1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions 2015 10 26 N Status No future usage D. Murtonen, NA 2008 03 19 Activated M. Dumitrescu Copyright 2015 Ford Global Technologies, LLC Page 1 of 2 FABRIC, BLADE PATTERN, FLAT CIRCULAR KNIT TRILAMINATED WSS-M1H1136-A NOT TO BE USED FOR NEW DESIGN
2、 1. SCOPE The material defined by this specification is a BLADE pattern, flat CIRCULAR KNIT bodycloth of good quality and uniform composition. The fabric is approved as a trilaminated fabric with foam and knitted scrim. 2. APPLICATION This specification was released originally for material used as a
3、 bolster of seat fabric for the 2009 P415 vehicle. 3. REQUIREMENTS Material specification requirements are to be used for initial qualification of materials. In addition to the requirements listed herein, the fabric shall meet all requirements of: WSS-M8P18-A1/A4. 3.1 STANDARD REQUIREMENTS FOR PRODU
4、CTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3887) Wales 110/10 cm Courses 154/10 cm 3.2.2 Fabric Weight, +/- 5% tolerance (FLTM
5、 BN 106-01) Face Fabric 326 g/m2 Knitted Nylon Scrim 40 g/m2 Laminated to 3 mm foam and scrim 366 g/m2 ENGINEERING MATERIAL SPECIFICATION WSS-M1H1136-A Copyright 2015 Ford Global Technologies, LLC Page 2 of 2 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4. Fabric 100% Polyester Knitted Scrim 100% Nylon Scrim 3.4 YARN CONSTRUCTION (ASTM D 1244) Face 16.7 tex f34 (natural polyester) x 2 Back 16.7 tex f36 (natural polyester) x 1 3.5 METHOD OF DYEING Piece dyed 3.6 FINISHING OPERATIONS Knit, Setmake, Dye, Heatset, Inspect