1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 0 2014 11 18 Released M. Montgomery, EU Controlled document at www.MATS Copyright 2014, Ford Global Technologies, LLC Page 1 of 2 FABRIC, CAVITY EMBOSSED, WSS-M1H1184-A1 LAMINATED 1. SCOPE The material defined is a woven polyester face f
2、abric with embossed pattern added after lamination. 2. APPLICATION This specification is for material used as an interior trim fabric for 2015 MY seat insert and bolster. The fabric is approved as trilaminated with foam and backing fabric/scrim. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTI
3、ON MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). In addition to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.2 FABRIC CONSTRUCTION 3.2.1
4、 Fabric Count, -10 /+ 10 % tolerance (ASTM D3775) Warp 905 / 10 cm Weft 283/ 10 cm 3.2.2 Fabric Weight, -10 + 10 % tolerance (FLTM BN 106-01) Face fabric 320 g/m2 Backcoat 55 g/m2 Total Weight 375 g/m2 3.3 COMPOSITION (ASTM D629) Fabric 100% polyester Backcoating Acylic Backing fabric/scrim 100% pol
5、yester, Circular knit ENGINEERING MATERIAL SPECIFICATION WSS-M1H1184-A1 Copyright 2014, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D1244) Warp 167 Dtex (polyester, false twist texturized) Weft 167 Dtex x2, (polyester, false twist texturized 3.5 METHOD OF DYEING Solution dy
6、ed or as approved by Materials Engineering, 3.6 FINISHED OPERATIONS Wash, dye, coating, drying, brushing (optional) 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Eng
7、ineering Material Specifications. 4.1 Purchase departments will ensure that the material defined in this specification and shipped to any one assembly plant will be produced by one supplier only. 4.2 If yarn is locally sourced it must meet the above fabric construction, composition and yarn construction. The fabric must also meet the requirements of WSS-M8P18-A1/A2/A3/A4. 4.3 Global strategy for this fabric is to use tri-laminate/foam & scrim construction in all regions