1、Designation: B505/B505M 10Standard Specification forCopper Alloy Continuous Castings1This standard is issued under the fixed designation B505/B505M; the number immediately following the designation indicates the yearof original adoption or, in the case of revision, the year of last revision. A numbe
2、r in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope*1.1 This specification establishes requirements for continu-ou
3、sly cast rod, bar, tube, and shapes produced from copperalloys with nominal compositions as listed in Table 1.21.2 Castings produced to this specification may be manu-factured for and supplied from stock. In such cases themanufacturer shall maintain heat traceability to specific manu-facturing date
4、and chemical analysis.1.3 The values stated in either SI units or inch/pound unitsare to be regarded separately as standard. The values stated ineach system may not be exact equivalents; therefore, eachsystem shall be used independently of the other. Combiningvalues from the two systems may result i
5、n non-conformancewith the standard.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limit
6、ations prior to use.2. Referenced Documents2.1 The following documents in the current issue of theAnnual Book of ASTM Standards form a part of this specifi-cation to the extent referenced herein:2.2 ASTM Standards:3B208 Practice for Preparing Tension Test Specimens forCopper Alloy Sand, Permanent Mo
7、ld, Centrifugal, andContinuous CastingsB824 Specification for General Requirements for CopperAlloy CastingsB846 Terminology for Copper and Copper AlloysE8 Test Methods for Tension Testing of Metallic MaterialsE8M Test Methods for Tension Testing of Metallic Materi-als Metric4E10 Test Method for Brin
8、ell Hardness of Metallic MaterialsE18 Test Methods for Rockwell Hardness of Metallic Ma-terialsE255 Practice for Sampling Copper and Copper Alloys forthe Determination of Chemical CompositionE527 Practice for Numbering Metals and Alloys in theUnified Numbering System (UNS)3. Terminology3.1 For defin
9、itions of terms related to copper and copperalloys, refer to Terminology B846.4. General Requirements4.1 The following sections of Specification B824 form apart of this specification. The definition of a casting lot asdefined in Section 12, Sampling, takes precedence over Speci-fication B824.4.1.1 T
10、erminology (Section 3),4.1.2 Other Requirements (Section 7),4.1.3 Workmanship, Finish, and Appearance (Section 9),4.1.4 Number of Tests and Retests (Section 11),4.1.5 Specimen Preparation (Section 12),4.1.6 Test Methods (Section 13),4.1.7 Significance of Numerical Limits (Section 14),4.1.8 Inspectio
11、n (Section 15),4.1.9 Rejection and Rehearing (Section 16),4.1.10 Certification (Section 17),4.1.11 Test Report (Section 18),4.1.12 Product Marking (Section 19),4.1.13 Packaging and Package Marking (Section 20),4.1.14 Keywords (Section 21), and4.1.15 Supplementary Requirements.1This specification is
12、under the jurisdiction ofASTM Committee B05 on Copperand Copper Alloys and is the direct responsibility of Subcommittee B05.05 onCastings and Ingots for Remelting.Current edition approved April 1, 2010. Published May 2010. Originallyapproved in 1970. Last previous edition approved in 2009 as B505/B5
13、05M 09.DOI: 10.1520/B0505_B0505M-10.2The UNS system for copper and copper alloys (see Practice E527) is a simpleexpansion of the former standard designation system accomplished by the additionof a prefix “C” and a suffix “00”. The suffix can be used to accommodatecomposition variations of the base a
14、lloy.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.4Withdrawn. The last approved version of this historical
15、 standard is referencedon www.astm.org.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5. Ordering Information5.1 Include the following information in orders for produ
16、ct:5.1.1 ASTM designation and year of issue (for example,B505/B505M 04),5.1.2 Copper Alloy UNS No. (for example, C93200), in-cluding HT if heat treatment is required.5.1.3 Condition (Table 9) and (as cast, heat treated, and soforth),5.1.4 Dimensions: inside diameter, outside diameter, thick-ness and
17、 width,5.1.5 Form: cross-section, such as tube, round, hexagon,octagon, square, or rectangle,5.1.6 Tolerances, if different from Section 10 and Tables2-8.5.1.7 Length (including length tolerance if other than milllengths),TABLE 1 Nominal CompositionCopper Alloy UNSNo.DesignationComposition, %Copper
18、Tin Lead Zinc Nickel Aluminum Iron ManganeseC83600 leaded red brass 85 5 5 5 . . . .C83800 leaded red brass 82.9 3.8 6 6.5 . . . .C84200 leaded semi-red brass 80 5 2.5 13 . . . .C84400 leaded semi-red brass 80 2.9 7 8.5 . . . .C84800 leaded semi-red brass 76 2.5 6.2 15 . . . .C85700 leaded naval bra
19、ss 61 1 1.2 36 . . . .C86200 high-strength yellow brass 63 . . 25 . 4 3 3.8C86300 high-strength yellow brass 63 . . 25 . 6.2 3 3.8C86500 high-strength yellow brass 57.5 . . 39 . 1 1.2 0.8C87700Asilicon bronze 88.5 . . 8 . . . .C87710Bsilicon bronze 86 . . 10 . . . .C87850Csilicon brass 76 . . 20.9 .
20、 . . .C89320Dbismuth tin bronze 89 6 . . . . . .C90300 tin bronze 87.5 8.2 . 4 . . . .C90500 tin bronze 87.5 10 . 2 . . . .C90700 tin bronze 89 11 . . . . . .C91000 tin bronze 85 15 . . . . . .C91300 tin bronze 80.5 19 . . . . . .C92200 leaded tin bronze 88 6 1.5 4 . . . .C92300 leaded tin bronze 87
21、 8.2 0.6 3.8 . . . .C92500 nickel-phosphor bronze 86.5 11 1.2 . 1.2 . . .C92700 leaded tin bronze 87.5 10 1.8 . . . . .C92800 leaded tin bronze 80 16 5 . . . . .C92900 leaded nickel-tin bronze 84 10 2.6 . 3.4 . . .C93200 high-leaded tin bronze 83 6.9 7 3 . . . .C93400 high-leaded tin bronze 83.5 8 8
22、 . . . . .C93500 high-leaded tin bronze 84.5 5.2 9 1 . . . .C93600 high-leaded tin bronze 81 7 12 . . . . .C93700 high-leaded tin bronze 80 10 9.5 . . . . .C93800 high-leaded tin bronze 77 6.9 14.5 . . . . .C93900 high-leaded tin bronze 78 6 16 . . . . .C94000 high-leaded tin bronze 70.5 13 15 . . .
23、 . .C94100 high-leaded tin bronze 75.5 5.5 20 . . . . .C94300 high-leaded tin bronze 69.5 5.2 25 . . . . .C94700 nickel-tin bronze 87.5 5.2 0 1.8 5.2 . . .C94800 leaded nickel-tin bronze 86.5 5.2 0.6 1.8 5.2 . . .C95200 aluminum bronze 87.8 . . . . 9 3.2 .C95300 aluminum bronze 88.8 . . . . 10 1.2 .
24、C95400 aluminum bronze 85.2 . . . . 10.8 4 .C95410 aluminum bronze 83.2 . . . 2 10.8 4 .C95500 nickel-aluminum bronze 81 . . . 4.2 10.8 4 .C95520 nickel-aluminum bronze 79.1 . . . 5.1 11 4.8 .C95700 manganese nickel aluminum 74.8 . . . 2.2 7.5 3 12.5bronzeC95800 nickel-aluminum bronze 81.3 . . . 4.5
25、 9 4 1.2C95900 aluminum bronze 83.2 . . . . 12.8 4.0 .C96400 copper-nickel 67 . . . 30 . 0.90 .C96900 copper-nickel 76.8 8 . . 15 . . 0.20C96970 copper-nickel-tin 85 6 . . 9.0 . . .C97300 leaded nickel bronze 55.5 2.2 9.5 21 12.5 . . .C97600 leaded nickel bronze 65 4 4 6 20.2 . . .C97800 leaded nick
26、el bronze 65.5 4.8 1.8 2.5 25.5 . . .C99500Especial alloy 89.1 . . 1.2 4.5 1.2 4.0 .ASilicon 3BSilicon 4CSilicon 3, Phosphorus 0.12DBismuth 5.0ESilicon 1.3B505/B505M 1025.1.8 Number of castings or total weight, for each size andform,5.1.9 ASME Boiler and Pressure Vessel Code5requirements(if required
27、 see Section 9),5.1.10 When castings are purchased for agencies of the U.S.government, the Supplementary Requirements of SpecificationB824 may be specified.5.2 The following requirements are optional and should bespecified in the purchase order when required:5.2.1 Chemical analysis of residual eleme
28、nts (Section 7 andSpecification B824),5.2.2 Mechanical requirements, (Section 8 Test MethodsE8),5Available from American Society of Mechanical Engineers (ASME), ASMEInternational Headquarters, Three Park Ave., New York, NY 10016-5990, http:/www.asme.org.TABLE 2 Suggested Heat TreatmentsCopper AlloyU
29、NS No.Solution Treatment (not less than1 h followed by water quench),F(C)Annealing Treatment(not less than 2 hfollowed by air cool),F(C)C9530015851635(860890)11501225(620660)C95400,C95410, C9550016001675(870910)11501225(620660)C95520 (2 h followed by water quench)16001700 (870925)9251000(495540)TABL
30、E 3 Finishing Allowances for Tube (Round Only)Finished Outside Diameter,in. (mm)Finish Allowances Added toFinished or PrintDimensions of the Part, in. (mm)Inside DiameterOutsideDiameterAll Alloys Except as Noted BelowUp to 4 (102), excl 0.031 (0.79) + 0.031 (0.79)4 (102)5 (127), incl 0.063 (1.6) + 0
31、.063 (1.6)Over 5 (127) 0.094 (2.4) + 0.094 (2.4)Copper Alloy UNS Nos. C86200, C86300, C86500, C87700, C87710, C87850,C95200, C95300, C95400,C95500, C95800, C95900, and C96400Up to 3 (76.2), incl 0.125 (3.2) + 0.063 (1.6)Over 3 (76.2)4 (102), incl 0.125 (3.2) + 0.094 (2.4)Over 4 (102)512 (140), incl
32、0.188 (4.8) + 0.125 (3.2)Over 512 (140) 0.250 (6.4) + 0.188 (4.8)TABLE 4 Finishing Allowances for Rod and BarFinished Outside Diameter orDistance BetweenParallel Surfaces, in. (mm)RoundsSquares,Rectangles,Hexagons,OctagonsAll Alloys Except as Noted BelowUp to 4 (102), excl + 0.031 (0.79) + 0.031 (0.
33、79)4 (102)5 (127), incl + 0.063 (1.6) + 0.063 (1.6)Over 5 (127) + 0.094 (2.4) + 0.094 (2.4)Copper Alloy UNS Nos. C86200, C86300, C86500, C87700, C87710, C87850,C95200, C95300,C95400, C95500, C95800, C95900, C96400Up to 3 (76.2), incl + 0.0625 (1.6) + 0.0625 (1.6)Over 3 (76.2)4 (102), incl + 0.093 (2
34、.4) + 0.093 (2.4)Over 4 (102)512 (140), incl + 0.125 (3.2) + 0.125 (3.2)Over 512 (140) + 0.188 (4.8) + 0.188 (4.8)TABLE 5 Diameter Tolerances for Rod and BarDiameter or Distance Be-tween Parallel Surfaces,in. (mm)Tolerances, PlusAand Minus,Ain. (mm)RoundsSquares, Rectangles,Hexagons,OctagonsAll Allo
35、ys Except as Noted BelowUp to 4 (102), excl 0.005 (0.13) 0.016 (0.41)4 (102)5 (127), incl 0.008 (0.20) 0.016 (0.41)Over 5 (127) 0.016 (0.41) 0.016 (0.41)Copper Alloy UNS Nos. C86200, C86300, C86500, C87700, C87710, C87850,C95200, C95300, C95400, C95500, C95800, C95900, and C96400Up to 3 (76.2), incl
36、 0.010 (0.25) 0.020 (0.51)Over 3 (76.2)4 (102), incl 0.015 (0.38) 0.020 (0.51)Over 4 (102)512 (140), incl 0.020 (0.51) 0.020 (0.51)Over 512 (140) 0.025 (0.64) 0.025 (0.64)AWhen tolerances are specified as all plus or all minus, double the values given.TABLE 6 Diameter Tolerances for Tube (Round Only
37、)Average Outside Diameter,in. (mm)Tolerances, in. (mm)OutsideDiameterInside DiameterPlusAorMinusAPlusBMinusBAll Alloys Except as Noted BelowUp to 4 (102), excl 0.005 (0.13) 0.012 (0.30) 0.033 (0.84)4 (102)5 (127), incl 0.008 (0.20) 0.016 (0.41) 0.046 (1.2)Over 5 (127) 0.016 (0.41) 0.032 (0.81) 0.064
38、 (1.6)Copper Alloy UNS Nos. C86200, C86300, C86500, C87700, C87710, C87850,C95200, C95300, C95400, C95500, C95800, C95900, and C96400Up to 3 (76), incl 0.010 (0.25) 0.012 (0.32) 0.033 (0.84)Over 3 (76)4 (102), incl 0.015 (0.38) 0.015 (0.38) 0.050 (1.3)Over 4 (102)512 (140), incl 0.020 (0.51) 0.025 (
39、0.64) 0.070 (1.8)Over 512 (140) 0.025 (0.64) 0.035 (0.86) 0.090 (2.3)AWhen tolerances are specified as all plus or all minus double the values given.BWhen tolerances are specified as all plus or all minus, total the values given.TABLE 7 Roundness TolerancesOutside Diameter, in. (mm)Maximum Out-of-Ro
40、undness,Ain. (mm)Up to 4 (102), excl 0.020 (0.51)4 (102)5 (127), incl 0.032 (0.81)Over 5 (127) 0.064 (1.6)Copper Alloy UNS Nos. C86200, C86300, C86500, C87700, C87710, C87850,C95200, C95300, C95400, C95500, C95800, C95900, and C96400Up to 3 (76.2), incl 0.025 (0.64)Over 3 (76.2)4 (102), incl 0.040 (
41、1.0)Over 4 (102)512 (140), incl 0.060 (1.5)Over 512 (140) 0.075 (1.9)AThe deviation from roundness is measured as the difference between majorand minor diameters as determined at any one cross section of the tube.TABLE 8 Tolerances for ShapesOutside Dimension,Ain. (mm) Inside Dimension,Bin. (mm)All
42、Alloys Except as Noted BelowPlus Minus Plus Minus0.016 (0.41) 0.016 (0.41) 0.032 (0.81) 0.064 (1.6)Copper Alloy UNS Nos. C86200, C86300, C86500, C87700, C87710, C87850,C95200, C95300, C95400, C95500, C95800, C95900, and C96400Dimensional tolerances shall be subject to agreement between purchaserand
43、manufacturer.AWhen tolerances are specified as all plus or all minus, double the values given.BWhen tolerances are specified as all plus or all minus, total the values given.B505/B505M 1035.2.3 Witness inspection (Specification B824),5.2.4 Certification (Specification B824),5.2.5 Foundry test report
44、 (Specification B824),5.2.6 Product marking (Specification B824),5.2.7 Castings for seawater service (Section 6), andTABLE 9 Mechanical RequirementsCopper AlloyUNS No.Tensile Strength, minAYield Strength, at 0.5 % ExtensionUnder Load, minAElongation in 2in.or50mm,min, %Brinell Hardness,minRemarksksi
45、BMPaCksiBMPaCC83600 36 248 19 131 15C83800 30 207 15 97 16C84200 32 221 16 110 13C84400 30 207 15 103 16C84800 30 207 15 103 16C85700 40 276 14 97 15C86200 90 621 45 310 18C86300 110 758 62 427 14C86500 70 483 25 172 25C87700 25 172 17 117 18C87710 64 441 22 152 20C87850 65 448 25 172 8 103 (500 kg)
46、C89320 35 241 18 124 15C90300 44 303 22 152 18C90500 44 303 25 172 10C90700 40 276 25 172 10C91000 30 207 . . .C91300 . . . . . 160 (3000 kg)C92200 38 262 19 131 18C92300 40 276 19 131 16C92500 40 276 24 165 10C92700 38 252 20 138 8 . RockwellC92800 . . . . . B7282C92900 45 310 25 172 8C93200 35 241
47、 20 138 10C93400 34 234 20 138 8C93500 30 207 16 110 12C93600 33 227 20 138 10C93700 35 241 20 138 6C93800 25 172 16 110 5C93900 25 172 16 110 5C94000 . . . . . 80 (500 kg)C94100 25 172 17 117 7C94300 21 145 15 103 7C94700 45 310 20 138 25C94700HT 75 517 50 345 5 heat treatedC94800 40 276 20 138 20C
48、95200 68 469 26 179 20C95300 70 483 26 179 25C95300HT 80 552 40 276 12 heat treatedC95400 85 586 32 221 12C95400HT 95 655 45 310 10 heat treatedC95410 85 586 32 221 12C95410HT 95 655 45 310 10 heat treatedC95500 95 655 42 290 10C95500HT 110 758 62 427 8 heat treatedC95520HT 125 862 95D655D2 262 (300
49、0 kg) heat treatedEC95700 90 620 40 275 15C95800F85 586 35 241 18C95900 . . . . . 241 (3000 kg)C96400 65 448 35 241 25C96900HT 110 758 105D724D4 Rockwell C32C97300 30 207 15 103 8C97600 40 276 20 138 10C97800 45 310 22 152 8C99500 70 483 40 276 12C96970 105 723 90D620D3 Rockwell C27AMinimum tensile strength and yield strength shall be reduced 10 % for cast bars having a cross section, thickness, diameter, or wall of 4 in. (102 mm) or more. Thecross sections are the diameter of a round solid, the distance across the flats