1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2008 02 06 N-STATUS No replacement named M. Dumitrescu 2002 07 31 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 1 of 2 FABRIC, ZACH PATTERN, PILE WARP KNIT WSS-M1H895-A NOT TO BE USE
2、D FOR NEW DESIGN 1. SCOPE The material defined by this specification is a ZACH PATTERN, 56 Gauge, pile Raschel warp knitted body cloth of good quality and uniform composition. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for Taurus/Sable 2004
3、 seat insert. 3. REQUIREMENTS In addition, to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Produ
4、ction Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3887) Wales 118 wales/10 cm Courses 252 courses/10 cm 3.2.2 Fabric Weight, range, g/m2(FLTM BN 106-01) Face w/ Backcoat 375 - 395 ENGINEERING MATERIAL SPECIFICATIONWSS-M1H895-A Printed copies are u
5、ncontrolled Copyright 2008, Ford Global Technologies, LLC Page 2 of 2 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 100% Polyester Backcoat Acrylic 3.4 YARN CONSTRUCTION (ASTM D 1244) Face 7.8 tex f72 (semi-dull Polyester) Middle 7.8 tex f36 (full-dull Polyester) Back 16.7 tex f36 (semi-dull Polyester) 3.5 METHOD OF DYEING Disperse Piece Dye 3.6 FINISHING OPERATIONS Shear, Heat Set, Dye, Tenter Dry, Range, Millitex, Inspect