1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions Rev. 0 2009 01 07 Activated M. Dumitrescu, FNA Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 1 of 2 FABRIC, GRIDLOCK PATTERN, FLAT WOVEN WSS-M1H1200-A 25% MINIMUM PIR CONTENT 1. SCOPE The material defined b
2、y this specification is a GRIDLOCK pattern, Dobby, flat woven bodycloth of good quality and uniform composition. The fabric has min 25% PIR (Post Industrial Recycled) yarn content and it is backcoated. 2. APPLICATION This specification was released originally for material used as a seat fabric, inse
3、rt application for 2011 P473 F 250/350/450. 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirements of: WSS-M8P18-A1/A4. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requir
4、ements for Production Materials (WSS-M99P1111-A) 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3775) Warp 330 ends/10 cm Fill 135 picks/10 cm 3.2.2 Fabric Weight, +/- 5% tolerance (FLTM BN 106-01) Face Fabric w/backcoat 410 g/m2 Backcoat 35 g/m23.3 COMPOSITION (ASTM D 629) Tol
5、erance as specified in WSS-M8P18-A1/A4. Fabric 85% Polyester, 15% Nylon Backcoating Acrylic ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1200-A Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 65 tex f48 (air texture 100%
6、polyester) x 1 Fill 172 tex (flock 100% PA 6.6) x 1 85 tex f192 (air texture 100% PIR polyester yarn) x 1 3.5 METHOD OF DYEING Solution dye/yarn-package dye 3.6 FINISHING OPERATIONS Warping, weaving, backcoated, heat set 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase department will ensure that the material defined in this specification and shipped to any one assembly plant will be produced by one supplier only.