1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 05 22 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 2 FABRIC, FINO PATTERN, KNIT WSS-M1H1028-A 1. SCOPE The material defined by this specification is a FINO PATTERN, 3 bars
2、, 28 Gauge, TRICOT knit, napped finish, body cloth of good quality and uniform composition. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for 2006/2007 CD33X seat bolster. 3. REQUIREMENTS Material specification requirements are to be used for
3、initial qualification of materials. In addition, to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For
4、 Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3887) Wales 134 wales/10 cm Courses 252 courses/10 cm 3.2.2 Fabric Weight, range, g/m2 (FLTM BN 106-01) Laminated * Face w/no Backcoat 414 - 457 316 - 349 * 3 mm foam thickness ENGINEERING MA
5、TERIAL SPECIFICATIONWSS-M1H1028-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 100% Polyester 3.4 YARN CONSTRUCTION (ASTM D 1244) Face 7.8 tex( natural polyester) Middle 7.8 tex (natural polyester) Back 7.8 tex (natural polyester) 3.5 METHOD OF DYEING Piece Dye 3.6 FINISHING OPERATIONS Wash, preset, dye, dry, nap, heat set, shear, inspect