1、Designation: A 625/A 625M 08Standard Specification forTin Mill Products, Black Plate, Single-Reduced1This standard is issued under the fixed designation A 625/A 625M; the number immediately following the designation indicates the yearof original adoption or, in the case of revision, the year of last
2、 revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This specification covers single-reduced
3、black plateproduced from low carbon, cold-reduced steel, furnished incoils and cut sizes, for use in the manufacture of containers,closures, signs, toys and other products, as well as for platingapplications.1.2 It may be supplied dry or oiled and with or withoutsurface treatment. This product is no
4、rmally supplied with atrimmed edge.1.3 This specification is applicable to orders in eitherinch-pound units (as A 625), which is supplied in thicknessesfrom 135-lb base weight (0.0149 in.) and lighter, or SI units (asA 625M), which is supplied in thicknesses from 0.378 mm andlighter.1.4 The values s
5、tated in either inch-pound or SI units are tobe regarded as standard. Within the text, the SI units are shownin brackets. The values stated in each system are not exactequivalents; therefore, each system must be used indepen-dently of the other. Combining values from the two systemsmay result in non
6、conformance with this specification.2. Referenced Documents2.1 ASTM Standards:2A 623 Specification for Tin Mill Products, General Require-mentsA 623M Specification for Tin Mill Products, General Re-quirements Metric3. Ordering Information3.1 Orders for product under this specification shall includet
7、he following information, as required and applicable, toadequately describe the desired materials.3.1.1 Name of product (single-reduced black plate).3.1.2 Surface appearance and finish (Section 4).3.1.2.1 Dry.3.1.2.2 Oiled (type of oil; mineral or suitable for lithograph-ing) (Section 5).3.1.2.3 Che
8、mically treated and oiled (see SpecificationA 623 or Specification A 623M).3.1.3 Thickness (see Specification A 623 or SpecificationA 623M).3.1.4 Width.3.1.5 Length, for cut sizes only.3.1.6 Rolling direction must be specified by underlining thesteel (rolling width) for cut sizes.3.1.7 Steel type (s
9、ee Specification A 623 or SpecificationA 623M).3.1.8 Mechanical designation requirements (see Specifica-tion A 623 or Specification A 623M).3.1.9 Intended application.3.1.10 Quantity, in base boxes SITAs (see Note 5).3.1.11 On coils, specify minimum of range or acceptableinside diameters. The standa
10、rd inside diameter is approxi-mately 16 in. if ordered to Specification A 625 410 mm ifordered to Specification A 625M. Coils should be specified toa maximum coil weight if ordered to SpecificationA 625 massif ordered to Specification A 625M or maximum outsidediameter, or both.3.1.12 Packaging.3.1.1
11、3 ASTM specification designation and year of issue.3.1.14 Special requirements, where applicable.NOTE 1Atypical ordering description is as follows: 1000 Base Boxes,Single-Reduced Black Plate, oiled, 80 lb base weight, 30 in. by coil, MR,T5CA for lithographed can bodies to ASTM A 625/A 625M - XX. 600
12、SITAs, Single-Reduced Black Plate, oiled, 0.25 mm, 810 mm by coil, MR,T5CA for lithographed can bodies to Specification A 625/A 625M.NOTE 2A typical ordering description for cut sizes is as follows: 500Base Boxes, Single Reduced Black Plate, oiled, 80 lb base weight MR, T-2BA, 7C, 3034 in. by 30716
13、in., for lithographed can bodies in accordancewith Specification A 625/A 625M - XX. 100 SITAS, Single ReducedBlack Plate, oiled, MR, T-2 BA, 7C, 0.28 mm thickness, 781 by 773 mm,for lithographed can bodies in accordance with Specification A 625M/A 625M - XX.NOTE 3The production of coils does not aff
14、ord the same opportunityfor inspection, grading, and sorting as does the production of cut sizes.Accordingly, appropriate processing and quality control procedures arerequired by the purchaser to obtain optimum utilization of the material.1This specification is under the jurisdiction of ASTM Committ
15、ee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.20 on Tin Mill Products.Current edition approved Oct. 1, 2008. Published October 2008. Originallyapproved in 1968. Last previous edition approved in 2003 as A 625/A 625M 03.2For referenced ASTM sta
16、ndards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken,
17、 PA 19428-2959, United States.Cut sizes are line-inspected visually and mechanically during production.Sheets having surface imperfections that will not interfere with theirutilizations are included.NOTE 4Single-reduced black plate is highly susceptible to rusting andmust be properly handled during
18、transit and storage.NOTE 5In inch-pound units single-reduced black plate is supplied onan area basis expressed in base boxes. In coils, the number of base boxesis computed from the measured length and the specified width. In cutlengths, the number of base boxes is computed from the specified lengtha
19、nd width dimensions and sheet count. For calculating mass, the densityof steel for tin mill products is 0.2836 lbf/in.3. In SI units single-reducedblack plate is supplied on an area basis computed in SITAs. In coils, thenumber of SITAs is computed from the specified length and the specifiedwidth. In
20、 cut lengths, the number of SITAs is computed from the specifiedlength and width dimensions and sheet count. For calculating mass, thedensity of steel for tin mill tests is 7850 kg/m2.4. Surface Appearance and Finish4.1 Surface AppearanceSingle-reduced black plate is cus-tomarily produced with groun
21、d roll and shot-blasted rollfinishes as follows:4.1.1 Ground-Roll Finishes:4.1.1.1 7AA lustrous smooth finish intended for electro-plating by the purchaser.4.1.1.2 7BAsmooth finish that may contain fine grit lines.This finish is specified for special applications.4.1.1.3 7CA smooth finish with grit
22、lines. The surfaceroughness will range from 10 to 25 in. Ra 0.254 to 0.635 mRa. This is the standard finish for tin mill products.4.1.2 Blasted and/or Otherwise Textured Roll Finishes:4.1.2.1 5AA shot-blasted finish (SBF) intended for litho-graphing.4.1.2.2 5CA shot-blasted finish (SBF) for general
23、appli-cations. The surface roughness will range from 30 to 60 in. Ra0.760 to 1.52 m Ra.5. Oiling5.1 Black plate is furnished oiled or dry. Unless indicated bythe purchaser, single-reduced black plate will be supplied dry.Any required oiling treatment will be negotiated between thepurchaser and the s
24、upplier.6. General Requirements for Delivery6.1 Product furnished under this specification shall conformto the applicable requirements of the current edition of Speci-fication A 623 or Specification A 623M unless otherwise pro-vided herein.ASTM International takes no position respecting the validity
25、 of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject
26、to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters
27、. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is
28、 copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).A 625/A 625M 082