1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 0 2012 08 27 Released M. Montgomery, FOE Controlled document at www.MATS Copyright 2012, Ford Global Technologies, LLC Page 1 of 2 FABRIC, CHICANE PATTERN, DOBBY WOVEN WSS-M1H1151-A1 UNLAMINATED 1. SCOPE The material defined is a dobby w
2、oven polyester face fabric embossed. Laminated and finished with Textrim (HF-welded) 2. APPLICATION This specification was released originally for material used as an interior trim fabric for 2013.5 MY seat insert. The fabric was originally approved as trilaminated with foam and backing fabric/scrim
3、. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1.1 WSS-M1H1151-A1. This specification is based on virgin materials. 3.1.2 In addition to the req
4、uirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 10 % tolerance (ASTM D3775) warp 218 / 10 cm weft 176/ 10 cm 3.2.2 Fabric Weight, +/- 10 % tolerance 340 g/m2 (FLTM BN 106-01) 3.3 COMPOSITION (ASTM
5、 D629) Fabric 100% polyester 3.4 YARN CONSTRUCTION* (ASTM D1244) Warp 830dtexf192(polyester,semi-dull,air texturized, round section) Weft 830dtex f192(polyester, semi-dull, air texturized, round section) 550dtex f108(polyester, fully oriented, trilobal,bright) ENGINEERING MATERIAL SPECIFICATION WSS-
6、M1H1151-A1 Copyright 2012, Ford Global Technologies, LLC Page 2 of 2 3.5 METHOD OF DYEING Solution dyed or as approved by Materials Engineering, 3.6 FINISHED OPERATIONS Washing, drying, framing or as approved by Materials Engineering. 3.7 SPECIFIC OPERATIONS HF-welding after lamination 4. GENERAL IN
7、FORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. 4.1 Purchase departments will ensure that the material defined in this specification and shippe
8、d to any one assembly plant will be produced by one supplier only. 4.2 If yarn is locally sourced it must meet the above fabric construction, composition and yarn construction. The fabric must also meet the requirements of WSS-M8P18-A1/A2/A3/A4. 4.3 Global strategy for this fabric is to use tri-laminate/foam & scrim construction in all regions