1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2009 01 06 N-STATUS No Replacement B. Haggart, FNA 2002 07 25 Revised Updated & Renumbered 1996 06 13 Activated B. Chen L. Graham Printed copies are uncontrolled Page 1 of 2 Copyright 2009, Ford Global Techn
2、ologies, Inc. FABRIC, FARGO PATTERN, WOVEN WSS-M1H460-B NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a Fargo pattern woven bodycloth of good quality and uniform composition. 2. APPLICATION This specification was released originally for material used as an inte
3、rior trim fabric for Light Truck. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5 % tolerance (ASTM
4、 D 3775) Warp 11.0 ends/cm Fill 11.0 picks/cm 3.2.2 Fabric Weight, range 450 - 530 g/m2(FLTM BN 106-01) 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSB-M8P1-I/ Fabric 100 % polyester Face Finish Wax emulsion Backcoating Vinylidene chloride butadiene ENGINEERING MATERIAL SPECIFICATION WSS-
5、M1H460-B Page 2 of 2 Copyright 2009, Ford Global Technologies, Inc. 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 83.4 tex Z 335 tpm (polyester, 67% disperse, 33 % basic, 3.3 d tex, 51 mm staple) x 2 S 240 tpm Fill (V) B 183.7 tex f 50/68 t 0 (polyester, T26/T55A) (W) 83.4 tex Z 335 tpm (polyester, 67% disperse, 33 % basic, 3.3 d tex, 51 mm staple) x 2 S 240 tpm (X) B 183.7 tex f 34/50 t 0 (polyester T92/T26) 3.5 METHOD OF DYEING Piece dyed (Jet) 3.6 FINISHING OPERATIONS Dry/treat, nap, shear, backcoat 3.7 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute