1、Designation: A568/A568M 13a1Standard Specification forSteel, Sheet, Carbon, Structural, and High-Strength, Low-Alloy, Hot-Rolled and Cold-Rolled, General Requirementsfor1This standard is issued under the fixed designation A568/A568M; the number immediately following the designation indicates the yea
2、rof original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Departme
3、nt of Defense.1NOTETable X2.3 was editorially updated in October 2013.1. Scope*1.1 This specification covers the general requirements forsteel sheet in coils and cut lengths. It applies to the followingspecifications that describe carbon steel, structural steel, andhigh-strength, low-alloy steel (HS
4、LA) furnished as hot-rolledsheet and cold-rolled sheet: Specifications A414/A414M,A424, A606, A659/A659M, A794, A1008/A1008M, A1011/A1011M, and A1039/A1039M.1.2 This specification is not applicable to hot-rolled heavy-thickness carbon sheet coils (Specification A635/A635M).1.3 In case of any conflic
5、t in requirements, the requirementsof the individual material specification shall prevail over thoseof this general specification.1.4 For the purposes of determining conformance with thisand the appropriate product specification referenced in 1.1,values shall be rounded to the nearest unit in the ri
6、ght handplace of figures used in expressing the limiting values inaccordance with the rounding method of Practice E29.1.5 AnnexA1 lists permissible variations in dimensions andmass (see Note 1) in SI metric units. The values listed are notexact conversions of the values listed in the inch-pound tabl
7、es,but instead are rounded or rationalized values. Conformance toAnnex A1 is mandatory when the “M” specification is used.NOTE 1The term weight is used when inch-pound units are thestandard. However, under SI the preferred term is mass.1.6 The values stated in either SI units or inch-pound unitsare
8、to be regarded separately as standard. The values stated ineach system may not be exact equivalents; therefore, eachsystem shall be used independently of the other. Combiningvalues from the two systems may result in non-conformancewith the standard.1.7 This specification and the applicable material
9、specifica-tions are expressed in both inch-pound units and SI units.However, unless the order specifies the applicable “M” speci-fication designation (SI units), the material shall be furnishedto inch-pound units.2. Referenced Documents2.1 ASTM Standards:2A370 Test Methods and Definitions for Mechan
10、ical Testingof Steel ProductsA414/A414M Specification for Steel, Sheet, Carbon, andHigh-Strength, Low-Alloy for Pressure VesselsA424 Specification for Steel, Sheet, for Porcelain EnamelingA606 Specification for Steel, Sheet and Strip, High-Strength, Low-Alloy, Hot-Rolled and Cold-Rolled, withImprove
11、d Atmospheric Corrosion ResistanceA635/A635M Specification for Steel, Sheet and Strip,Heavy-Thickness Coils, Hot-Rolled, Alloy, Carbon,Structural, High-Strength Low-Alloy, and High-StrengthLow-Alloy with Improved Formability, General Require-ments forA659/A659M Specification for Commercial Steel (CS
12、),Sheet and Strip, Carbon (0.16 Maximum to 0.25 Maxi-mum Percent), Hot-RolledA700 Practices for Packaging, Marking, and Loading Meth-ods for Steel Products for ShipmentA751 Test Methods, Practices, and Terminology for Chemi-cal Analysis of Steel ProductsA794 Specification for Commercial Steel (CS),
13、Sheet, Car-bon (0.16 % Maximum to 0.25 % Maximum), Cold-Rolled1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.19 on Steel Sheet and Strip.Current edition approved Oct. 1, 2013. Publish
14、ed October 2013. Originallyapproved in 1966. Last previous edition approved in 2013 as A568/A568M 13.DOI: 10.1520/A0568_A0568M-13a1.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume inform
15、ation, refer to the standards Document Summary page onthe ASTM website.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1A941 Terminology Relating to Steel, Stainless Stee
16、l, RelatedAlloys, and FerroalloysA1008/A1008M Specification for Steel, Sheet, Cold-Rolled,Carbon, Structural, High-Strength Low-Alloy, High-Strength Low-Alloy with Improved Formability, SolutionHardened, and Bake HardenableA1011/A1011M Specification for Steel, Sheet and Strip,Hot-Rolled, Carbon, Str
17、uctural, High-Strength Low-Alloy, High-Strength Low-Alloy with ImprovedFormability, and Ultra-High StrengthA1030/A1030M Practice for Measuring Flatness Character-istics of Steel Sheet ProductsA1039/A1039M Specification for Steel, Sheet, Hot Rolled,Carbon, Commercial, Structural, and High-Strength Lo
18、w-Alloy, Produced by Twin-Roll Casting ProcessE11 Specification for Woven Wire Test Sieve Cloth and TestSievesE29 Practice for Using Significant Digits in Test Data toDetermine Conformance with SpecificationsE59 Practice for Sampling Steel and Iron for Determinationof Chemical Composition (Withdrawn
19、 1996)3E290 Test Methods for Bend Testing of Material for Ductil-ity2.2 Military Standards:4MIL-STD-129 Marking for Shipment and Storage2.3 Federal Standards:4Fed. Std. No. 123 Marking for Shipments (Civil Agencies)3. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 Steel Types:3.
20、1.2 carbon steeldesignation for steel when no minimumcontent is specified or required for aluminum, chromium,cobalt, columbium, molybdenum, nickel, titanium, tungsten,vanadium, zirconium, or any element added to obtain a desiredalloying effect; when the specified minimum for copper doesnot exceed 0.
21、40 %; or when the maximum content specified forany of the following elements does not exceed the percentagesnoted: manganese 1.65, silicon 0.60, or copper 0.60.3.1.2.1 DiscussionIn all carbon steels small quantities ofcertain residual elements unavoidably retained from raw ma-terials are sometimes f
22、ound which are not specified or required,such as copper, nickel, molybdenum, chromium, etc. Theseelements are considered as incidental and are not normallydetermined or reported.3.1.3 high-strength, low-alloy steelspecific group of steelsin which higher strength, and in some cases additional resis-t
23、ance to atmospheric corrosion or improved formability, areobtained by moderate amounts of one or more alloyingelements.3.1.4 Product Types:3.1.5 hot-rolled sheetmanufactured by hot rolling slabs ina continuous mill to the required thickness and can be suppliedin coils or cut lengths as specified.(1)
24、 Hot-rolled carbon steel sheet is commonly classified bysize as follows:Coils and Cut LengthsWidth, in. Thickness, in.All WidthsA0.027 to 0.230, exclAHot-rolled sheet in coils and cut lengths less than 12 in. in width must have cutedges. Hot-rolled material with mill edges 12 in. and less in width i
25、s consideredhot-rolled strip.Coils and Cut LengthsWidth, mm Thickness, mmAll WidthsA0.7 to 6.0, exclAHot-rolled sheet in coils and cut lengths less than 300 mm. in width must havecut edges. Hot-rolled material with mill edges 300 mm and less in width isconsidered hot-rolled strip.(2) Hot-rolled high
26、-strength low-alloy steel sheet is com-monly classified by size as follows:Coils and Cut LengthsWidth, in. Thickness, in.All WidthsA0.031 to 0.230, exclAHot-rolled sheet in coils and cut lengths less than 12 in. in width must have cutedges. Hot-rolled material with mill edges 12 in. and less in widt
27、h is consideredhot-rolled strip.Coils and Cut LengthsWidth, in. Thickness, mmAll WidthsA0.8 to 6.0, exclAHot-rolled sheet in coils and cut lengths less than 300 mm in width must have cutedges. Hot-rolled material with mill edges 300 mm and less in width is consideredhot-rolled strip.NOTE 2The change
28、s in width limits with the publication of A568/A568M 06a result in a change in tensile testing direction for materialfrom 0.180 in. 4.5 mm to 0.230 in. exclusive 6.0 mm exclusive over 48in. 1200 mm wide. Material formerly tested in the transverse directionwill be tested in the longitudinal direction
29、. This is expected to result insome changes in reported properties. The purchaser is advised to discussthis change with the supplier.3.1.6 cold-rolled sheetmanufactured from hot-rolled des-caled coils by cold reducing to the desired thickness, generallyfollowed by annealing to recrystallize the grai
30、n structure. If thesheet is not annealed after cold reduction it is known as fullhard with a hardness of 84 HRB minimum and can be used forcertain applications where ductility and flatness are not re-quired.(1) Cold-rolled carbon sheet is commonly classified by sizeas follows:Width, in. Thickness, i
31、n.All WidthsA,BThrough 0.142Width, mm Thickness, mmAll WidthsA,BThrough 4.0ACold-rolled sheet coils and cut lengths, slit from wider coils with cut edge (only)and in thicknesses through 0.142 in. 4.0 mm carbon 0.25 % maximum by castanalysis.BWhen no special edge or finish (other than matte, commerci
32、al bright, or lusterfinish) or single strand rolling of widths, or both under 24 in. 600 mm is notspecified or required.(2) Cold-rolled high-strength low-alloy sheet is commonlyclassified by size as follows:3The last approved version of this historical standard is referenced onwww.astm.org.4Availabl
33、e from Standardization Documents Order Desk, DODSSP, Bldg. 4,Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098, http:/www.dodssp.daps.mil.A568/A568M 13a12Width, in. Thickness, in.Through 12A0.019 through 0.082Over 12B0.020 and overWidth, mm Thickness, mmTo 300, inclAOver 300B0.5 to 2.0, incl0
34、.5 and OverACold-rolled sheet coils and cut lengths, slit from wider coils with cut edge (only)and in thicknesses 0.019 in. 0.5 mm through 0.082 in. 2.0 mm carbon 0.25 %maximum by cast analysis.BWhen no special edge or finish (other than matte, commercial bright, or lusterfinish) or single strand ro
35、lling of widths, or both under 24 in. 600 mm is notspecified or required.3.1.6.1 DiscussionSteel products are available in variousthickness, width, and length combinations depending uponequipment and processing capabilities of various manufactur-ers and processors. Historic limitations of a product
36、based upondimensions (thickness, width, and length) do not take intoaccount current production and processing capabilities. Toqualify any product for a particular product specificationrequires all appropriate and necessary tests be performed andthat the results meet the limits prescribed in that pro
37、ductspecification. If the necessary tests required by a productspecification cannot be conducted, the product cannot bequalified to that specification. This general requirements speci-fication contains permitted variations for the commonly avail-able sizes. Permitted variations for other sizes are s
38、ubject toagreement between the customer and the manufacturer orprocessor, whichever is applicable.3.1.7 retests, nadditional test, or tests, made from theoriginal material when the original test did not meet theappropriate acceptance criteria required by a product specifi-cation and the failure was
39、mechanical in natures as described inSection 11.3.1.8 resample, nadditional test or tests made when thetest on the original sample did not meet the appropriateacceptance criteria required by the product specification, butpossibly requiring that the material in question have anappropriate amount disc
40、arded prior to securing the new sampleor samples.3.1.9 steel manufacturer, nthe organization that directlycontrols or is responsible for the melting and refining of steeland the conversion of that steel into semifinished steel productsknown as slabs either through continuous casting, conventionalor
41、compact methods, or ingot casting and subsequent conver-sion of the ingots to slabs, and for one or more additionaloperations such as testing, marking, loading for shipment, andcertification.3.1.10 coil processorthe organization that directly con-trols or is responsible for operations involved in pr
42、ocessing thecoil such as leveling, cutting to length, testing, inspection,blanking, slitting, pickling, cold rolling (cold reduction), heattreating, temper rolling, coating, packaging, marking, loadingfor shipment, and certification.3.1.10.1 DiscussionThe processing operations need not becontrolled
43、by the organization that hot rolls the slab into a coil.If only one organization controls or is responsible for (or both)the hot rolling and processing operations, that organization istermed the manufacturer. If more than one organization con-trols or is responsible for (or both) hot rolling and pro
44、cessingoperations, the organization that controls and is responsible forthe hot rolling is termed the hot roll manufacturer and theorganization or organizations controlling and responsible forthe processing operations is/are termed the processor or pro-cessors. Likewise, one organization may be the
45、manufacturerof the hot roll coil and another the manufacturer of the cold rollcoil. In such case, the organization responsible for the conver-sion of the hot roll coil to a cold roll coil and other processingoperations will also be termed the cold roll manufacturer andorganizations performing additi
46、onal processing operations tothe cold roll coil will be termed the coil processor or coilprocessors.3.1.11 hot roll manufacturer, nthe organization that di-rectly controls or is responsible for the conversion of steelslabs, by hot rolling into coils, and for one or more additionaloperations such as
47、leveling, cutting to length, testing,inspection, blanking, slitting, pickling, cold rolling, heattreating, coating, packaging, marking, loading for shipment,and certification.3.1.12 cold roll manufacturer, nthe organization that di-rectly controls or is responsible for the conversion of hot rollcoil
48、s into cold roll coils, and for one or more additionaloperations such as pickling, annealing, temper rolling, slitting,cutting to length, testing, inspection, blanking, coating,packaging, marking, loading for shipment, and certification.3.2 Refer to Terminology A941 for additional definitions ofterm
49、s used in this standard.4. Materials and Manufacture4.1 Unless otherwise specified, hot-rolled material shall befurnished hot-rolled, not annealed, not pickled.4.2 Coil breaks, stretcher strains, and fluting can occurduring the users processing of hot-rolled or hot-rolled pickledsheet. When any of these features are detrimental to theapplication, the manufacturer shall be notified at time ofordering in order to properly process the sheet.4.3 Cold-rolled carbon steel sheet is available as discussedin 10.2, 10.3, and in Table 1.4.4 Unless spec