1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 0 2012 09 13 Released R.Kyle, EU Controlled document at www.MATS Copyright 2012, Ford Global Technologies, LLC Page 1 of 2 FABRIC, LIVEWIRE, AAT (THAILAND), WOVEN JACQUARD, WSS-M1H1076-A1 UNLAMINATED FABRIC, LIVEWIRE, SOUTH AFRICA, WOVEN
2、 JACQUARD, WSS-M1H1076-A2 UNLAMINATED FABRIC, LIVEWIRE, ARGENTINA, WOVEN JACQUARD, WSS-M1H1076-A3 UNLAMINATED 1. SCOPE The material defined by this specification is a polyester woven jacquard face fabric. 2. APPLICATION This specification was released originally for material used as an interior trim
3、 insert fabric for use in the T6 program. Fabric was developed as a Tri-Laminate using local content and the suffix denotes the location. A1 is for AAT (Thailand) A2 is for South Africa A3 is for Argentina 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requi
4、rements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 10% (ASTM D3775) A1 (
5、AAT) A2 (South Africa) A3 (Argentina) Warp 500 ends/10 cm 320 ends/10 cm 370 ends/10 cm Weft 196 picks/10 cm 195 picks/10 cm 130 picks/10 cm 3.2.2 Fabric Weight, +/- 10% (FLTM BN 106-01) A1 (AAT) A2 (South Africa) A3 (Argentina) Face Fabric 450 g/m2 510 g/m2 700 g/m2 Back coat 60 g/m2 100 g/m2 50 g/
6、m2 Total Weight 510 g/m2 610 g/m2 750 g/m2 ENGINEERING MATERIAL SPECIFICATION WSS-M1H1076-A1 WSS-M1H1076-A2 WSS-M1H1076-A3 Copyright 2012, Ford Global Technologies, LLC Page 2 of 2 3.3 COMPOSITION (ASTM D629) Fabric 100% polyester 3.4 YARN CONSTRUCTION (ASTM D1244) A1 (AAT) A2 (South Africa) A3 (Arg
7、entina) Warp 110dtex, f48/2 167dtex, f48/2 167dtex, f34/3 168dtex, f48/3 Weft 1650dtex 4400dtex, f768 6000dtex, f1152 84dtex, f36/2 167dtex, f48/2 500dtex, f132/2 3.5 METHOD OF DYEING Yarn dyed or as approved by Materials Engineering 3.6 FINISHED OPERATIONS Washing Drying Back coating Or as approved
8、 by Materials Engineering 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. 4.1 Purchase departments will ensure that the material d
9、efined in this specification and shipped to any one assembly plant will be produced by one supplier only. 4.2 Global Strategy is to use Tri-Laminate construction in all regions. 4.3 If yarn is locally sourced it must meet the above fabric construction, composition and yarn construction requirements. The fabric must also meet the requirements of WSS-M8P18-A1/A2/A3/A4.