1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 01 24 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 2 FABRIC, PREFERRED SUEDE II, NON-WOVEN WSS-M1H770-B 1. SCOPE The material defined by this specification is a needle pun
2、ched non-woven fabric made from 0.333 tex polyester microfiber, impregnated with micro-porous polyurethane and backcoated. The fabric could be used plain, perforated, or embossed. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for S197 2007 Cal
3、ifornia Special. 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materi
4、als (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Weight, range (FLTM BN 106-01) Face w/Backcoat 375 425 g/m2Laminated with 3 mm foam 469 519 g/m2Backcoat 34 g/m23.2.2 Composition (ASTM D 629) Fabric 70% Polyester 30% Polyurethane Backcoat Acrylic 3.2.3 Fiber Construction (ASTM D 1244) 0.33
5、3 tex Polyester Microfiber impregnated with Micro-Porous Polyurethane ENGINEERING MATERIAL SPECIFICATIONWSS-M1H770-B Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 3.3 METHOD OF DYEING Piece dye, closed jet 3.4 FINISHING OPERATIONS Dry, heatset, backcoat inspect