1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions 2016 05 12 N Status No replacement named D. Murtonen. NA 2008 01 09 Activated M. Dumitrescu Copyright 2016, Ford Global Technologies, LLC Page 1 of 2 FABRIC, VOLTA PATTERN, FLAT WOVEN 25% MINIMUM WSS-M1H1132-A POST INDUSTRIAL CONTENT NOT TO B
2、E USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a VOLTA pattern, flat woven bodycloth of good quality and uniform composition. The fabric is backcoated. 2. APPLICATION This specification was released originally for material used as a seat fabric, bolster application for
3、2010 CD338 Ford SEL 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirements of: WSS-M8P18-A1/A4. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Ma
4、terials (WSS-M99P1111-A) 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3775) Warp 287 ends/10 cm Fill 190 picks/10 cm 3.2.2 Fabric Weight, +/- 5% tolerance (FLTM BN 106-01) Face Fabric w/backcoat 330 g/m2 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4.
5、Fabric 100% Polyester Backcoating Acrylic ENGINEERING MATERIAL SPECIFICATION WSS-M1H1132-A Copyright 2016, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 16.7 tex f48 (false twist sol dye polyester) x 3 Fill 16.7 tex f48 (false twist 100% PI polyester) x 3 16.7 tex f48 (false twist polyester) x 3 3.5 METHOD OF DYEING Solution dye/yarn package dye 3.6 FINISHING OPERATIONS Woven, heat set, backcoated