1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2009 01 06 N-STATUS No Replacement B. Haggart, FNA 2003 03 18 Revised Para 3.0 inserted ; Para 3.1, 3.2, 3.3, 3.9, 4 deleted 1998 10 05 Activated L. Daniv-ZarewychPrinted copies are uncontrolled Page 1 of 2
2、Copyright 2009, Ford Global Technologies, Inc. FABRIC, TRIAD GOLD PATTERN, WOVEN VELOUR WSS-M1H701-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a dobby pattern, woven velour bodycloth of good quality and uniform composition. 2. APPLICATION This specification
3、 was released originally for material used as an interior trim fabric for Ranger XLT. 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirements of: WSS-M8P18-A1/A4. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers mu
4、st conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 FABRIC CONSTRUCTION 3.4.1 Fabric Count, +/- 5 % tolerance (ASTM D 3775) Wales 413 wales/10 cm Courses 141 courses/10 cm 3.4.2 Fabric Weight, range 481 - 533 g/m2(FLTM BN 106-01) 3.5 COMPOSITION (ASTM D 62
5、9) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 100 % Polyester Face Finish None Backoating Acrylic ENGINEERING MATERIAL SPECIFICATION WSS-M1H701-A Page 2 of 2 Copyright 2009, Ford Global Technologies, Inc. 3.6 YARN CONSTRUCTION (ASTM D 1244) Warp Pile 55.6 tex f 200 (dul, polyester)Back 16.7 tex f34 (semi-dul,polyester) Fill 11.1 tex f 34 (semi-dul,polyester) 3.7 METHOD OF DYEING Yarn (disperse) 3.8 FINISHING OPERATIONS Shear, Tiger (brush), Shear