1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2003 10 09 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 1 of 2 FABRIC, HERRINGBONE PATTERN, WOVEN WSS-M1H935-A 1. SCOPE The material defined by this specification is a Herringbone
2、pattern, flat Dobby woven body cloth of good quality and uniform composition. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for 2005 U364 seat insert. The fabric is back-coated and laminated. 3. REQUIREMENTS In addition, to the requirements li
3、sted herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4 as applicable. The fabric must be backcoated. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A).
4、3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3775) Warp 486 ends/10 cm Fill 228 picks/10 cm 3.2.2 Fabric Weight, range, g/m2(FLTM BN 106-01) Laminated * Face with Backcoat 382 - 423 254 - 281 * At 3 mm thickness 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18
5、-A1/A4 Fabric 100% Polyester Backcoating EVA ENGINEERING MATERIAL SPECIFICATIONWSS-M1H935-APrinted copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 16.7 tex f36 (semi-dull polyester, false twist textured yarn) Fill 25 tex f50
6、 (semi-dull polyester, false twist textured yarn) 3.5 METHOD OF DYEING Piece dye - Solution dye 3.6 FINISHING OPERATIONS set make, wash, jet scour, dye, dry, scotch, dry, coat 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase departments will ensure that material defined in this specification and shipped to any one assembly plant will be produced by one supplier only.