer Compatibility (ASTM D 4289, 70h, 100oC, DIN 53505, DIN 53504) Note: Not tested for initial application of this grease. Grease must be tested for elastomer compatibility when used on additional applications that come in contact with elastomers. Application
16、 specific elastomer should be used for testing instead of a reference elastomer. . 5. SUMMARY OF REVISIONS 2011 06 28 Reclassify NLGI consistency for A2. Include additional functions within Application. Lot certification tests moved to requirements, all other requirements moved to general information. Add information on interface compatibility which is a requirement of WSS-M13P12-A. Supplements A, B and C removed.